经由[Ni(en)3](SeO3)配合物电镀制备的硒化镍高效电催化水分解反应

doi:10.13208/j.electrochem.181141

摘要/Abstract

摘要： 电催化水分解是一种高效制备清洁氢气能源的有效方法. 开发高效、稳定、廉价、双功能的电催化剂用于水的氧化与还原反应一直以来都是具有挑战的课题. 在这篇论文中，作者报道了一种生长在碳布上高活性的硒化镍微球. 该催化剂通过对同时包含镍和硒元素的亚硒酸镍配合物进行电解制备. 由于前驱分子同时含有两种有效元素，制备得到的硒化镍具有很好的形貌和元素分步均一性. 制备得到的NiSe-EA/CC电极能够双功能催化水的氧化与还原. 在154 mV析氢过电势下能达到10 mA·cm^-2的催化电流. 同时，在250 mV析氧过电势下能达到20 mA·cm^-2电催化电流. 用该电极材料同时作为阴极和阳极制备的全电解水电解池能在1.53 V的电压下实现10 mA·cm^-2的稳定电解电流.

关键词: 电催化, 硒化镍, 水分解, 析氢反应, 析氧反应

Abstract: Electrocatalytic water splitting is considered as a promising technology for renewable energy. The development of efficient, stable, cost-effective, and bifunctional catalysts for both water reduction and oxidation has continued to face significant challenges. Herein, we report a robust and highly active nickel selenide (NiSe) spheres grown on carbon cloth (CC) by electrodeposition from a nickel selenite complex which is a single source containing both Ni and Se. A combination of two chemicals containing, separately, Ni and Se is used in traditional preparations of metal selenides, causing possible problems in the uniformity of the products. The as-prepared NiSe-EA/CC electrode exhibited electrocatalytic activities toward both water reduction and oxidation, with overpotentials of 154 mV at 10 mA·cm^-2 and 250 mV at 20 mA·cm^-2, respectively. A water electrolysis cell could realize a current density of 10 mA·cm^-2 at a cell voltage of 1.53 V with excellent stability, when using NiSe-EA/CC electrode as both the anode and the cathode.

Key words: electrocatalysis, nickel selenide, water splitting, hydrogen evolution reaction, oxygen evolution reaction

中图分类号:

O646

陈丹丹, 高学庆, 刘红飞, 张伟, 曹睿. 经由[Ni(en)₃](SeO₃)配合物电镀制备的硒化镍高效电催化水分解反应[J]. 电化学（中英文）, 2019, 25(5): 553-561.

CHEN Dan-dan, GAO Xue-qing, LIU Hong-fei, ZHANG Wei, CAO Rui. Nickel Selenide Derived from [Ni(en)₃](SeO₃) Complex for Efficient Electrocatalytic Overall Water Splitting[J]. Journal of Electrochemistry, 2019, 25(5): 553-561.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.181141

https://electrochem.xmu.edu.cn/CN/Y2019/V25/I5/553

参考文献

[1] Qi J, Zhang W, Cao R. Solar-to-hydrogen energy conversion based on water splitting[J]. Advanced Energy Materials, 2018, 8(5): 1701620.
[2] Zhang X Q, Cheng X B, Zhang Q. Nanostructured energy materials for electrochemical energy conversion and storage: A review[J]. Journal of Energy Chemistry, 2016, 25(6): 967-984.
[3] Dou S, Tao L, Wang R L, et al. Plasma-assisted synthesis and surface modification of electrode materials for renewable energy[J]. Advanced Materials, 2018, 30(21): 1705850.
[4] Duan X C, Xu J T, Ma J M, et al. Atomically thin transition-metal dichalcogenides for electrocatalysis and energy storage[J]. Small Methods, 2017, 1(11): 1700156.
[5] Qi J, Zhang W, Cao R. Porous materials as highly efficient electrocatalysts for the oxygen evolution reaction[J]. ChemCatChem, 2018, 10(6): 1206-1220.
[6] Zhu W X, Yue X Y, Zhang W T, et al. Nickel sulfide microsphere film on Ni foam as an efficient bifunctional electrocatalyst for overall water splitting[J]. Chemical Communications, 2016, 52(7): 1486-1489.
[7] Li X, Zhang L, Huang M R, et al. Cobalt and nickel selenide nanowalls anchored on graphene as bifunctional electrocatalysts for overall water splitting[J]. Journal of Materials Chemistry A, 2016, 4(38): 14789-14795.
[8] Hou C C, Cao S, Fu W F, et al. Ultrafine CoP nanoparticles supported on carbon nanotubes as highly active electrocatalyst for both oxygen and hydrogen evolution in basic media[J]. ACS Applied Materials & Interfaces, 2015, 7(51): 28412-28419.
[9] Liu H F, Gao X Q, Yao X L, et al. Manganese(II) phosphate nanosheet assembly with native out-of-plane Mn centres for electrocatalytic water oxidation[J]. Chemical Science, 2018,10(1): 191-197.
[10] Wan S, Qi J, Zhang W, et al. Hierarchical Co(OH)F superstructure built by low-dimensional substructures for electrocatalytic water oxidation[J]. Advanced Materials, 2017, 29(28): 1700286.
[11] Tian J Q, Liu Q, Asiri A M, et al. Self-supported nanoporous cobalt phosphide nanowire arrays: An efficient 3D hydrogen-evolving cathode over the wide range of pH 0-14[J]. Journal of the American Chemical Society, 2014, 136(21): 7587-7590.
[12] Zhou W J, Wu X J, Cao X H, et al. Ni₃S₂ nanorods/Ni foam composite electrode with low overpotential for electrocatalytic oxygen evolution[J]. Energy & Environmental Science, 2013, 6(10): 2921-2924.
[13] Zhang M T, Chen Z, Kang P, et al. Electrocatalytic water oxidation with a copper(II) polypeptide complex[J]. Journal of the American Chemical Society, 2013, 135(6): 2048-2051.
[14] Wu Y Z, Chen M X, Han Y Z, et al. Fast and simple preparation of iron-based thin films as highly efficient water-oxidation catalysts in neutral aqueous solution[J]. Angewandte Chemie International Edition, 2015, 54(16): 4870-4875.
[15] Chen M X, Qi J, Zhang W, et al. Electrosynthesis of NiP_x nanospheres for electrocatalytic hydrogen evolution from a neutral aqueous solution[J]. Chemical Communications, 2017, 53(40): 5507-5510.
[16] Gao Z, Qi J, Chen M X, et al. An electrodeposited NiSe for electrocatalytic hydrogen and oxygen evolution reactions in alkaline solution[J]. Electrochimica Acta, 2017, 224: 412-418.
[17] Hernandez-Pagan E A, Vargas-Barbosa N M, Wang T H, et al. Resistance and polarization losses in aqueous buffer-membrane electrolytes for water-splitting photoelectrochemical cells[J]. Energy & Environmental Science, 2012, 5(6): 7582-7589.
[18] McCrory C C L, Jung S, Ferrer I M, et al. Benchmarking hydrogen evolving reaction and oxygen evolving reaction electrocatalysts for solar water splitting devices[J]. Journal of the American Chemical Society, 2015, 137(13): 4347-4357.
[19] Bau J A, Luber E J, Buriak J M. Oxygen evolution catalyzed by nickel-iron oxide nanocrystals with a nonequilibrium phase[J]. ACS Applied Materials & Interfaces, 2015, 7(35): 19755-19763.
[20] Gao Y G, Li H B, Yang G W. Amorphous nickel hydroxide nanosheets with ultrahigh activity and super-long-term cycle stability as advanced water oxidation catalysts[J]. Crystal Growth & Design, 2015, 15(9): 4475-4483.
[21] Tang D, Liu J, Wu X Y, et al. Carbon quantum dot/NiFe layered double-hydroxide composite as a highly efficient electrocatalyst for water oxidation[J]. ACS Applied Materials & Interfaces, 2014, 6(10): 7918-7925.
[22] Wang T x, Li X, Jiang Y M, et al. Reduced graphene oxide-polyimide/carbon nanotube film decorated with NiSe nanoparticles for electrocatalytic hydrogen evolution reactions[J]. Electrochimica Acta, 2017, 243: 291-298.
[23] Li Y X, Yan D F, Zou Y Q, et al. Rapidly engineering the electronic properties and morphological structure of NiSe nanowires for the oxygen evolution reaction[J]. Journal of Materials Chemistry A, 2017, 5(48): 25494-25500.
[24] Wang F M, Li Y C, Shifa TA, et al. Selenium-enriched nickel selenide nanosheets as a robust electrocatalyst for hydrogen generation[J]. Angewandte Chemie International Edition, 2016, 55(24): 6919-6924.
[25] Zhao Q, Zhong D Z, Liu L, et al. Facile fabrication of robust 3D Fe-NiSe nanowires supported on nickel foam as a highly efficient, durable oxygen evolution catalyst[J]. Journal of Materials Chemistry A, 2017, 5(28): 14639-14645.
[26] Zhang W, Qi J, Liu K Q, et al. A nickel-based integrated electrode from an autologous growth strategy for highly efficient water oxidation[J]. Advanced Energy Materials, 2016, 6(12): 1502489.
[27] Akbar K, Jeon J H, Kim M, et al. Bifunctional electrodeposited 3D NiCoSe₂/nickle foam electrocatalysts for its applications in enhanced oxygen evolution reaction and for hydrazine oxidation[J]. ACS Sustainable Chemistry & Engineering, 2018, 6(6): 7735-7742.
[28] Swesi A T, Masud J, Nath M. Nickel selenide as a high-efficiency catalyst for oxygen evolution reaction[J]. Energy & Environmental Science, 2016, 9(5): 1771-1782.
[29] Liu F Y, Wang B, Lai Y Q, et al. Electrodeposition of cobalt selenide thin films[J]. Journal of the Electrochemical Society, 2010, 157(10): D523-D527.
[30] Xiao P, Chen W, Wang X. A review of phosphide-based materials for electrocatalytic hydrogen evolution[J]. Advanced Energy Materials, 2015, 5(24): 1500985.
[31] Liu Z J, Zhao Z H, Wang Y Y, et al. In situ exfoliated, edge-rich, oxygen-functionalized graphene from carbon fibers for oxygen electrocatalysis[J]. Advanced Materials, 2017, 29(18): 1606207.
[32] Mi L W, Sun H, Ding Q, et al. 3D hierarchically patterned tubular NiSe with nano-/microstructures for Li ion battery design[J]. Dalton Transactions, 2012, 41(40): 12595-12600.
[33] Kukunuri S, Krishnan M R, Sampath S. The effect of structural dimensionality on the electrocatalytic properties of the nickel selenide phase[J]. Physical Chemistry Chemical Physics, 2015, 17(36): 23448-23459.
[34] Biesinger M C, Payne B P, Lau L W M, et al. X-ray photoelectron spectroscopic chemical state quantification of mixed nickel metal, oxide and hydroxide systems[J]. Surface and Interface Analysis, 2009, 41(4): 324-332.
[35] Tang C, Cheng N Y, Pu Z H, et al. NiSe nanowire film supported on nickel foam: An efficient and stable 3D bifunctional electrode for full water splitting[J]. Angewandte Chemie International Edition, 2015, 54(32): 9351-9355.
[36] Frost RL, Keeffe E C. Raman spectroscopic study of the selenite mineral: Ahifeldite, NiSeO₃·2H₂O[J]. Journal of Raman Spectroscopy, 2009, 40(5): 509-512.
[37] Zhou X M, Gao P, Sun S C, et al. Amorphous, crystalline and crystalline/amorphous selenium nanowires and their different (de)lithiation mechanisms[J]. Chemistry of Materials, 2015, 27(19): 6730-6736.
[38] Qi J, Zhang W, Cao R. Aligned cobalt-based Co@CoO_x nanostructures for efficient electrocatalytic water oxidation[J]. Chemical Communications, 2017, 53(66): 9277-
9280.
[39] Song D Y, Wang H Q, Wang X Q, et al. NiSe₂ nanoparticles embedded in carbon nanowires as highly efficient and stable electrocatalyst for hydrogen evolution reaction[J]. Electrochimica Acta, 2017, 254: 230-237.
[40] Louie M W, Bell A T. An investigation of thin-film Ni-Fe oxide catalysts for the electrochemical evolution of oxygen[J]. Journal of the American Chemical Society, 2013, 135(33): 12329-12337.

经由[Ni(en)₃](SeO₃)配合物电镀制备的硒化镍高效电催化水分解反应

Nickel Selenide Derived from [Ni(en)₃](SeO₃) Complex for Efficient Electrocatalytic Overall Water Splitting

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	万紫轩, Aidar Kuchkaev, Dmitry Yakhvarov, 康雄武. 单分散Cu-TCPP/Cu₂O杂化微球:一种具有优异电还原CO₂产C₂性能的级联电催化剂[J]. 电化学（中英文）, 2024, 30(1): 2303271-.
[2]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[3]	丁明宇, 蒋文杰, 余天琦, 卓小燕, 覃晓静, 尹诗斌. CeO₂电子调控FeNi纳米片大电流密度电解水催化剂[J]. 电化学（中英文）, 2023, 29(5): 2208121-.
[4]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[5]	冯辛, 刘博文, 郭可鑫, 范林丰, 王根香, 次素琴, 温珍海. 基于阳极甘油氧化电催化的碱/酸混合电解制氢研究[J]. 电化学（中英文）, 2023, 29(2): 2215005-.
[6]	孟庆成, 金林薄, 马梦泽, 高学庆, 陈爱兵, 周道金, 孙晓明. 层状金属氢氧化物中铁位点辅助分散铂纳米颗粒用于高效甲醇氧化[J]. 电化学（中英文）, 2023, 29(2): 2215007-.
[7]	韦宗楠, 曹敏纳, 曹荣. 瓜环基金属纳米催化剂的电化学研究进展[J]. 电化学（中英文）, 2023, 29(1): 2215008-.
[8]	李家欣, 冯立纲. 析氧反应铁镍基预催化剂的表界面调控与进展[J]. 电化学（中英文）, 2022, 28(9): 2214001-.
[9]	郭鸿波, 王亚妮, 郭凯, 雷海涛, 梁作中, 张学鹏, 曹睿. 吸电子和亲水性Co-卟啉促进电催化氧还原反应的研究[J]. 电化学（中英文）, 2022, 28(9): 2214002-.
[10]	郭丹丹, 俞红梅, 迟军, 邵志刚. 自支撑NiFe LDHs@Co-OH-CO₃纳米棒阵列电极用于碱性阴离子交换膜电解水[J]. 电化学（中英文）, 2022, 28(9): 2214003-.
[11]	梁宵, 张可新, 沈雨澄, 孙轲, 石磊, 陈辉, 郑克岩, 邹晓新. 钙钛矿型水氧化电催化剂[J]. 电化学（中英文）, 2022, 28(9): 2214004-.
[12]	周澳, 郭伟健, 王月青, 张进涛. 焦耳热快速合成双功能电催化剂用于高效水分解[J]. 电化学（中英文）, 2022, 28(9): 2214007-.
[13]	王英超, 马自在, 吴一凡, 王孝广. GCP载钯颗粒复合材料的制备及其电化学合成氨性能研究[J]. 电化学（中英文）, 2022, 28(5): 2104091-.
[14]	张天恩, 颜雅妮, 张俊明, 瞿希铭, 黎燕荣, 姜艳霞. 调控Pt₃Zn合金化程度改善酸性氧还原活性与稳定性[J]. 电化学（中英文）, 2022, 28(4): 2106091-.
[15]	Jafar Hussain Shah, 谢起贤, 匡智崇, 格日乐, 周雯慧, 刘朵绒, Alexandre I. Rykov, 李旭宁, 罗景山, 王军虎. 原位 ⁵⁷Fe穆斯堡尔光谱技术及其在Ni-Fe基析氧反应电催化剂中的应用[J]. 电化学（中英文）, 2022, 28(3): 2108541-.