氧化铁镍电极上析氧反应的电化学研究(英文)

电化学（中英文） ›› 2006, Vol. 12 ›› Issue (2): 154-158.

氧化铁镍电极上析氧反应的电化学研究(英文)

黄金昭;徐征;李海玲;亢国虎;王文静;

北京交通大学发光与光信息技术教育部重点实验室,北京交通大学发光与光信息技术教育部重点实验室,北京市太阳能研究所,北京市太阳能研究所,北京市太阳能研究所北京100044,北京100044,北京100083,北京100083,北京100083

收稿日期:2006-05-28 修回日期:2006-05-28 出版日期:2006-05-28 发布日期:2006-05-28

Electrochemical Studies of Iron-doped Nickel Oxide Electrode for Oxygen Evolution Reaction

HUANG Jin-zhao1,XUZheng*1,LI Hai-ling2,KANG Guo-hu2,WANG Wen-jing2

(1.Key Laboratory ofLuminescence and Optical Information,Ministry ofEducation,Institute ofoptoelectronic technology,Beijing jiaotong university,Beijing100044,China,2.Beijing solar energy research institute,Beijing100083,China

Received:2006-05-28 Revised:2006-05-28 Published:2006-05-28 Online:2006-05-28

摘要/Abstract

摘要： 应用射频反应磁控溅射法制备阳极催化氧化铁镍薄膜,由循环伏安、线性扫描伏安、极化曲线和电化学交流阻抗谱等研究发生在该电极上的氧化反应.结果表明,作为活化中心的铁能使过电势降低,并且随着溅射过程氧流量的增加催化性能增强,铁的掺入使得速率限定步骤由OH-的释放变为氧原子的结合.与镍相比,氧化铁镍是更理想的催化阳极材料,当电流密度为50 mA/cm2时,其氧的过电势比镍的下降了500 mV.

关键词: 氧化铁镍, 电催化

Abstract: In this paper,the iron-doped nickel oxide thin film as anode catalyst was prepared by RF reactivesputtering method.The oxygen evolution reaction(OER) on the iron-doped nickel oxide was investigated withcyclic voltammetry,liner sweep voltammetry,polarization curves and electrochemical impedance spectroscopy.Results showthat the iron acts as active site in the film which makes the overpotential lower,and changes therate-limiting from primary discharge of OH-ions to the recombination of oxygen atom.With the increasing of ox-ygen content in flu ratio during sputtering,the electrocatalytic activities of the film increase.Iron-doped nickeloxide thin film is promising material as OER electrocatalyst for hydrogen production than the nickel electrode.The oxygen overpotential on the film was over 500 mV lower than the overpotential with nickel at50mA/cm2.

Key words: Iron-doped nickel oxide, Electrocatalytic

中图分类号:

O646.54

黄金昭;徐征;李海玲;亢国虎;王文静;. 氧化铁镍电极上析氧反应的电化学研究(英文)[J]. 电化学（中英文）, 2006, 12(2): 154-158.

HUANG Jin-zhao1,XUZheng*1,LI Hai-ling2,KANG Guo-hu2,WANG Wen-jing2. Electrochemical Studies of Iron-doped Nickel Oxide Electrode for Oxygen Evolution Reaction[J]. Journal of Electrochemistry, 2006, 12(2): 154-158.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2006/V12/I2/154

参考文献

[1]Barreto L,Makihira A,Riahi K.The hydrogen econo-my in the 21stcentury:a sustainable development scena-rioc[J].Int.J.Hydrogen Energy,2003,28:267. [2]Midilli A,Dincer I,Rosen M A.On hydrogen and hy-drogen energy strategies II:future projections affectingglobal stability and unrest[J].Renew.Sust.EnergyRev.,2005,9:273. [3]Massimo S,Mickele C,Sara M.Design and analysis ofstand-alone hydrogen energy systems with different re-newable sources[J].Int.J.Hydrogen Energy,2004,29:1571. [4]Tsuneo H.Research and development of internationalclean energy network using hydrogen energy(WE-NET)[J].Int.J.Hydrogen Energy,2002,27:115. [5]Seth D.Hydrogen futures:toward a sustainable energysystem[J].Int.J.Hydrogen Energy,2002,27:235. [6]Bak T,Nowotny J,Rekas M,et al.Photo-electrochem-ical hydrogen generation from water using solar energy[J].Int.J.Hydrogen Energy,2002,27:991. [7]Trasatti S.Electrocatalysis in the anodic evolution of ox-ygen and chlorine[J].Electrochimica Acta,1983,29:1503. [8]Suredini HB,Cerne J L,Crnkovic F C,et al.Recentdevelopments in electrode materials for water electrolysis[J].Int.J.Hydrogen Energy,2000,25:415. [9]Tiwari S K,Chartier P,Singh R N.Preparation of per-ovskite-type oxides of cobalt by the malic acid aidedprocess and their electrocatalytic surface properties inrelation to oxygen evolution[J].J.Electrochem.Soc.,1995,142:148. [10]Kibria M F,Mridha M SH.Electrochemical studies ofthe nickel electrode for the oxygen evolution reaction[J].Int.J.Hydrogen Energy,1996,21:179. [11]Choquette Y,Brossard L,Lasia A,et al.Investigationof hydrogen evolution on raney-nickel composite-coatedelectrodes[J].Electrochimica Acta.,1990,35:1251. [12]Choquette Y,Menard H,Brossard L,Electrocatalyticperformance of composite-coated electrodes for alkalinewater electrolysis[J].Int.J.Hydrogen Energy,1990,15:21. [13]Kamnev AA,Ezhov B B.Electron spectroscopy of solu-ble anodic oxidation products of iron in alkaline solu-tions[J].Soviet Electrochemistry,1989,24:1027. [14]Corrigan D.The catalysis of the oxygen evolution reac-tion by iron impurities in thin film nickel oxide elec-trodes[J].J.Electrochem.Soc.,1987,134(2):377.

[1]	高梦婷, 卫莹, 霍雪萌, 朱文洁, 刘箐箐, 强晋源, 刘婉婉, 王颖, 李旭, 黄剑锋, 冯永强. 氮掺杂碳纳米管上钴和钌位点之间的电子通信促进碱性析氢反应[J]. 电化学（中英文）, 2024, 30(9): 2403081-.
[2]	王昱喆, 蒋卓良, 温波, 黄耀辉, 李福军. 锂氧电池中钌基电催化剂的研究进展[J]. 电化学（中英文）, 2024, 30(8): 2314004-.
[3]	韦聚才, 易娟, 吴旭. 电化学法深度处理电厂脱硫废水[J]. 电化学（中英文）, 2024, 30(4): 2205041-.
[4]	万紫轩, Aidar Kuchkaev, Dmitry Yakhvarov, 康雄武. 单分散Cu-TCPP/Cu₂O杂化微球:一种具有优异电还原CO₂产C₂性能的级联电催化剂[J]. 电化学（中英文）, 2024, 30(1): 2303271-.
[5]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[6]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[7]	冯辛, 刘博文, 郭可鑫, 范林丰, 王根香, 次素琴, 温珍海. 基于阳极甘油氧化电催化的碱/酸混合电解制氢研究[J]. 电化学（中英文）, 2023, 29(2): 2215005-.
[8]	孟庆成, 金林薄, 马梦泽, 高学庆, 陈爱兵, 周道金, 孙晓明. 层状金属氢氧化物中铁位点辅助分散铂纳米颗粒用于高效甲醇氧化[J]. 电化学（中英文）, 2023, 29(2): 2215007-.
[9]	韦宗楠, 曹敏纳, 曹荣. 瓜环基金属纳米催化剂的电化学研究进展[J]. 电化学（中英文）, 2023, 29(1): 2215008-.
[10]	郭鸿波, 王亚妮, 郭凯, 雷海涛, 梁作中, 张学鹏, 曹睿. 吸电子和亲水性Co-卟啉促进电催化氧还原反应的研究[J]. 电化学（中英文）, 2022, 28(9): 2214002-.
[11]	梁宵, 张可新, 沈雨澄, 孙轲, 石磊, 陈辉, 郑克岩, 邹晓新. 钙钛矿型水氧化电催化剂[J]. 电化学（中英文）, 2022, 28(9): 2214004-.
[12]	周澳, 郭伟健, 王月青, 张进涛. 焦耳热快速合成双功能电催化剂用于高效水分解[J]. 电化学（中英文）, 2022, 28(9): 2214007-.
[13]	王英超, 马自在, 吴一凡, 王孝广. GCP载钯颗粒复合材料的制备及其电化学合成氨性能研究[J]. 电化学（中英文）, 2022, 28(5): 2104091-.
[14]	张天恩, 颜雅妮, 张俊明, 瞿希铭, 黎燕荣, 姜艳霞. 调控Pt₃Zn合金化程度改善酸性氧还原活性与稳定性[J]. 电化学（中英文）, 2022, 28(4): 2106091-.
[15]	Jafar Hussain Shah, 谢起贤, 匡智崇, 格日乐, 周雯慧, 刘朵绒, Alexandre I. Rykov, 李旭宁, 罗景山, 王军虎. 原位⁵⁷Fe穆斯堡尔光谱技术及其在Ni-Fe基析氧反应电催化剂中的应用[J]. 电化学（中英文）, 2022, 28(3): 2108541-.