Pt纳米花/ZnO复合阵列的制备及对甲醇氧化催化的研究

doi:10.61558/2993-074X.2019

电化学（中英文） ›› 2009, Vol. 15 ›› Issue (4): 426-431. doi: 10.61558/2993-074X.2019

Pt纳米花/ZnO复合阵列的制备及对甲醇氧化催化的研究

高莉;鄂义峰;范楼珍;

北京师范大学化学学院;

收稿日期:2009-11-28 修回日期:2009-11-28 出版日期:2009-11-28 发布日期:2009-11-28

Preparation of Pt Nanoflower/ZnO Composites Arrays and Their Electrocatalysis for Methanol Oxidation

GAO Li,E Yi-feng,FAN Lou-zhen*

(Department of Chemistry,Beijing Normal University,Beijing 100875,China

Received:2009-11-28 Revised:2009-11-28 Published:2009-11-28 Online:2009-11-28

摘要/Abstract

摘要： 利用调控ZnO纳米棒阵列的疏水、亲水性,由电化学方法制备了Pt纳米花/ZnO(PtNF/ZnO)复合阵列.该复合阵列排列规则、尺寸均一、方向一致.每一根ZnO纳米棒的顶端都覆盖着由Pt纳米颗粒构成的Pt纳米花,具有大的比表面积.与以亲水性的ZnO纳米棒制得的覆盖Pt纳米颗粒的ZnO复合阵列(PtNP/ZnO)以及单独的Pt颗粒相比,PtNF/ZnO复合阵列对甲醇氧化具有更高的电化学催化活性.

关键词: Pt纳米花/ZnO复合阵列, 电沉积, 直接甲醇燃料电池

Abstract: The Pt nanoflower/ZnO(PtNF/ZnO) nanorod composites arrays were electrochemically prepared by controlling the hydrophobicity and the hydrophilicity of ZnO nanorods arrays.The Pt nanoflowers grew on the tip of ZnO nanorods,which maintain the vertical array of Zno nanorods with a high degree of size uniformity and high surface area.Compared with Pt nanoparticle covered ZnO nanorod arrays,which were prepared by controlling the hydrophilicities of ZnO nanorods and Pt nanoparticles,the PtNF/ZnO displayed highest electrocatalytic activities for the oxidation of methanol.

Key words: Pt nanoflower/ZnO nanorod composites arrays, electrodeposition, direct methanol fuel cell

中图分类号:

高莉, 鄂义峰, 范楼珍, . Pt纳米花/ZnO复合阵列的制备及对甲醇氧化催化的研究[J]. 电化学（中英文）, 2009, 15(4): 426-431.

GAO Li, E Yi-feng, FAN Lou-zhen. Preparation of Pt Nanoflower/ZnO Composites Arrays and Their Electrocatalysis for Methanol Oxidation[J]. Journal of Electrochemistry, 2009, 15(4): 426-431.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2019

https://electrochem.xmu.edu.cn/CN/Y2009/V15/I4/426

参考文献

[1]Chen C Y,Yang P.Performance of an air-breathing di-rect methanol fuel cell[J].J Power Sources,2003,123:37-42. [2]Arico A S,Srinivasan S,Antonucci V.DMFCs:fromfundamental aspects to technology development[J].Fu-el Cells,2001,1:133-161. [3]Liang Z X,Zhao TS.NewDMFC anode structure con-sisting of platinum nanowires deposited into a Nafionmembrane[J].J Phys Chem C,2007,111:8128-8134. [4]Reddington E,Sapienza A,Gurau B,et al.Combinato-rial electrochemistry:a highly parallel,optical screen-ing method for discovery of better electrocatalysts[J].Science,1998,280:1735-1737. [5]Winter M,Brodd R J.What are batteries,fuel cells,and supercapacitors?[J].Chem Rev,2004,104:4245-4270. [6]Steele B C H,Heinzel A.Materials for fuel-cell tech-nologies[J].Nature,2001,414:345-352. [7]Bell A T.The impact of nanoscience on heterogeneouscatalysis[J].Science,2003,299:1688-1691. [8]Christensen P A,Hamnetand A,Troughton Q L.Therole of morphology in the methanol electro-oxidation re-action[J].J Electroanal Chem,1993,362:207-218. [9]B nnemann H,Wald fner N,Haubold H G.Prepara-tion and characterization of three-dimensional Pt nanop-article networks[J].Chem Mater,2002,14:1115-1120. [10]Tian N,Zhou Y,Sun S G,et al.Synthesis of tetra-hexahedral platinum nanocrystals with high-index facetsand high electro-oxidation activity[J].Science,2007,316:732-735. [11]Ahmadi T S,Wang Z L,Green T C,et al.Shape-controlled synthesis of colloidal platinum nanoparticles[J].Science,1996,272:1924-1925. [12]Tian N,Zhou Z Y,Sun S G,et al.Synthesis of tetra-hexahedral platinum nanocrystals with high-index facetsand high electro-oxidation activity[J].Science,2007,316:732-735. [13]Liang H P,Zhang H M,Hu J S,et al.Pt hollownanospheres:facile synthesis and enhanced electrocat-alysts[J].Angew Chem Int Ed.,2004,43(12):1540-1543. [14]Sun S H,Yang D,Villers D,et al.Template-and sur-factant-free room temperature synthesis of self-assem-bled 3D Pt nanoflowers from single-crystal nanowire[J].Adv Mater,2008,20;571-4. [15]Zhao Y,Fan L Z,Zhong HZ,et al.Platinum nanop-article clusters immobilized on multi-walled carbonnanotubes:electrodeposition and enhanced electrocata-lytic activity for methanol oxidation[J].Adv FunctMater,2007,17:1537. [16]Huang M H,Mao S,Feick H,et al.Room-tempera-ture ultraviolet nanowire nanolasers[J].Science,2001,292:1897-1899. [17]Feng X J,Feng L,Jin M,et al.Reversible super-hy-drophobicity to super-hydrophilicity transition of a-ligned ZnO nanorod films[J].J Am Chem Soc,2004,126:62-63.

Pt纳米花/ZnO复合阵列的制备及对甲醇氧化催化的研究

Preparation of Pt Nanoflower/ZnO Composites Arrays and Their Electrocatalysis for Methanol Oxidation

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	谭卓, 李凯旋, 毛秉伟, 颜佳伟. 电化学扫描隧道显微术：以Cu在Au(111)表面初始阶段电沉积为例[J]. 电化学（中英文）, 2023, 29(7): 2216003-.
[2]	杨家强, 金磊, 李威青, 王赵云, 杨防祖, 詹东平, 田中群. 亚硫酸盐无氰电沉积金新工艺及机制[J]. 电化学（中英文）, 2022, 28(7): 2213005-.
[3]	孙云娜, 吴永进, 谢东东, 蔡涵, 王艳, 丁桂甫. 硅通孔内铜电沉积填充机理研究进展[J]. 电化学（中英文）, 2022, 28(7): 2213001-.
[4]	黄葵, 黄容姣, 刘素琴, 何震. 电子功能外延薄膜的电沉积[J]. 电化学（中英文）, 2022, 28(7): 2213006-.
[5]	倪修任, 张雅婷, 王翀, 洪延, 陈苑明, 苏元章, 何为, 陈先明, 黄本霞, 续振林, 李毅峰, 李能彬, 杜永杰. 电沉积纳米锥镍的生长机理及其性能的研究[J]. 电化学（中英文）, 2022, 28(7): 2213008-.
[6]	魏丽君, 周紫晗, 吴蕴雯, 李明, 王溯. 芯片钴互连及其超填充电镀技术的研究进展[J]. 电化学（中英文）, 2022, 28(6): 2104431-.
[7]	缪桦, 李明瑞, 邹文中, 周国云, 王守绪, 叶晓菁, 朱凯. Sn-Ag-Cu三元合金焊料电沉积中添加剂的影响研究[J]. 电化学（中英文）, 2022, 28(6): 2104411-.
[8]	战充波, 张润佳, 付旭, 孙海静, 周欣, 王保杰, 孙杰. 氯离子对ChCl-Urea低共熔溶剂中银电沉积的电化学行为影响[J]. 电化学（中英文）, 2022, 28(5): 2111151-.
[9]	王昊, 曹晓舟, 薛向欣. 锑在氯化胆碱-乙二醇低共熔溶剂中的电沉积研究[J]. 电化学（中英文）, 2022, 28(4): 2103071-.
[10]	李江, 李作鹏, 白云峰, 罗宿星, 郭永, 鲍雅妍, 李容, 刘海燕, 冯锋. 一种基于电沉积3D花状CoS在自支撑石墨烯胶带电极上的非酶葡萄糖传感器的研究与应用[J]. 电化学（中英文）, 2022, 28(1): 2104211-.
[11]	刘双娟, 王海静, 郭靖, 王鹏程, 周昊, 孟才, 郭汉杰. 电沉积法制备石墨烯纸-金属复合材料的初步研究[J]. 电化学（中英文）, 2021, 27(4): 396-404.
[12]	Dylan Siltamaki, 陈帅, Farnood Pakravan, Jacek Lipkowski, 陈爱成. 纳米晶枝CuAu 合金催化剂对二氧化碳电催化还原性能的研究[J]. 电化学（中英文）, 2021, 27(3): 278-290.
[13]	吴丽文, 王玮, 黄逸凡. 应用镍超微电极的电化学表面增强拉曼光谱技术研究[J]. 电化学（中英文）, 2021, 27(2): 208-215.
[14]	吴丹丹, 吴旭. 钛基氧化铱电极电沉积制备技术研究进展[J]. 电化学（中英文）, 2021, 27(1): 35-44.
[15]	晋通正, 杨雨萌, 范圣慧, 卫国英, 张昭. 溶解氧及波长对光助阳极沉积CeO₂薄膜的影响[J]. 电化学（中英文）, 2020, 26(6): 868-875.