电化学(中英文) ›› 2016, Vol. 22 ›› Issue (6): 577-581.  doi: 10.13208/j.electrochem.160567

• 界面电化学近期研究专辑(厦门大学 毛秉伟教授) • 上一篇    下一篇

[BMIm]BF4/Pt电极界面激光诱导电沉积Cu基材料研究

徐敏敏,梅金华,姚建林*,顾仁敖   

  1. 苏州大学材料与化学化工学部 江苏 苏州 215123
  • 收稿日期:2016-07-09 修回日期:2016-10-25 出版日期:2016-12-28 发布日期:2016-11-24
  • 通讯作者: 姚建林 E-mail:jlyao@suda. edu. cn
  • 基金资助:

    国家自然科学基金项目(No. 21173155, No. 21303115, No. 21473118)资助

Investigation on Laser Induced Deposition of Cu-Based Materials at [BMIm]BF4/Pt Electrode Interface

XU Min-min, Mei Jin-hua, YAO Jian-lin*, GU Ren-ao   

  1. College of Chemistry,Chemical Engineering and Materials Science,Soochow University,Suzhou 215123, Jiangsu, China
  • Received:2016-07-09 Revised:2016-10-25 Published:2016-12-28 Online:2016-11-24
  • Contact: YAO Jian-lin E-mail:jlyao@suda. edu. cn

摘要:

本文利用激光诱导并结合控制一定的电极电位,在[BMIm]BF4/Pt电极体系中实现了激光诱导电沉积Cu基材料. 研究表明在非沉积电位(-0.2 V)激光可诱导产生电沉积. 激光的功率和照射时间对沉积产物有显著影响:功率越大,照射时间越长,则表面沉积物的量越多,且沉积仅仅发生在激光照射点以内. 此类激光诱导电沉积的发生主要源于激光的热效应可使电极表面局域温度显著上升,从而降低沉积的阈值电位,促使电沉积在非沉积电位区间发生. SEM研究表明电极表面的沉积点由50 nm左右的纳米粒子聚集而成,进一步的EDS和拉曼光谱证明该产物主要由Cu和Cu2O的混合物组成. 以对巯基苯甲酸(MBA)为探针分子,通过SERS信号的强度变化,现场监测了激光诱导电沉积的过程,在起始阶段其沉积物的SERS效应明显,随沉积时间延长,因沉积物增多其形貌发生变化,“热点”消失,其SERS效应反而降低并随后保持不变. 同时,沉积点以外的SERS中并未检测到MBA,说明激光诱导作用仅仅发生在激光照射区域内,这为电极表面的定向沉积提供了新的途径.

关键词: 离子液体, 激光, 诱导电沉积, 铜, 表面增强拉曼光谱(SERS)

Abstract:

By controlling the negative potential, Cu-based materials were deposited at the [BMIm]BF4/Pt electrode interface under the laser irradiation. The effects of laser power and irradiation time on the yield of deposition products were studied by using different laser powers and different irradiation time. The product yield could be directly determined by the size of deposition point through the observation from the optical microscope. Further mechanism study combined with the formula deduced that the thermal effect of the laser could make the electrode surface temperature rise 110 degrees, which can promote the occurrence of electrodeposition. By SEM characterization, the deposition point was formed from nanoparticle aggregation with the diameter of 50 nm. The EDS and Raman spectra showed that the product was a mixture of Cu and Cu2O. The sedimentary formation and growth process could be monitored by the changes in the intensity of the SERS signals from 1 mM of mercaptobenzoic acid (MBA). In addition, it was concluded based on the SERS experiments that no deposition products were formed without the laser irradiation.

Key words: ionic liquids, laser, induced electrodeposition, Copper, surface enhanced Raman spectroscopy