LiF-BaF2-LiCl熔盐体系中Li+的电化学行为

doi:10.13208/j.electrochem.150918

电化学（中英文） ›› 2016, Vol. 22 ›› Issue (3): 306-310. doi: 10.13208/j.electrochem.150918

LiF-BaF₂-LiCl熔盐体系中Li⁺的电化学行为

杨少华，王君*，赖晓晖，王浩然

江西理工大学冶金与化学工程学院，江西赣州 341000

收稿日期:2015-09-21 修回日期:2015-10-11 出版日期:2016-06-28 发布日期:2015-11-19
通讯作者: 王君 E-mail:1556390714@qq.com
作者简介:王君
基金资助:
国家自然科学基金项目(No. 3203204516)资助

The Electrochemical Behavior of Li+ in LiF-BaF₂-LiCl Molten Salt System

YANG Shao-hua, WANG Jun*, LAI Xiao-hui, WANG Hao-ran

School of Metallurgy and Chemical Engineering, JiangXi University of Science and Technology, Ganzhou, 341000, Jiangxi, China

Received:2015-09-21 Revised:2015-10-11 Published:2016-06-28 Online:2015-11-19
Contact: WANG Jun E-mail:1556390714@qq.com
About author:WANG Jun

摘要/Abstract

摘要：

运用三电极在电化学工作站AUTOLAB以循环伏安法、计时电流法和计时电位法研究了LiF-BaF₂-LiCl熔盐体系中1203 K温度下锂在钨（W）电极上的电化学还原过程及其控制步骤. 结果表明，Li⁺在W电极上的还原过程是一步得电子的准可逆反应，析出电位在-1.0 V附近. 阴极过程受离子的扩散步骤控制，计算得出扩散系数为4.5 × 10^-6 cm²•s^-1.

关键词: 熔盐, 阴极过程, 电化学, 扩散控制

Abstract:

The electrochemical reduction process and rate determining step of Li ion on a tungsten electrode at 1203 K in a LiF-BaF₂-LiCl molten system were studied by cyclic voltammetry, chronoamperometry and chronopotentiometry methods using a three-electrode system and electrochemical workstation AUTOLAB. The results showed that the reduction potential of Li ion was at around -1.0 V on a tungsten electrode as compared with a platinum electrode. The reduction process of Li ion on a tungsten electrode occurred in a single step with the exchange of one electron. Chronoamperograms indicated that the cathode process was controlled by the diffusion step of ions and the diffusion coefficient was calculated to be 4.5 × 10^-6 cm²•s^-1.

Key words: molten salt, cathode process, electrochemical, diffusion control

中图分类号:

O646

杨少华，王君，赖晓晖，王浩然. LiF-BaF₂-LiCl熔盐体系中Li⁺的电化学行为[J]. 电化学（中英文）, 2016, 22(3): 306-310.

YANG Shao-hua, WANG Jun, LAI Xiao-hui, WANG Hao-ran. The Electrochemical Behavior of Li+ in LiF-BaF₂-LiCl Molten Salt System[J]. Journal of Electrochemistry, 2016, 22(3): 306-310.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.150918

https://electrochem.xmu.edu.cn/CN/Y2016/V22/I3/306

参考文献

[1] Zhang M J(张明杰), Guo Q F(郭清富). Energetic metal of the 21st century-the situation and development of lithium metallurgy[J]. Journal of Salt Lake Research(盐湖研究), 2001, 9(3): 52-60.

[2] China Nonferrous Metals Industry Association(中国有色金属工业协会). Series of nonferrous metals. Lithium, rubidium and cesium of china[M]. Beijing: Metallurgical Industry Press(冶金工业出版社), 2013.

[3] Kuhn A T. Industrial electrochemical process[M]. London: Elesevier, 1971: 207-209.

[4] Zhang M J(张明杰), Li J D(李继东), Wang Y W(王耀武). Electrochemical behavior of lithium carbonate in KCl-LiCl melt[J]. Journal of Northeastern University: Natural Science(东北大学学报: 自然科学版). 2005, 26(6): 570-573.

[5] Yan Y D(颜永得), Zhang M L(张密林), Han W(韩伟), et al. Prepartion and theory analysis of Mg-Li alloys via codeposition in KCI-LiCI-MgCl₂ melts[J]. Chinese Journal of Inorganic Chemistry(无机化学学报), 2008, 24(6): 902-906.

[6] Yan Y D, Zhang M L, Xue Y, et al. Electrochemical study of the codeposition of Mg-Li-Al alloys from LiCI-KCl-MgCl₂-AlCl₃ melts[J]. Journal of Applied Electrochemistry, 2009, 39(3): 455-461.

[7] Cao P, Zhang M L, Han W, et al. Preparation of ternary Mg-Li-Sn alloys from molten salt by electrolysis[J]. Acta Metallurgica Sinica: English Letters, 2012, 25(4): 265-271.

[8] Dai X F(戴兴福), Zhang M J(张明杰), Tan Y J(谭亚菊). Preparation of Al-Li master alloys by molten salt electrolysis[J]. Light Metals(轻金属), 1998, 1: 38-41.

[9] Xu J F(许建峰). Preparation and mechanism research of Ba-Li alloy and Zn-Ba-Li alloy via molten salt electrolysis process[D]. Harbin Engineering University, 2011. DOI: 10.7666/d.y2053200.

[10] Li J D(李继东), Zhang M J(张明杰). Zhang Y A(张延安), et al. Preparation of Al-Li master alloys by molten salt electrolysis[J]. The Chinese Journal of Nonferrous Metals(中国有色金属学报), 2008, 18(8): 1555-1559.

[11] Liu J N(刘江宁), Sun Z(孙泽), Jin X W(晋心文), et al. The cathodic reduction of magnesium in KCl-NaCl-MgCl₂ melts on a platinum electrode[J]. Nonferrous Metals: Extractive Metallurgy(有色金属: 冶炼部分), 2007, 6: 35-38.

[12] Chen Z(陈增), Zhang M L(张密林), Han W(韩伟), et al. Electrochemical reduction of Zr(IV) in the LiCl-KCl molten salt[J]. Rare Metal Materials and Engineering(稀有金属材料与工程), 2009, 38(3): 456-459.

[13] Bard A J, Faulkner L R. Electrochemical fundamentals and applications (2nd Edition)[M]. New York: John Wiley and Sons INC., 2003: 225- 227.

[14] Li M(李梅), Sun T T(孙婷婷), Liu B(刘斌), et al. Electrochemical behavior of Dy(Ⅲ) and the selective formation of Dy-Ni intermetallic compounds in LiCl-KCl eutectic melts[J]. Acta Physico-Chimica Sinica, 2015, 31(2): 309-314.

[15] Barde A J, Faulkner L R. Electrochemical methods, fundamentals and applications[M]. Beijing: Chemical Industry Press(化学工业出版社), 2005: 159.

[16] Paul M S Monck. Fundamentals of electroanalytical chemistry[M]. Beijing: Chemical Industry Press(化学工业出版社), 2001: 100-101.

[17] Greef R, Peat R, Pletcher L M, et al. Instrumental methods in electrochemistry[M]. London: Ellis Hrwood, 1990: 316- 317.

[18] McDonald D D. Transient techniques in electrochemistry[M]. New York: Plenum Press, 1977: 365-367.

LiF-BaF₂-LiCl熔盐体系中Li⁺的电化学行为

The Electrochemical Behavior of Li+ in LiF-BaF₂-LiCl Molten Salt System

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	崔苗苗, 韩联欢, 曾兰平, 郭佳瑶, 宋维英, 刘川, 吴元菲, 罗世翊, 刘云华, 詹东平. 单层石墨烯微米尺度图案化和功能化：调控电子传输特性[J]. 电化学（中英文）, 2024, 30(3): 2305251-.
[2]	梁志豪, 王家正, 王丹, 周剑章, 吴德印. 陷阱态对Ag-TiO₂光诱导界面电荷转移的影响：电化学、光电化学和光谱表征[J]. 电化学（中英文）, 2023, 29(8): 2208101-.
[3]	谭卓, 李凯旋, 毛秉伟, 颜佳伟. 电化学扫描隧道显微术：以Cu在Au(111)表面初始阶段电沉积为例[J]. 电化学（中英文）, 2023, 29(7): 2216003-.
[4]	胡琼, 李诗琪, 梁伊依, 冯文星, 骆怡琳, 曹晓静, 牛利. 基于硼酸盐亲和辅助电化学调控ATRP的癌胚抗原超灵敏电化学适体传感研究[J]. 电化学（中英文）, 2023, 29(6): 2218001-.
[5]	覃晓丽, 詹子颖, Sara Jahanghiri, Kenneth Chu, 张丛洋, 丁志峰. 金属有机框架材料在电化学/电化学发光免疫分析中的应用[J]. 电化学（中英文）, 2023, 29(6): 2218003-.
[6]	静超, 龙亿涛. 暗场显微镜下的彩色“纳米星”[J]. 电化学（中英文）, 2023, 29(6): 2218006-.
[7]	张生雅, 姚敏, 王泽, 刘天娇, 张蓉芳, 叶慧琴, 冯彦俊, 卢小泉. 通过扫描光电化学显微镜研究超分子光敏剂-二氧化钛薄膜系统的光诱导电子转移[J]. 电化学（中英文）, 2023, 29(6): 2218005-.
[8]	陈涛, 许元红, 李景虹. 基于电化学阻抗谱的致病菌检测传感器的研究进展[J]. 电化学（中英文）, 2023, 29(6): 2218002-.
[9]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[10]	罗宇, 马如琴, 龚正良, 杨勇. 固态锂硫电池研究进展[J]. 电化学（中英文）, 2023, 29(3): 2217007-.
[11]	张芯婉, 孟广源, 方立强, 常定明, 李童, 胡锦文, 陈鹏, 刘勇弟, 张乐华. 基于BP神经网络的电化学还原硝酸盐过程智能控制[J]. 电化学（中英文）, 2023, 29(12): 211215-.
[12]	汪恒吉, 陈文国, 全周益, 赵凯, 孙毅飞, 陈旻, 奥坚科·弗拉基米尔. 多孔陶瓷支撑型管式固体氧化物电解池性能研究[J]. 电化学（中英文）, 2023, 29(12): 2204131-.
[13]	乔行, 朱勇, 孙升, 张统一. 电解液中Cu(111)晶面电溶解/沉积势垒施加电荷相关性的跨尺度计算[J]. 电化学（中英文）, 2023, 29(10): 2205171-.
[14]	罗大娟, 刘冰倩, 覃蒙颜, 高荣, 苏丽霞, 苏永欢. 基于Au/rGO/FeOOH的新型电化学传感器一步检测亚硝酸盐[J]. 电化学（中英文）, 2022, 28(8): 2110191-.
[15]	谭柏照, 梁剑伦, 赖子亮, 罗继业. 高均匀性的铜柱凸块电镀[J]. 电化学（中英文）, 2022, 28(7): 2213004-.