壳聚糖单体溶胶凝胶煅烧合成LiFePO4/C正极

doi:10.61558/2993-074X.2112

电化学（中英文） ›› 2013, Vol. 19 ›› Issue (2): 189-192. doi: 10.61558/2993-074X.2112

壳聚糖单体溶胶凝胶煅烧合成LiFePO₄/C正极

徐嘉¹，王艳艳¹，王蕊²，王博¹，潘越¹，曹殿学¹，王贵领^1*

1. 哈尔滨工程大学材料科学与化学工程学院，黑龙江哈尔滨 150001；2. 哈药集团三精制药有限公司，黑龙江哈尔滨，150069

收稿日期:2012-01-05 修回日期:2012-02-11 出版日期:2013-04-28 发布日期:2012-02-21
通讯作者: 王贵领 E-mail:wangguiling@hrbeu.edu.cn
基金资助:
国家自然科学基金项目（No. 20973048）资助

Synthesis of LiFePO₄/C Cathode by Sol-gel and Calcining Method with Chitosan Monomer

XU Jia¹, WANG Yan-Yan¹, WANG Rui², WANG Bo¹, PAN Yue¹, CAO Dian-Xue¹, WANG Gui-Ling^1*

1. College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China; 2. Harbin Pharm. Group Sanjing Pharmaceutical Shareholding Co., Ltd, Harbin 150069, China

Received:2012-01-05 Revised:2012-02-11 Published:2013-04-28 Online:2012-02-21
Contact: WANG Gui-Ling E-mail:wangguiling@hrbeu.edu.cn

摘要/Abstract

摘要： 本文以壳聚糖单体为碳源兼凝胶剂，利用溶胶-凝胶煅烧合成了锂离子电池LiFePO₄/C正极材料，使用XRD和SEM对合成的材料进行表征. 用恒电流充放电测试了LiFePO₄/C电极的电化学性能，当壳聚糖单体与LiFePO4摩尔比为1:1.2时，600 ^oC煅烧的LiFePO4/C电极性能最佳，其粒径分布均匀（200 ～ 400 nm），该电极0.2C倍率放电比容量为155 mAh.g^-1，30周期循环放电比容量仍保持152 mAh.g^-1，库仑效率为97.9 %.

关键词: 壳聚糖, 磷酸亚铁锂, 溶胶-凝胶法, 锂离子电池

Abstract: The LiFePO₄/C cathode materials for Li-ion battery were synthesized by sol-gel and calcining method using chitosan monomer as a carbon source and a gelating agent. The structures and morphologies were characterized by X-ray diffraction spectroscopy (XRD) and scanning electron microscopy (SEM). The electrochemical performance was investigated by the galvanostatic charge–discharge test. When the molar ratios between chitosan monomer and LiFePO₄were 1:1.2, the LiFePO₄/C cathode calcined at 600 ^oC showed the best performance. The particle sizes ranged 200 ～ 400 nm. The initial discharge capacity of 155 mAh.g-¹ was achieved at room temperature with discharge rate of 0.2C, while the capacity of 152 mAh.g^-1 could be maintained after 30 charge-discharge cycles. The coulombic efficiency was 97.9%.

Key words: chitosan, LiFePO4/C, sol-gel method, Li-ion battery

中图分类号:

O611.4

徐嘉, 王艳艳, 王蕊, 王博, 潘越, 曹殿学, 王贵领. 壳聚糖单体溶胶凝胶煅烧合成LiFePO₄/C正极[J]. 电化学（中英文）, 2013, 19(2): 189-192.

XU Jia, WANG Yan-Yan, WANG Rui, WANG Bo, PAN Yue, CAO Dian-Xue, WANG Gui-Ling. Synthesis of LiFePO₄/C Cathode by Sol-gel and Calcining Method with Chitosan Monomer[J]. Journal of Electrochemistry, 2013, 19(2): 189-192.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2112

https://electrochem.xmu.edu.cn/CN/Y2013/V19/I2/189

参考文献

[1] Sabina B, Libero D, Marina M. MW-assisted synthesis of LiFePO4 for high power applications[J]. Journal of Power Sources, 2008, 180(2): 875-879.
[2] Li J(李军), Lai G T(赖桂棠), Huang H M(黄慧民), et al. Preparation and properties of high capacity LiFePO4[J]. Journal of Electrochemistry(电化学), 2007, 13(4): 403-406.
[3] Fisher C A J, Islam M S. Surface structures and crystal morphologies of LiFePO4: Relevance to electrochemical behaviour[J]. Journal of Materials Chemistry, 2008, 18: 1209-1215.
[4] Park O K, Cho Y, Lee S, et al. Who will drive electric vehicles, olivine or spinel?[J]. Energy & Environmental Science, 2011, 4(5): 1621-1633.
[5] Daiwon C, Prashant N K. Surfactant based sol-gel approach to nanostructured LiFePO4 for high rate Li-ion batteries[J]. Journal of Power Sources, 2007, 163(2): 1064-1069.
[6] Kobayashi G, Nishimura S I, Park M S, et al. Isolation of solid solution phases in size-controlled LixFePO4 at room temperature[J]. Advanced Functional Materials, 2009, 19(3): 395-403.
[7] Keisuk S, Kaoru D, Kiyoshi K. Formation of impurities on phospho-olivine LiFePO4 during hydrothermal synthesis[J]. Journal of power Sources, 2008, 146(1/2): 555-558.
[8] Prosini P P , Lisi M , Zane D, et al. Determination of the chemical diffusion coefficient of lithium in LiFePO4[J]. Solid State Ionics, 2002, 148(1/2):45-51.
[9] Bai Y(白莹), Yang J M(杨觉明), Qing C B(卿春波), et al. Electrochemical performances of C-coating and co-doping LiFePO4[J]. Journal of Electrochemistry(电化学), 2011, 17(3): 334-338.
[10] Li T(李婷), Qian J F(钱江峰), Cao Y L(曹余良), et al. Electrochemical performance of Li1-xMxFePO4 cathode materials synthesized by polymer pyrolysis route[J]. Journal of Electrochemistry(电化学), 2007, 13(2): 136-139.
[11] Zou H L(邹红丽), Zhang G H(张光辉), Shen P K(沈培康). Hydrothermal reduction synthesis of LiFePO4 and its electrochemical performance[J]. Journal of Electrochemistry(电化学), 2010, 16(4): 416-419.
[12] Zhu C, Yu Y, Gu L, et al. Electrospinning of highly electroactive carbon-coated single- crystalline LiFePO4 nanowires[J]. Angewandte Chemie International Edition, 2011, 50(28): 6278-6282
[13] Yu L H(余丽红), Cao Y L(曹余良), Zhang X F(张晓飞), et al. Structure and electrochemical characteristics of LiFePO4 prepared by the polyacrylates pyrolysis reduction method for Li-ion batteries[J]. Journal of Electrochemistry(电化学), 2006, 12(4): 442-444.
[14] Wang L, Liang G C, Ou X Q, et al. Effect of synthesis temperature on the properties of LiFePO4/C composites prepared by carbothermal reduction[J]. Journal of Power Sources, 2009, 189(1): 423-428.
[15] Peng Y Y(彭友谊), Zhang H Y(张海燕), He C H(贺春华), et al. A study on the LiFePO4/ MWCNTs cathode materials for Li-ion batteries[J]. Journal of Electrochemistry(电化学), 2009, 15(3): 331-335.
[16] Lepage D, Michot C, Liang G, et al. A soft chemistry approach to coating of LiFePO4 with a conducting polymer[J]. Angewandte Chemie International Edition. 2011, 50(30): 6884-6887.
[17] Suh J, Matthew H. Application of chitosan-based polysaccharide biomaterials in cartilage tissue engineering: A review[J]. Biomaterials, 2000, 21(24):2589-2598.
[18] Kumar M. A review of chitin and chitosan applications[J]. Reactive and functional polymers, 2000, 46(1): 1-27.
[19] 王贵领，曹殿学，王博. 壳聚糖改性锂离子电池LiFePO4正极材料[P]. CN200910071245.2.

壳聚糖单体溶胶凝胶煅烧合成LiFePO₄/C正极

Synthesis of LiFePO₄/C Cathode by Sol-gel and Calcining Method with Chitosan Monomer

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[2]	陈思, 郑淞生, 郑雷铭, 张叶涵, 王兆林. 水热法制备锂电池Si@C负极材料的工艺优化研究[J]. 电化学（中英文）, 2022, 28(8): 2112221-.
[3]	王京玥, 王睿, 王诗琦, 王立帆, 詹纯. 一步固相法合成锂离子电池高镍层状正极材料[J]. 电化学（中英文）, 2022, 28(8): 2112131-.
[4]	谯渭川, 李芳儒, 肖瑾林, 屈丽娟, 赵晓, 张梦, 庞春雷, 李子坤, 任建国, 贺雪琴. 硅氧材料的膨胀性能研究和改善[J]. 电化学（中英文）, 2022, 28(5): 2108121-.
[5]	王加义, 郭胜楠, 王新, 谷林, 苏东. 锂离子电池高镍层状氧化物正极结构失效机制[J]. 电化学（中英文）, 2022, 28(2): 2108431-.
[6]	郭瑞琪, 吴锋, 王欣然, 白莹, 吴川. 多电子反应材料推动高能量密度电池发展：材料与体系创新[J]. 电化学（中英文）, 2022, 28(12): 2219011-.
[7]	朱振威, 邱景义, 王莉, 曹高萍, 何向明, 王京, 张浩. 人工智能在锂离子电池研发中的应用[J]. 电化学（中英文）, 2022, 28(12): 2219003-.
[8]	侯廷政, 陈翔, 蒋璐, 唐城. 当前和下一代锂离子电池电解液的原子尺度微观认识和研究进展[J]. 电化学（中英文）, 2022, 28(11): 2219007-.
[9]	李丹丹, 纪翔宇, 陈明, 杨燕茹, 王晓东, 冯光. 低聚离子液体的体相与界面及其电化学储能应用[J]. 电化学（中英文）, 2022, 28(11): 2219002-.
[10]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.
[11]	袁会芳, 张越, 翟兴吾, 胡立兵, 葛桂贤, 王刚, 于锋, 代斌. 氮掺杂碳原位锚定铜纳米颗粒用于高效氧还原反应催化剂[J]. 电化学（中英文）, 2021, 27(6): 671-680.
[12]	蔡雪凡, 孙升. 多孔电极电池的循环伏安法模拟[J]. 电化学（中英文）, 2021, 27(6): 646-657.
[13]	彭依, 张伟, 左防震, 吕浩莹, 洪凯骏. 二硒化钼纳米球储锂和储镁的性能和机理研究[J]. 电化学（中英文）, 2021, 27(4): 456-464.
[14]	周莉, 吴勰, 薛照明. 热塑性聚氨酯基聚合物电解质的制备与表征[J]. 电化学（中英文）, 2021, 27(4): 439-448.
[15]	李丽娟, 朱振东, 代娟, 王蓉蓉, 彭文. 锂离子电池正极材料Li[Ni_xCo_yMn_z]O₂ (x = 0.6, 0.85)相变对比[J]. 电化学（中英文）, 2021, 27(4): 405-412.