竹节状硅纳米管的制备及锂离子嵌入/脱出性能研究

电化学（中英文） ›› 2006, Vol. 12 ›› Issue (4): 363-367.

竹节状硅纳米管的制备及锂离子嵌入/脱出性能研究

刘增涛;傅焰鹏;李晨;杨勇;

固体表面物理化学国家重点实验室厦门大学化学系,固体表面物理化学国家重点实验室厦门大学化学系,固体表面物理化学国家重点实验室厦门大学化学系,固体表面物理化学国家重点实验室厦门大学化学系福建厦门361005,福建厦门361005,福建厦门361005,福建厦门361005

收稿日期:2006-11-28 修回日期:2006-11-28 出版日期:2006-11-28 发布日期:2006-11-28

Preparation and Electrochemical Property of Bam boo-shaped Silicon Nanotubes

LIU Zeng-tao,FU Yan-peng,LI Chen,YANG Yong~*

(State Key Lab for Physical Chemistry of Solid Surface & Department of Chemistry,Xiamen University,Xiamen 361005,China

Received:2006-11-28 Revised:2006-11-28 Published:2006-11-28 Online:2006-11-28

摘要/Abstract

摘要： 应用改进的化学气相沉积法,成功地合成出一种新的竹节状硅纳米管材料.微电极循环伏安测试表明:锂离子在该硅纳米材料中可能存在两种嵌入位,即实心节部嵌入位和空心管壁嵌入位.作为锂离子电池负极材料,该材料也在一定程度上抑制了一般硅材料所面临的体积效应问题.

关键词: 负极材料, 锂离子电池, 竹节状硅纳米管

Abstract: A novel 1D bamboo-shaped silicon nanotubes was synthesized by chemical vapor deposition with Au catalyst and their electrochemical properties were primarily studied.The results showed that these silicon nanotubes were amorphous with the length about tens micrometer and the diameter about one hundred nanometer.Cyclic voltammetry studies showed that Li ions could intercalate into such silicon nanotubes at two location,i.e.,from the conjoint location and the wall of the hole.Meanwhile,the bamboo-shaped structure could help release the expansion of volume,which is usually serious in the lithium batteries.

Key words: Anode material, Li-ion battery, Bamboo-shaped Si nanotubes

中图分类号:

TM912

刘增涛;傅焰鹏;李晨;杨勇;. 竹节状硅纳米管的制备及锂离子嵌入/脱出性能研究[J]. 电化学（中英文）, 2006, 12(4): 363-367.

LIU Zeng-tao,FU Yan-peng,LI Chen,YANG Yong~*. Preparation and Electrochemical Property of Bam boo-shaped Silicon Nanotubes[J]. Journal of Electrochemistry, 2006, 12(4): 363-367.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2006/V12/I4/363

参考文献

[1]M egahed S,Scrosati B.L ith ium-ion rechargeab le bat-teries[J].J.Power Sources,1994,5(1~2):79. [2]Ohzuku T,Iwakosh i Y,Sawai K.Form ation of lith ium-graph ite intercalation compounds in nonaqueous electro-lytes and the ir app lication as a negative electrode for alith ium ion(shuttlecock)cell[J].J.E lectrochem.Soc.,1993,140:2490. [3]Aurbach D,E in-E li Y,M arkovsky Y B,et al.Thestudy of electrolyte solutions based on ethylene and d i-ethyl carbonates for rechargeab le L i Batteries[J].J.E lectrochem.Soc.,1995,142(9):2882. [4]Am ezawa K,Yam amoto N,Tom iiY,et al.S ingle-elec-trode peltier heats of L i-S i alloy electrodes in L iC l-KC leutectic m elt[J].J.E lectrochem.Soc.,1998,145(6):1986. [5]Huggins,Robert A.L ith ium alloy negative electrodesform ed from convertib le oxides[J].Solid State Ion ics,1998,113~115:57. [6]L iH,Huang X,Chen L,et al.A h igh capac ity nano-S i composite anode m aterial for lith ium rechargeab lebatteries[J].E lectrochem,Solid State Lett.,1999,2(11):547. [7]L i H,Huang X,Chen L,et al.The crystal structuralevolution of nano-S i anode caused by lith ium insertionand extraction at room temperature[J].Solid State Ion-ics,2000,135(1~4):181. [8]L i C,L iu Z T,Yang Y.Controllab le synthesis andgrowth model of amorphous silicon nanotubes w ith peri-od ically dom e-shaped interiors[J].Adv.M ater.,2006,18:228. [9]L i Chen.Synthesis and characterization of one-d im en-sional sem iconductor nanom aterials[D].X iam en:X ia-m en Un iversity,2005. [10]Xu M eng-q ing(许梦清),ZUO X iao-xi(左晓希),LIW e i-shan(李伟善),et al.E lectrochem ical behaviorof carbonate solvent used in electrolytes for L i-ion bat-teries[J].Ch inese Battery Industry(in Ch inese),2005,10(5):274. [11]REN N ing(任宁),Y IN Ge-p ing(尹鸽平),ZUOPeng-jian(左朋建),et al.E lectrochem ical perform-ance of S i-Mn composites in L i-ion battery[J].Ch i-nese Journal of Inorgan ic Chem istry(in Ch inese),2005,21:1677. [12]SUN Yang-zheng,LIAO X iao-zhen,MA Z i-feng.Re-search progress in silicon based anode m aterials for L i-ion batteries[J].Battery B imonthly,2004,3:40.

[1]	范佳琪, 宋焕巧, 安佳莹, 阿依达娜·阿曼太, 陈默. 碳限域Li₃VO₄纳米材料的制备及其储锂性能[J]. 电化学（中英文）, 2023, 29(11): 211203-.
[2]	殷秀平, 赵玉峰, 张久俊. 钠离子电池硬碳基负极材料的研究进展[J]. 电化学（中英文）, 2023, 29(10): 2204301-.
[3]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[4]	陈思, 郑淞生, 郑雷铭, 张叶涵, 王兆林. 水热法制备锂电池Si@C负极材料的工艺优化研究[J]. 电化学（中英文）, 2022, 28(8): 2112221-.
[5]	王京玥, 王睿, 王诗琦, 王立帆, 詹纯. 一步固相法合成锂离子电池高镍层状正极材料[J]. 电化学（中英文）, 2022, 28(8): 2112131-.
[6]	谯渭川, 李芳儒, 肖瑾林, 屈丽娟, 赵晓, 张梦, 庞春雷, 李子坤, 任建国, 贺雪琴. 硅氧材料的膨胀性能研究和改善[J]. 电化学（中英文）, 2022, 28(5): 2108121-.
[7]	王加义, 郭胜楠, 王新, 谷林, 苏东. 锂离子电池高镍层状氧化物正极结构失效机制[J]. 电化学（中英文）, 2022, 28(2): 2108431-.
[8]	郭瑞琪, 吴锋, 王欣然, 白莹, 吴川. 多电子反应材料推动高能量密度电池发展：材料与体系创新[J]. 电化学（中英文）, 2022, 28(12): 2219011-.
[9]	朱振威, 邱景义, 王莉, 曹高萍, 何向明, 王京, 张浩. 人工智能在锂离子电池研发中的应用[J]. 电化学（中英文）, 2022, 28(12): 2219003-.
[10]	侯廷政, 陈翔, 蒋璐, 唐城. 当前和下一代锂离子电池电解液的原子尺度微观认识和研究进展[J]. 电化学（中英文）, 2022, 28(11): 2219007-.
[11]	李丹丹, 纪翔宇, 陈明, 杨燕茹, 王晓东, 冯光. 低聚离子液体的体相与界面及其电化学储能应用[J]. 电化学（中英文）, 2022, 28(11): 2219002-.
[12]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.
[13]	李姝谨, 曹志康, 王文凯, 张晓菡, 向兴德. 硫酸盐功能电解液增强水系钠离子电池NaTi₂(PO₄)₃/C负极材料电化学性能的研究[J]. 电化学（中英文）, 2021, 27(6): 605-613.
[14]	蔡雪凡, 孙升. 多孔电极电池的循环伏安法模拟[J]. 电化学（中英文）, 2021, 27(6): 646-657.
[15]	彭依, 张伟, 左防震, 吕浩莹, 洪凯骏. 二硒化钼纳米球储锂和储镁的性能和机理研究[J]. 电化学（中英文）, 2021, 27(4): 456-464.