乙醛酸化学镀铜的电化学研究

电化学（中英文） ›› 2005, Vol. 11 ›› Issue (4): 402-406.

乙醛酸化学镀铜的电化学研究

吴丽琼;杨防祖;黄令;孙世刚;周绍民;

厦门大学化学化工学院固体表面物理化学国家重点实验室,厦门大学化学化工学院固体表面物理化学国家重点实验室,厦门大学化学化工学院固体表面物理化学国家重点实验室,厦门大学化学化工学院固体表面物理化学国家重点实验室,厦门大学化学化工学院固体表面物理化学国家重点实验室福建厦门361005,福建厦门361005,福建厦门361005,福建厦门361005,福建厦门361005

收稿日期:2005-11-28 修回日期:2005-11-28 出版日期:2005-11-28 发布日期:2005-11-28

An Electrochemical Study of Electroless Copper Plating Using Glyoxylic Acid as Reducing Agent

WU Li-Qiong,YANG Fang-Zu~

(*),HANG Ling,SUN Shi-Gang,ZHOU Shao-Min(College of Chemistry and Chemical Engineering,State Key Laboratory ofPhysical Chemistry of the Solid Surfaces,Xiamen University,Xiamen 361005,China

Received:2005-11-28 Revised:2005-11-28 Published:2005-11-28 Online:2005-11-28

摘要/Abstract

摘要： 以乙醛酸作还原剂,Na2EDTA.2H2O为络合剂,亚铁氰化钾和2,2'-联吡啶为添加剂组成化学镀铜液体系,应用线性扫描伏安法研究分析了络合剂、添加剂对该镀铜体系电化学性能的影响.结果表明,络合剂Na2EDTA对乙醛酸的氧化和铜的还原有阻碍作用.亚铁氰化钾和过量(20 mg/L)的2,2'-联吡啶对乙醛酸的氧化起较明显的抑制作用.

关键词: 化学镀铜, 乙醛酸, 络合剂, 添加剂

Abstract: The electroless copper plating using glyoxylic acid as a reducing agent,Na_(2)EDTA as a chelating agent and K_(4)Fe(CN)_(6) and 2,2'-dipyridyl as additives was studied.The effect of chelating agent and addtives on the polangation behaviovs of copper reduction and glyoxylie acid oxidation were analyzed by linear sweep voltammetry.The results mainly demonstrated that the chelating agent hindered both the oxidation of glyoxylic acid and the reduction of copper complexing ions.It has revealed that K_(4)Fe(CN)_(6)and 2,2'-dipyridyl(with the content over than 20 mg/L)both played negative actions on the oxidation of glyoxylic acid.

Key words: Electroless copper plating, glyoxylic acid, Chelating agent, Additives, Polarization

中图分类号:

TQ153

吴丽琼;杨防祖;黄令;孙世刚;周绍民;. 乙醛酸化学镀铜的电化学研究[J]. 电化学（中英文）, 2005, 11(4): 402-406.

WU Li-Qiong,YANG Fang-Zu~. An Electrochemical Study of Electroless Copper Plating Using Glyoxylic Acid as Reducing Agent[J]. Journal of Electrochemistry, 2005, 11(4): 402-406.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2005/V11/I4/402

参考文献

[1]Yosi Shacham-D iam and,Sergey Lopatin.Integratedelectroless m etallization for ULSI[J].E lectroch im icaActa,1999,44:3639~3649. [2]Garza M,L iu J.Adhesion behavior of electroless deposi-ted Cu on Pt/Ta silicate and Pt/S iO2[J].App lied Sur-face Sc ience,2004,222:253~262. [3]Jiang X iao-X ia(姜晓霞),Shen W e i(沈伟).The fun-dam entals and practice of electroless p lating[M].Be i-jing:National Defence Industry Press,2000:13~19. [4]Paunovic M.E lectrochem ical aspects of electroless depo-sition ofm etals[J].P lating,1968,55:1 161~1 167. [5]Honm a H,Kobayash i T.E lectroless copper despositionpresence using glyoxylic ac id as a reduc ing agent[J].J.E lectrochem.Soc.,1994,141(3):730~733. [6]L in Y i-M ao,Yen Sh i-Chern.E ffects of add itives andchelating agents on electroless copper p lating[J].App l.Surf.Sc i.,2001,178(3):116~126. [7]Vas kelis A,Jus ke nas R,and Jac iausk ien J.Copperhydride form ation in the electroless copper p latingprocess:in situ x-ray d iffraction evidence and electro-chem ical study[J].E lectroch im ica.Acta,1998,43(9):1 061~1 066. [8]B indra P,Roldan J.M echan ism of electroless m etalp lating[J].J.E lectrochem.Soc.,1985,132(11):2581. [9]Burke L D,Ahern M J G,Ryan T G.An investigationof the anod ic behavior of copper and its anod ically pro-duced oxides in aqueous solutions of h igh pH[J].J.E lectrochem.Soc.,1990,137(2):553. [10]Jun L i,HarleyHayden,Pau lA Kohl.The influence of2,2'-d ipyridyl on non-form aldehyde electroless cop-per p lating[J].E lectroch im ica Acta.,2004,49:1 789~1 795. [11]Deposition rate and morphology of electroless copperfilm from solutions contain ing 2,2'-d ipyridyl[J].E lectroch im ica.Acta,1997,42(9):1 435~1 440. [12]Nuzzi F J.Accelerating the rate of electroless copperplating[J].Plat&Surf.Finish,1983,70(1):51~54. [13]Hung A.E ffects of th iourea guan id ine hydrochloride onelectroless copper p lating[J].J.E lectrochem.Soc.,1985,132(5):1 047~1 049.

[1]	张修庆, 唐帅, 付永柱. 锂硫电池电解液功能性添加剂研究进展[J]. 电化学（中英文）, 2023, 29(4): 2217005-.
[2]	谭柏照, 梁剑伦, 赖子亮, 罗继业. 高均匀性的铜柱凸块电镀[J]. 电化学（中英文）, 2022, 28(7): 2213004-.
[3]	沈钰, 李冰冰, 马艺, 王增林. 化学镀钴和超级化学镀填充的研究进展[J]. 电化学（中英文）, 2022, 28(7): 2213002-.
[4]	徐佳莹, 王守绪, 苏元章, 杜永杰, 齐国栋, 何为, 周国云, 张伟华, 唐耀, 罗毓瑶, 陈苑明. 特殊整平剂甲基橙在通孔电镀铜的应用[J]. 电化学（中英文）, 2022, 28(7): 2213003-.
[5]	纪执敬, 凌惠琴, 吴培林, 余瑞益, 于大全, 李明. 玻璃通孔三维互连镀铜填充技术发展现状[J]. 电化学（中英文）, 2022, 28(6): 2104461-.
[6]	杨森, 王文昌, 张然, 秦水平, 吴敏娴, 光崎尚利, 陈智栋. 醇硫基丙烷磺酸钠对电解高性能锂电铜箔的影响[J]. 电化学（中英文）, 2022, 28(6): 2104501-.
[7]	杨凯, 陈际达, 陈世金, 许伟廉, 郭茂桂, 廖金超, 吴熷坤. 高深径比通孔脉冲电镀添加剂及电镀参数的优化[J]. 电化学（中英文）, 2022, 28(6): 2104491-.
[8]	缪桦, 李明瑞, 邹文中, 周国云, 王守绪, 叶晓菁, 朱凯. Sn-Ag-Cu三元合金焊料电沉积中添加剂的影响研究[J]. 电化学（中英文）, 2022, 28(6): 2104411-.
[9]	战充波, 张润佳, 付旭, 孙海静, 周欣, 王保杰, 孙杰. 氯离子对ChCl-Urea低共熔溶剂中银电沉积的电化学行为影响[J]. 电化学（中英文）, 2022, 28(5): 2111151-.
[10]	谢茂玲, 王钧, 胡晨吉, 郑磊, 孔华彬, 沈炎宾, 陈宏伟, 陈立桅. 基于非亲核电解液构建稳定的镁离子电池[J]. 电化学（中英文）, 2022, 28(3): 2108561-.
[11]	黄波, 张新胜, 钮东方, 胡硕真. 对称季铵碱的烷基链长度对草酸电还原反应的影响[J]. 电化学（中英文）, 2021, 27(5): 529-539.
[12]	张彪, 帅毅, 王玉, 杨纳川, 陈康华. 碳酸酯类电解液中Mg(NO₃)₂添加剂抑制锂枝晶生长的研究[J]. 电化学（中英文）, 2021, 27(4): 423-428.
[13]	王赵云, 金磊, 杨家强, 李威青, 詹东平, 杨防祖, 孙世刚. 高密度互连印制电路板孔金属化研究和进展[J]. 电化学（中英文）, 2021, 27(3): 316-331.
[14]	王翀, 彭川, 向静, 陈苑明, 何为, 苏新虹, 罗毓瑶. 印制电路中电镀铜技术研究及应用[J]. 电化学（中英文）, 2021, 27(3): 257-268.
[15]	常增花, 韩富娟, 杨夕馨, 王建涛, 卢世刚. 纳米硅在含添加剂的高浓度电解液中循环特征及其表面协同成膜的研究[J]. 电化学（中英文）, 2020, 26(5): 759-771.