纯钯电沉积及其成核机理研究

摘要/Abstract

摘要： 研究在柠檬酸钾和草酸铵镀液体系中纯钯电沉积及电结晶机理．结果表明，采用本实验室研制的添加剂②ＸＰ－４和ＸＰ－７，可在电流密度０．５～３．５Ａ／ｄｍ２，温度４０～６０℃的宽广范围内获得全光亮的钯电沉积积层．采用脉冲电源电镀可有效地改善厚沉积层质量，减少沉积层裂纹和孔洞．循环伏安实验表明，钯电极过程的阴阳极峰电位之差达１．０５Ｖ，说明其电极过程明显不可逆；伏安图上同时出现一感抗性电流环，说明钯沉积过程发生晶核形成过程；ＸＰ－４和ＸＰ－７阻化电沉积和氢的析出，提高钯电沉积的沉积电位．电位阶跃实验进一步表明，钯遵循连续成核和三－维生长的电结晶机理．

关键词: 钯, 电沉积, 成核, 脉冲电镀

Abstract: The electrodeposition and nucleation of palladium are studied in the system of potassium citrate and ammonium oxalate. The results show that, with the additives of XP 4 and XP 7 prepared in our laboratory, a full bright palladium electrodeposits will be obtained in the wide ranges of the cathode current densities 0.5～3.5 A/dm 2 and temperature 40～60 ℃; the qualities of the thick deposits will be effectively improved by means of pulse current plating. Cyclic voltammograms results show that the division of peaks between anodic and cathodic on the electrode process of palladium will be up to 1.05 V, which shows the irreversible electrode process; and a inductive current cycle is appeared,which means the process of nucleation; XP 4 and XP 7 inhibit both palladium electrodeposition and hydrogen evolution, therefore cause the deposition potential of palladium to more negative; potential step experiments furtherly show that the nucleation of palladium obeyed progressive uncleation mechanism both with the studied additives or without them.

Key words: Palladium, Electrodeposition, Nucleation, Pulse electroplation

中图分类号:

O646.541

杨防祖,许书楷,姚士冰,陈秉彝,郑雪清,钟晓慧,周绍民. 纯钯电沉积及其成核机理研究[J]. 电化学（中英文）, 1997, 3(1): 103-108.

Yang Fangzu Xu Shukai Yao Shibing Chen Bingyi Zheng Xueqing Zhong Xiaohui Zhou Shaomin . A Study on the Electrodeposition of Palladium and it′s Nucleation[J]. Journal of Electrochemistry, 1997, 3(1): 103-108.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y1997/V3/I1/103

参考文献

1RonaldJMorrissey．Rhodiumplating．PlatingandSurfaceFinishing，1995，82（8）：692JosephAAbys．Paladiumplating．PlatingandSurfaceFinishing，1995，82（8）：67～683LEPenvenR，LevasonW，PletcherD．StudiesofpaladiumelectrodepositionfrombathsbasedonPd（NH3）2X2Salts．I：［Pd（NH3）2Cl2］baths．J．Appl．Electrochem．，1992，20：399～4044LEPenvenR，LevasonW，PletcherD．StudiesofpaladiumelectrodepositionfrombathsbasedonPd（NH3）2X2．PartII：X＝BrandX＝NO2．J．Appl．Electrochem．，1992，22：421～4245JayakrishnanS，NatarajanRS．Hydrogencodepositioninpaladiumplating．MetalFinishing，1991，89（1）：23～256LaiCK，WangYY，WanCC．Paladiumelectrodepositionfromammonia－freeelectrolyte．J．Elec－troanal．Chem．，1992，322：267～2787Su－IlPyun，ChanLim．Asutdyontheelectrodepositionmechanismofplaladiumfromammoniacalsolu－tionusingarotatingPtRing－Cudiskelectrode．TRansactionsoftheInstituteofMetalFinishing，1993，71（4）：156～1608StraschilHK，AbbysJA，KudrrakEJetal．Newpaladiumstrikeimprovesadhensionandporosity．MetalFinishing，1992，90（1）：42～479KudrakEJ，AbbysJA，ChinchankarV，JJMaisano．Porosityofcompositepaladium，paladium－nickelandgoldelectrodeosits．PlatingandSurfaceFinishing，1992，79（2）：49～5510EnyoM，BiswasPC．Hydrogenabsorptioninpaladiumelectrodesinalkalinesolution．J．Electroanal．Chem．，1992，335：309～31911GrimmRD，LandoltD．Investigationoftheinfluenceofpulseparametersoncrackformationinpaladi－umelectrodeposits．SurfaceandCoatingsTechnology，1987，31（2）：151～16112MartinJL，TobenMP．Paladiumandpaladiumaloyelectrodepositsintheelectronicsindustry．MetalFinishing，1990，88（1）：39～4113GrahamAH，Pike－BiegunskiMJ，UpdegraffSW．Evaluationofpaladiumsubstitutesforgold．Plat－ingandSurfaceFinishing，1983，70（11）：52～5714FukumotoY，KawashimaY，HandaK，HayashiY．Pulsecurrentelectrodepositionofpaladium．MetalFinishing，1984，82（9）：77～8015MartinJL，McCaskieJE，TobenMP．Paladiumplating．USpatent4，622，110（Nov．11，1986）and4，545，868（Oct．8，1985）16FredINovel，JamesLMartin，MichaelPToben．Alkalinebathsandmethodsforelectrodepositionofpaladiumandpaladiumaloys．EuropeanPatentApplication0225422（June6，86）17FredINovel，SandsPoint，JamesLMartinelal．Alkalinebathsandmethodsforelectrodepositionofpaladiumandpaladiumaloys．USPatent4，741，818（May5，1988）18AbysJAetal．Paladiumcomplexant．USPatent4，911，798（Mar．27，1990）19AbysJAetal．Paladiumadditives．USPatent4，911，799（Mar．27，1990）20FranklinTC．Somemechanismsofactionofadditivesinelectrodepositionprocesses．SurfaceandCoat－ingsTechnology，1987，30：415～42821周绍民等编著．金属电沉积—原理与研究方法．上海：上海科学技术出版社，1987，284～30522FletcherS．Somenewformulaeaplicabletoelectrochemicalnucleationgrowth／colision．ElectrochimicaActa，1983，28（7）：917～92323ScharifkerB，HilsG．Theoreticalandexperimentalstudiesofmultiplenucleation．ElectrochimicaActa，1983，28（7）：879～889

[1]	丁伟杰, 杨春晖, 冯钟涛, 陆仕荣, 程旭. 钯催化电化学烯丙位4-吡啶化反应中的配体作用研究[J]. 电化学（中英文）, 2024, 30(5): 2313003-.
[2]	王玉玺, 高丽茵, 万永强, 李哲, 刘志权. 应用于大马士革工艺的纳米孪晶铜脉冲电沉积研究[J]. 电化学（中英文）, 2023, 29(8): 2209231-.
[3]	谭卓, 李凯旋, 毛秉伟, 颜佳伟. 电化学扫描隧道显微术：以Cu在Au(111)表面初始阶段电沉积为例[J]. 电化学（中英文）, 2023, 29(7): 2216003-.
[4]	张俊明, 张小杰, 陈瑶, 房英健, 樊友军, 贾建峰. 低共熔溶剂辅助合成新型的网状纳米结构用于加速甲酸电氧化[J]. 电化学（中英文）, 2023, 29(5): 2206231-.
[5]	吴炜星, 王莹. 乙烯在钯圆盘电极的电化学氧化研究[J]. 电化学（中英文）, 2023, 29(1): 2215004-.
[6]	杨家强, 金磊, 李威青, 王赵云, 杨防祖, 詹东平, 田中群. 亚硫酸盐无氰电沉积金新工艺及机制[J]. 电化学（中英文）, 2022, 28(7): 2213005-.
[7]	孙云娜, 吴永进, 谢东东, 蔡涵, 王艳, 丁桂甫. 硅通孔内铜电沉积填充机理研究进展[J]. 电化学（中英文）, 2022, 28(7): 2213001-.
[8]	黄葵, 黄容姣, 刘素琴, 何震. 电子功能外延薄膜的电沉积[J]. 电化学（中英文）, 2022, 28(7): 2213006-.
[9]	倪修任, 张雅婷, 王翀, 洪延, 陈苑明, 苏元章, 何为, 陈先明, 黄本霞, 续振林, 李毅峰, 李能彬, 杜永杰. 电沉积纳米锥镍的生长机理及其性能的研究[J]. 电化学（中英文）, 2022, 28(7): 2213008-.
[10]	马晓川, 李亚强, 杨培霞, 张锦秋, 安茂忠. 孔雀石绿对金属钴超填充和成核过程的影响[J]. 电化学（中英文）, 2022, 28(6): 2104521-.
[11]	张远航, 安茂忠, 杨培霞, 张锦秋. 数值模拟方法在周期换向脉冲电镀通孔中的应用[J]. 电化学（中英文）, 2022, 28(6): 2104511-.
[12]	魏丽君, 周紫晗, 吴蕴雯, 李明, 王溯. 芯片钴互连及其超填充电镀技术的研究进展[J]. 电化学（中英文）, 2022, 28(6): 2104431-.
[13]	赵健伟, 朱海锋, 于晓辉, 袁桂云, 孙志. 蚀刻引线框架用的弱碱性无氰镀银工艺的研究[J]. 电化学（中英文）, 2022, 28(6): 2104551-.
[14]	杨凯, 陈际达, 陈世金, 许伟廉, 郭茂桂, 廖金超, 吴熷坤. 高深径比通孔脉冲电镀添加剂及电镀参数的优化[J]. 电化学（中英文）, 2022, 28(6): 2104491-.
[15]	缪桦, 李明瑞, 邹文中, 周国云, 王守绪, 叶晓菁, 朱凯. Sn-Ag-Cu三元合金焊料电沉积中添加剂的影响研究[J]. 电化学（中英文）, 2022, 28(6): 2104411-.