高电压镍锰酸锂正极/电解液界面本征性质的研究

doi:10.13208/j.electrochem.160564

电化学（中英文） ›› 2016, Vol. 22 ›› Issue (6): 582-589. doi: 10.13208/j.electrochem.160564

• 界面电化学近期研究专辑（厦门大学毛秉伟教授） • 上一篇下一篇

高电压镍锰酸锂正极/电解液界面本征性质的研究

李丽^1,2，许晶晶¹，韩少杰¹，吴晓东¹，卢威¹，陈立桅¹*

1. 中国科学院苏州纳米技术与纳米仿生研究所，苏州 215123；2. 中国科学技术大学，纳米科学与纳米技术学院，苏州215123

收稿日期:2016-06-16 修回日期:2016-07-27 出版日期:2016-12-28 发布日期:2016-07-29
通讯作者: 陈立桅 E-mail:lwchen2008@sinano.ac.cn
基金资助:
国家自然科学基金项目(21473241，21273273和21503265), 苏州市科技计划项目(ZXG201419)资助.

Intrinsic Interfacial Property between High-Voltage LiNi_0.5Mn_1.5O₄Cathode and Electrolyte

LI Li^1,2, XU Jing-jing¹, HAN Shao-jie¹, LU Wei¹, Chen Li-wei¹*

1. i-Lab, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, Suzhou, Jiangsu 215125, China; 2. University of science and technology of China, Nanoscience and Technology Institute, Suzhou, Jiangsu 215125, China

Received:2016-06-16 Revised:2016-07-27 Published:2016-12-28 Online:2016-07-29
Contact: Chen Li-wei E-mail:lwchen2008@sinano.ac.cn

摘要/Abstract

摘要：

高电压正极材料的应用是提高锂离子电池能量密度的有效手段，然而高电压下正极/电解液界面稳定性成为决定锂离子电池在高电压工作条件下循环性能和安全性能的关键因素，因此高电压下正极/电解液界面具有重要的研究价值. 但是，目前报道的正极/电解液界面的研究中通常使用传统的极片制备方法，这需要引入导电剂和粘结剂，会对后期正极活性物质表面钝化膜的形貌和组分表征带来干扰，甚至造成固体电解质界面(SEI)膜存在的假象，难以获得正极材料与电解液之间界面的本征信息. 这里，我们采用溶胶凝胶旋涂法制备了不含导电剂和粘结剂的镍锰酸锂(LNMO)正极，以其为研究对象，通过扫描电镜(SEM)、原子力显微镜(AFM)和X射线光电子能谱(XPS)技术，结合电化学阻抗谱(EIS)研究了LNMO正极/电解液界面在充放电过程中的结构演变过程以及本征性质. 研究结果显示在充放电过程中，电解液中溶剂和电解质都会参与反应，其中LiPF₆的降解主要发生在高电压下，其降解产物在放电过程中又会被反应消耗掉. 它们的降解产物沉积到LNMO正极形成表面膜，该表面膜的主要成分随着电压的不同组分有所不同.

关键词: 高电压镍锰酸锂, 正极/电解液界面, 本征性质, 固体电解质界面, 电解液氧化分解, 表面膜

Abstract:

To obtain high energy density, developing high-voltage cathode materials is an effective approach. The cathode/electrolyte interface stability is the key factor for the cycle performance and safety performance of high-voltage lithium ion batteries. It is, therefore, of significant importance to study the stability of cathode/electrolyte interface. However, many reports have shown that at the cathode/electrolyte interface the cathodes were prepared by coating the mixture of active materials with a conductive additive and a binder on an Al current collector. The introduction of additives will interfere the surface morphology and component analyses, resulting in difficulty to acquire the intrinsic information at the cathode/electrolyte interface. In this paper, the LiNi_0.5Mn_1.5O₄ (LNMO) film electrodes were prepared via sol-gel method without using conductive additive and binder. The surface morphology and the intrinsic property of LNMO electrode/electrolyte interface during the charge/discharge process were studied by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and Electrochemical impedance spectroscopy (EIS). The results demonstrated that both solvents and LiPF₆salt degraded during the charge/discharge process. The degradation of LiPF₆mainly happened at the high-voltage charge process and the intermediate POF₃was unstable which continued to be reacted during the discharge process. The degraded residues deposit on the surface of LNMO cathode to form a surface film and the compositions of the surface film varied with voltages during the electrochemical process.

Key words: high-voltage LiNi_0.5Mn_1.5O₄ cathode material, cathode/electrolyte interface, intrinsic property, solid electrolyte interphase, oxidized decomposition of electrolyte, surface film

中图分类号:

O646

李丽，许晶晶，韩少杰，吴晓东，卢威，陈立桅. 高电压镍锰酸锂正极/电解液界面本征性质的研究[J]. 电化学（中英文）, 2016, 22(6): 582-589.

LI Li, XU Jing-jing, HAN Shao-jie, LU Wei, Chen Li-wei. Intrinsic Interfacial Property between High-Voltage LiNi_0.5Mn_1.5O₄Cathode and Electrolyte[J]. Journal of Electrochemistry, 2016, 22(6): 582-589.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.160564

https://electrochem.xmu.edu.cn/CN/Y2016/V22/I6/582

参考文献

[1] Okubo M, Hosono E, Kim J, et al. Nanosize effect on high-rate Li-ion intercalation in LiCoO₂ electrode[J]. Journal of the American Chemical Society, 2007, 129(23): 7444-7452.

[2] Zhu JP, Xu QB, Junjie-Zhao, et al. Synthesis and Electrochemical Properties of Modification LiNi_1/3Co_1/3Mn_1/3O₂ Cathode Materials for Li-ion Battery[J]. Journal of Nanoscience and Nanotechnology, 2012, 12(3): 2534-2538.

[3] Okubo M, Mizuno Y, Yamada H, et al. Fast Li-Ion Insertion into Nanosized LiMn₂O₄ without Domain Boundaries[J]. ACS Nano, 2010, 4(2): 741-752.

[4] Li QY, Zheng FH, Huang YG, et al. Surfactants assisted synthesis of nano-LiFePO₄/C composite as cathode materials for lithium-ion batteries[J]. Journal of Materials Chemistry A, 2015, 3(5): 2025-2035.

[5] Liu J, Manthiram A. Understanding the Improved Electrochemical Performances of Fe-Substituted 5 V Spinel Cathode LiMn_1.5Ni_0.5O₄[J]. Journal of Physical Chemistry C, 2009, 113(33): 15073-15079.

[6] Kim K, Kim Y, Oh ES, et al. The role of fluoride in protecting LiNi_0.5Mn_1.5O₄ electrodes against high temperature degradation[J]. Electrochimica Acta, 2013, 114: 387-393.

[7] Konishi H, Suzuki K, Taminato S, et al. Effect of surface Li₃PO₄ coating on LiNi_0.5Mn_1.5O₄ epitaxial thin film electrodes synthesized by pulsed laser deposition[J]. Journal of Power Sources, 2014, 269(4): 293-298.

[8] Manthiram A, Chemelewski K, Lee ES. A perspective on the high-voltage LiMn_1.5Ni_0.5O₄ spinel cathode for lithium-ion batteries[J]. Energy & Environmental Science, 2014, 7(4): 1339-1350.

[9] Xu K. Nonaqueous liquid electrolytes for lithium-based rechargeable batteries[J]. Chemical Reviews, 2004, 104(10): 4303-4417.

[10] Zhang SS. A review on electrolyte additives for lithium-ion batteries[J]. Journal of Power Sources, 2006, 162(2): 1379-1394.

[11] Liu J, Manthiram A. Kinetics Study of the 5 V Spinel Cathode LiMn_1.5Ni_0.5O₄ Before and After Surface Modifications[J]. Journal of Electrochemical Society, 2009, 156(12): A833-A838.

[12] Wu HM, Belharouak I, Abouimrane A, et al. Surface modification of LiNi_0.5Mn_1.5O₄ by ZrP₂O₇ and ZrO₂ for lithium-ion batteries[J]. Journal of Power Sources, 2010, 195(5): 2909-2913.

[13] Xu JJ, Hu YY, Liu T, et al. Improvement of cycle stability for high-voltage lithium-ion batteries by in-situ growth of SEI film on cathode[J]. Nano Energy, 2014, 5(4): 67-73.

[14] Choi NS, Han JG, Ha SY, et al. Recent advances in the electrolytes for interfacial stability of high-voltage cathodes in lithium-ion batteries[J]. RSC Advances, 2015, 5(4): 2732-48.

[15] Bae SY, Shin WK, Kim DW. Protective organic additives for high voltage LiNi_0.5Mn_1.5O₄ cathode materials[J]. Electrochimica Acta, 2014, 125(12): 497-502.

[16] Li B, Wang YQ, Tu WQ, et al. Improving cyclic stability of lithium nickel manganese oxide cathode for high voltage lithium ion battery by modifying electrode/electrolyte interface with electrolyte additive[J]. Electrochimica Acta, 2014, 147: 636-642.

[17] Wang Y, Peng Q, Yang G, et al. High-stability 5 V spinel LiNi_0.5Mn_1.5O₄ sputtered thin film electrodes by modifying with aluminium oxide[J]. Electrochimica Acta, 2014, 136(8): 450-456.

[18] Xu JJ, Xia QB, Chen FY, et al. Facilely solving cathode/electrolyte interfacial issue for high-voltage lithium ion batteries by constructing an effective solid electrolyte interface film[J]. Electrochimica Acta, 2016, 191: 687-694.

[19] Han JG, Lee SJ, Lee J,et al. Tunable and Robust Phosphite-Derived Surface Film to Protect Lithium-Rich Cathodes in Lithium-Ion Batteries. ACS Applied Materials & Interfaces, 2015, 7(15): 8319-8329.

[20] Gellert M, Gries KI, Zakel J, et al. LiNi_0.5Mn_1.5O₄ Thin-Film Cathodes on Gold-Coated Stainless Steel Substrates: Formation of Interlayers and Electrochemical Properties[J]. Electrochimica Acta, 2014, 133: 146-152.

[21] Talyosef Y, Markovsky B, Salitra G, et al. The study of LiNi_0.5Mn_1.5O₄ 5-V cathodes for Li-ion batteries[J]. Journal of Power Sources, 2005, 146(1): 664-669.

[22] Chong J, Xun SD, Zhang JP, et al. Li₃PO₄-Coated LiNi_0.5Mn_1.5O₄: A Stable High-Voltage Cathode Material for Lithium-Ion Batteries[J]. Chemistry-European Journal, 2014, 20(24): 7479-7485.

[23] Tan S, Ji YJ, Zhang ZR, et al. Recent Progress in Research on High-Voltage Electrolytes for Lithium-Ion Batteries[J]. Chemphyschem, 2014, 15(10): 1956-1969.

[24] Aurbach D, Levi MD, Levi E, et al. Common electroanalytical behavior of Li intercalation processes into graphite and transition metal oxides[J]. Journal of Electrochemical Society, 1998, 145(9): 3024-3034.

[25] Duncan H, Duguay D, Abu-Lebdeh Y, et al. Study of the LiMn_1.5Ni_0.5O₄∕Electrolyte Interface at Room Temperature and 60°C[J]. Journal of Electrochemical Society, 2011, 158(5): A537-A545.

[26] Duncan H, Abu-Lebdeh Y, Davidson IJ. Study of the Cathode–Electrolyte Interface of LiMn_1.5Ni_0.5O₄ Synthesized by a Sol–Gel Method for Li-Ion Batteries[J]. Journal of Electrochemical Society, 2010, 157(4): A528-A535.

[27] Yang L, Ravdel B, Lucht BL. Electrolyte Reactions with the Surface of High Voltage LiNi_0.5Mn_1.5O₄ Cathodes for Lithium-Ion Batteries[J]. Electrochemical and Solid-State Letters, 2010, 13(8): A95-A97.

[28] Kim JW, Kim DH, Oh DY, et al. Surface chemistry of LiNi_0.5Mn_1.5O₄ particles coated by Al₂O₃ using atomic layer deposition for lithium-ion batteries[J]. Journal of Power Sources, 2015, 274: 1254-1262.

[29] Haik O, Leifer N, Samuk-Fromovich Z, et al. On the Surface Chemistry of LiMO₂ Cathode Materials (M=[MnNi] and [MnNiCo]): Electrochemical, Spectroscopic, and Calorimetric Studies[J]. Journal of Electrochemical Society, 2010, 157(10): A1099-A1107.

[30] Wu C, Bai Y, Wu F. Fourier-transform infrared spectroscopic studies on the solid electrolyte interphase formed on Li-doped spinel Li_1.05Mn_1.96O₄ cathode[J]. Journal of Power Sources, 2009, 189(1): 89-94.

高电压镍锰酸锂正极/电解液界面本征性质的研究

Intrinsic Interfacial Property between High-Voltage LiNi_0.5Mn_1.5O₄Cathode and Electrolyte

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 8

Metrics

[1]	戴昭霞, 郑大江, 宋光铃, 冯丹青, 苏培. 不同电位下极化后的纯钛表面生物污损行为[J]. 电化学（中英文）, 2022, 28(5): 2109061-.
[2]	张滟滟, 刘越, 陆一鸣, 于沛平, 杜文轩, 麻冰云, 谢淼, 杨昊, 程涛. 多尺度模拟研究溶质调控下电解液在锂金属电极上的分解机理[J]. 电化学（中英文）, 2022, 28(4): 2105181-.
[3]	程浩然, 马征, 郭营军, 孙春胜, 李茜, 明军. 影响电池性能的因素：金属离子溶剂化结构衍生的界面行为还是固体电解质界面膜?[J]. 电化学（中英文）, 2022, 28(11): 2219012-.
[4]	侯廷政, 陈翔, 蒋璐, 唐城. 当前和下一代锂离子电池电解液的原子尺度微观认识和研究进展[J]. 电化学（中英文）, 2022, 28(11): 2219007-.
[5]	马洪运, 姚晓辉, 妙孟姚, 易阳, 伍绍中, 周江. 高镍正极材料(LiNi_0.83Co_0.12Mn_0.05O₂)45°C循环失效机理研究[J]. 电化学（中英文）, 2020, 26(3): 431-440.
[6]	郭文君，李紫琼，柯若昊，钮东方，徐衡，张新胜. 脉冲电沉积抑制锂枝晶生成的研究[J]. 电化学（中英文）, 2018, 24(3): 246-252.
[7]	姚洋洋, 刘冬冬, 王莉, 何向明, 李建军, 张鼎. 二氟草酸硼酸钠作为电解液添加剂对石墨负极性能的影响[J]. 电化学（中英文）, 2015, 21(4): 387-392.
[8]	郑杰允，郑浩，汪锐，李泓*，陈立泉. 力曲线用于硅负极材料表面膜的研究[J]. 电化学（中英文）, 2013, 19(6): 530-536.

高电压镍锰酸锂正极/电解液界面本征性质的研究

Intrinsic Interfacial Property between High-Voltage LiNi0.5Mn1.5O4 Cathode and Electrolyte

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 8

Metrics

Intrinsic Interfacial Property between High-Voltage LiNi_0.5Mn_1.5O₄Cathode and Electrolyte