电化学法制备Zn-Ni合金晶须

doi:10.61558/2993-074X.1887

电化学（中英文） ›› 2008, Vol. 14 ›› Issue (2): 180-183. doi: 10.61558/2993-074X.1887

电化学法制备Zn-Ni合金晶须

梁镇海;夏玺华;

太原理工大学化学化工学院,太原理工大学化学化工学院山西太原030024,山西太原030024

收稿日期:2008-05-28 修回日期:2008-05-28 出版日期:2008-05-28 发布日期:2008-05-28

Preparation of Zn-Ni Alloy Whisker by Electrochemical Method

LIANG Zhen-hai,XIA Xi-hua

(College of Chemistry and Chemical Engineering,Taiyuan University ofTechnology,Taiyuan 030024,Shanxi,China

Received:2008-05-28 Revised:2008-05-28 Published:2008-05-28 Online:2008-05-28

摘要/Abstract

摘要： 应用电化学方法制备Zn-Ni合金晶须.样品的成分、形貌用XRD、SEM、EDS等方法表征,结果表明,晶须的物相是Ni5Zn21和Ni3Zn22,直径250 nm,长度2~4μm,长径比8~16.同时用循环伏安法探讨了该过程的电化学行为.为晶须的制备提供了一种新的方法.

关键词: Ni5Zn21, Ni3Zn22, 晶须, 电化学

Abstract: The Zn-Ni alloy whiskers were prepared by electrochemical method and were characterized by XRD、SEM and EDS methods.The results showed that Ni5Zn21 and Ni3Zn22 whiskers were obtained with the length of 2~4 μm and the diameter of 250 nm,thereby the rations of length/diameter fell between 8 and 16.The electrochemical behavior was investigated by cyclic voltammetry method simultaneously.A new method was provided on whisker preparation based on this work.

Key words: Ni5Zn21, Ni3Zn22, whisker, electrochemistry

中图分类号:

TG146.13

梁镇海, 夏玺华, . 电化学法制备Zn-Ni合金晶须[J]. 电化学（中英文）, 2008, 14(2): 180-183.

LIANG Zhen-hai, XIA Xi-hua. Preparation of Zn-Ni Alloy Whisker by Electrochemical Method[J]. Journal of Electrochemistry, 2008, 14(2): 180-183.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.1887

https://electrochem.xmu.edu.cn/CN/Y2008/V14/I2/180

参考文献

[1]LI Wu(李武).Inorganic whisker[M].Beijing:Chemical Industry Press,2005.1-29. [2]Pradhan B,Batabyal S K,Amlan J.Vertically alignedZnO nanowire arrays in Rose Bengal-based dye-sensi-tized solar cells[J].Solar Energy Materials&SolarCells,2007,91,769-773. [3]Ntep J M,Said Hassani S,Lusson A,et al.ZnO growthby chemical vapour transport[J].Journal of CrystalGrowth,1999,207:30-34. [4]Eriko O,Oginoa H,Niikura I.Growth of the 2-in-sizebulk ZnO single crystals by the hydrothermal method[J].Journal of Crystal Growth,2004,260:166-170. [5]Wang X L,Xue D F.Direct observation of the shape e-volution of MgO whiskers in a solution system[J].Ma-terials Letters,2006,60:3160-3164. [6]Rohnke M,Best T,Janek J.Controlled electrochemicalgrowth on solid electrolytes[J].Journal of Solid StateElectrochemistry,2005,9:239-243. [7]Masatou I,Hisami Y,Kazuo A.Zinc-nickel alloywhiskers electrodeposited from a sulfate bath[J].Ma-terials Science and Engineering B,1996,38:150-155. [8]Liu J H(刘建华),Yang J W(杨敬武),Tang Z Y(唐致远).Study on cyclic volmammetry characteristics ofdoping Ni(OH)2[J].Journal of Tianjin University.2000,30:118-121. [9]Zimmermann D,Mun~oz AG,Schultze J W.Formationof Zn-Ni alloys in the phosphating of Zn layers[J].Surface&Coatings Technology,2005,197:260-269. [10]Zimmermann D,Mun~oz A G,Schultze J W.Micro-scopic local elements in the phosphating process[J].Electrochimica Acta,2003,48:3267-3277. [11]Petrauskas A,Grinceviciene L,Cesuniene A.Studiesof phase composition of Zn-Ni alloy obtained in acetate-chloride electrolyte by using XRD and potentiodynamicstripping[J].Electrochimica Acta,2005,50:1189-1196. [12]Petrauskas A,Grinceviciene L,Cesuniene A.Study ofphase composition of Zn-Ni alloy electrodeposited inacetate-chloride electrolyte at a temperature of 50℃[J].Electrochimica Acta,2006,51:4204-4209.

[1]	崔苗苗, 韩联欢, 曾兰平, 郭佳瑶, 宋维英, 刘川, 吴元菲, 罗世翊, 刘云华, 詹东平. 单层石墨烯微米尺度图案化和功能化：调控电子传输特性[J]. 电化学（中英文）, 2024, 30(3): 2305251-.
[2]	梁志豪, 王家正, 王丹, 周剑章, 吴德印. 陷阱态对Ag-TiO₂光诱导界面电荷转移的影响：电化学、光电化学和光谱表征[J]. 电化学（中英文）, 2023, 29(8): 2208101-.
[3]	谭卓, 李凯旋, 毛秉伟, 颜佳伟. 电化学扫描隧道显微术：以Cu在Au(111)表面初始阶段电沉积为例[J]. 电化学（中英文）, 2023, 29(7): 2216003-.
[4]	胡琼, 李诗琪, 梁伊依, 冯文星, 骆怡琳, 曹晓静, 牛利. 基于硼酸盐亲和辅助电化学调控ATRP的癌胚抗原超灵敏电化学适体传感研究[J]. 电化学（中英文）, 2023, 29(6): 2218001-.
[5]	覃晓丽, 詹子颖, Sara Jahanghiri, Kenneth Chu, 张丛洋, 丁志峰. 金属有机框架材料在电化学/电化学发光免疫分析中的应用[J]. 电化学（中英文）, 2023, 29(6): 2218003-.
[6]	静超, 龙亿涛. 暗场显微镜下的彩色“纳米星”[J]. 电化学（中英文）, 2023, 29(6): 2218006-.
[7]	张生雅, 姚敏, 王泽, 刘天娇, 张蓉芳, 叶慧琴, 冯彦俊, 卢小泉. 通过扫描光电化学显微镜研究超分子光敏剂-二氧化钛薄膜系统的光诱导电子转移[J]. 电化学（中英文）, 2023, 29(6): 2218005-.
[8]	陈涛, 许元红, 李景虹. 基于电化学阻抗谱的致病菌检测传感器的研究进展[J]. 电化学（中英文）, 2023, 29(6): 2218002-.
[9]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[10]	罗宇, 马如琴, 龚正良, 杨勇. 固态锂硫电池研究进展[J]. 电化学（中英文）, 2023, 29(3): 2217007-.
[11]	张芯婉, 孟广源, 方立强, 常定明, 李童, 胡锦文, 陈鹏, 刘勇弟, 张乐华. 基于BP神经网络的电化学还原硝酸盐过程智能控制[J]. 电化学（中英文）, 2023, 29(12): 211215-.
[12]	汪恒吉, 陈文国, 全周益, 赵凯, 孙毅飞, 陈旻, 奥坚科·弗拉基米尔. 多孔陶瓷支撑型管式固体氧化物电解池性能研究[J]. 电化学（中英文）, 2023, 29(12): 2204131-.
[13]	乔行, 朱勇, 孙升, 张统一. 电解液中Cu(111)晶面电溶解/沉积势垒施加电荷相关性的跨尺度计算[J]. 电化学（中英文）, 2023, 29(10): 2205171-.
[14]	罗大娟, 刘冰倩, 覃蒙颜, 高荣, 苏丽霞, 苏永欢. 基于Au/rGO/FeOOH的新型电化学传感器一步检测亚硝酸盐[J]. 电化学（中英文）, 2022, 28(8): 2110191-.
[15]	谭柏照, 梁剑伦, 赖子亮, 罗继业. 高均匀性的铜柱凸块电镀[J]. 电化学（中英文）, 2022, 28(7): 2213004-.

电化学法制备Zn-Ni合金晶须

Preparation of Zn-Ni Alloy Whisker by Electrochemical Method

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics