Pt-Cu合金纳米枝晶的合成及其氧还原催化性能

罗柳轩¹，魏光华²，沈水云¹，朱凤鹃¹，柯长春¹，闫晓晖¹，章俊良^1*

1. 上海交通大学动力与机械工程学院燃料电池研究所，动力机械与工程教育部重点实验室，上海 200240; 2. 上海交通大学巴黎高科卓越工程师学院，上海 200240

收稿日期:2018-09-28 修回日期:2018-10-15 出版日期:2018-12-28 发布日期:2018-10-29
通讯作者: 章俊良 E-mail:junliang.zhang@sjtu.edu.cn
基金资助:
获国家重点研发项目（No. 2016YFB0101201）和国家自然科学基金项目（No. 21533005, No. 21503134）资助

Facile Synthesis of Pt-Cu Alloy Nanodendrites as High-Performance Electrocatalysts for Oxygen Reduction Reaction

LUO Liu-xuan¹, WEI Guang-hua², SHEN Shui-yun¹, ZHU Feng-juan¹, KE Chang-chun¹, YAN Xiao-hui¹, ZHANG Jun-liang^1*

1. Institute of Fuel Cells, School of Mechanical Engineering, MOE Key Laboratory of Power & Machinery Engineering; 2. SJTU-Paris Tech Elite Institute of Technology, Shanghai Jiao Tong University, Shanghai 200240, China)

Received:2018-09-28 Revised:2018-10-15 Published:2018-12-28 Online:2018-10-29
Contact: ZHANG Jun-liang E-mail:junliang.zhang@sjtu.edu.cn
Supported by:
This work was funded by the National Key Research and Development Program of China (No. 2016YFB0101201) and the National Natural Science Foundation of China (No.21533005 and No. 21503134)

摘要/Abstract

摘要： 纳米材料的结构和化学成分对其催化性能的显著影响已经得到验证. 因此，本文通过一种简易的蚀刻方法，合成出具有均匀合金结构且尺寸和形貌均一的Pt-Cu纳米枝晶（NDs）作为高效氧还原（ORR）催化剂. 其树枝状形貌的形成得益于由Br^-/O₂氧化蚀刻剂引起的蚀刻效应. 通过改变Pt/Cu前驱体的比例可以容易地调节Pt-Cu NDs的Pt/Cu原子比，而不会使其树枝状形貌发生改变. 活性最高的碳载Pt₁Cu₁ NDs（Pt₁Cu₁ NDs/C）的面积比活性为1.17 mA·cm^-2@0.9V（vs. RHE），约为商业Pt/C的5.32倍. 此外，Pt₁Cu₁ NDs/C还具有卓越的电化学耐久性，即使在经过加速衰减实验的12000个电势循环后仍保持其优异的ORR催化活性. Pt₁Cu₁ NDs/C优异的ORR催化活性和电化学耐久性得益于由其合金结构和枝晶形貌产生的电子效应和结构效应.

关键词: 铂, 合金, 电催化剂, 纳米枝晶, 氧还原

Abstract: Structures and compositions have significant effects on the catalytic properties of nanomaterials. Herein, a facile etching-based method was employed to synthesize Pt-Cu nanodendrites (NDs) with uniform and homogeneous alloy structures for enhancing oxygen reduction reaction (ORR). The formation of dendritic morphology was ascribed to the etching effect caused by the oxidative etchants of the Br^-/O₂ pair. The atomic ratio of Pt/Cu in Pt-Cu NDs could be easily tuned by altering the ratio of the Pt/Cu precursors, without deteriorating the dendritic morphology. The most active carbon-supported Pt₁Cu₁ NDs (Pt₁Cu₁ NDs/C) exhibited the area-specific activity of 1.17 mA·cm^-2@0.9 V (vs. RHE), which is ~5.32 times relative to that of commercial Pt/C. Moreover, Pt₁Cu₁ NDs/C also possessed a remarkable electrochemical durability, preserving its superior ORR catalytic activity even after 12000 potential cycles during the accelerated degradation test. Such excellent catalytic activity and electrochemical durability of Pt₁Cu₁ NDs/C toward ORR were resulted from the combined electronic and structural effects, which are imparted by the Pt-Cu alloy structure and the dendritic morphology.

Key words: Pt, alloy, electrocatalysts, nanodendrites, oxygen reduction reaction

中图分类号:

O646

罗柳轩，魏光华，沈水云，朱凤鹃，柯长春，闫晓晖，章俊良. Pt-Cu合金纳米枝晶的合成及其氧还原催化性能[J]. 电化学（中英文）, 2018, 24(6): 733-739.

LUO Liu-xuan, WEI Guang-hua, SHEN Shui-yun, ZHU Feng-juan, KE Chang-chun, YAN Xiao-hui, ZHANG Jun-liang. Facile Synthesis of Pt-Cu Alloy Nanodendrites as High-Performance Electrocatalysts for Oxygen Reduction Reaction[J]. Journal of Electrochemistry, 2018, 24(6): 733-739.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.180856

https://electrochem.xmu.edu.cn/CN/Y2018/V24/I6/733

参考文献

[1] Luo L X, Zhu F J, Tian R X, et al. Composition-graded Pd_xNi_1-x nanospheres with Pt monolayer shells as high-performance electrocatalysts for oxygen reduction reaction[J]. ACS Catalysis, 2017, 7(8): 5420-5430.
[2] Chen A C, Holt-Hindle P. Platinum-based nanostructured materials: synthesis, properties, and applications[J]. Chemical Reviews, 2010, 110(6): 3767-3804.
[3] Debe M K. Electrocatalyst approaches and challenges for automotive fuel cells[J]. Nature, 2012, 486(7401): 43-51.
[4] Wang Y J, Zhao N N, Fang B Z, et al. Carbon-supported Pt-based alloy electrocatalysts for the oxygen reduction reaction in polymer electrolyte membrane fuel cells: particle size, shape, and composition manipulation and their impact to activity[J]. Chemical Reviews, 2015, 115(9): 3433-3467.
[5] Cheng N C, Banis M N, Liu J, et al. Extremely stable platinum nanoparticles encapsulated in a zirconia nanocage by area-selective atomic layer deposition for the oxygen reduction reaction[J]. Advanced Materials, 2015, 27(2): 277-281.
[6] Wu J B, Gross A, Yang H, et al. Shape and composition-controlled platinum alloy nanocrystals using carbon monoxide as reducing agent[J]. Nano Letters, 2011, 11(2): 798-802.
[7] Zhang J L, Vukmirovic M B, Xu Y, et al. Controlling the catalytic activity of platinum-monolayer electrocatalysts for oxygen reduction with different substrates[J]. Angewandte Chemie International Edition, 2005, 44(14): 2132-2135.
[8] Tian R X, Shen S Y, Zhu F J, et al. Icosahedral Pt-Ni nanocrystalline electrocatalyst: growth mechanism and oxygen reduction activity[J]. ChemSusChem, 2018, 11(6): 1015-1019.
[9] Stamenkovic V, Markovic N M, Ross P N. Structure-relationships in electrocatalysis: oxygen reduction and hydrogen oxidation reactions on Pt(111) and Pt(100) in solutions containing chloride ions[J]. Journal of Electroanalytical Chemistry, 2001, 500(1/2): 44-51.
[10] Koenigsmann C, Santulli A C, Gong K P, et al. Enhanced electrocatalytic performance of processed, ultrathin, supported Pd-Pt core-shell nanowire catalysts for the oxygen reduction reaction[J]. Journal of the American Chemical Society, 2011, 133(25): 9783-9795.
[11] Lim B K, Jiang M J, Camargo P H C, et al. Pd-Pt bimetallic nanodendrites with high activity for oxygen reduction[J]. Science, 2009, 324(5932): 1302-1305.
[12] Lim B K, Jiang M J, Yu T K, et al. Nucleation and growth mechanisms for Pd-Pt bimetallic nanodendrites and their electrocatalytic properties[J]. Nano Research, 2010, 3(2): 69-80.
[13] Si W F, Li J, Li H Q, et al. Light-controlled synthesis of uniform platinum nanodendrites with markedly enhanced electrocatalytic activity[J]. Nano Research, 2013, 6(10): 720-725.
[14] Zhang G, Shao Z G, Lu W T, et al. One-pot synthesis of Ir@Pt nanodendrites as highly active bifunctional electrocatalysts for oxygen reduction and oxygen evolution in acidic medium[J]. Electrochemistry Communications, 2012, 22: 145-148.
[15] Wang L, Yamauchi Y. Autoprogrammed synthesis of triple-layered Au@Pd@Pt core-shell nanoparticles consisting of a Au@Pd bimetallic core and nanoporous Pt shell[J]. Journal of the American Chemical Society, 2010, 132(39): 13636-13638.
[16] Luo S P, Shen P K. Concave platinum-copper octopod nanoframes bounded with multiple high-index facets for efficient electrooxidation catalysis[J]. ACS Nano, 2016, 11(12): 11946-11953.
[17] Cordero B, Gomez V, Platero-Prats A E, et al. Covalent radii revisited[J]. Dalton Transactions, 2008, 21: 2832-2838.
[18] Gan L, Heggen M, Rudi S, et al. Core-shell compositional fine structures of dealloyed Pt_xNi_1-x nanoparticles and their impact on oxygen reduction catalysis[J]. Nano Letters, 2012, 12(10): 5423-5430.
[19] Adzic R R, Zhang J L, Sasaki K, et al. Platinum monolayer fuel cell electrocatalysts[J]. Topics in Catalysis, 2007, 46(3/4): 249-262.
[20] Wakisaka M, Mitsui S, Hirose Y, et al. Electronic structures of Pt-Co and Pt-Ru alloys for CO-tolerant anode catalysts in polymer electrolyte fuel cells studied by EC-XPS[J]. The Journal of Physical Chemistry B, 2006, 110(46): 23489-23496.

Pt-Cu合金纳米枝晶的合成及其氧还原催化性能

Facile Synthesis of Pt-Cu Alloy Nanodendrites as High-Performance Electrocatalysts for Oxygen Reduction Reaction

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	高梦婷, 卫莹, 霍雪萌, 朱文洁, 刘箐箐, 强晋源, 刘婉婉, 王颖, 李旭, 黄剑锋, 冯永强. 氮掺杂碳纳米管上钴和钌位点之间的电子通信促进碱性析氢反应[J]. 电化学（中英文）, 2024, 30(9): 2403081-.
[2]	王昱喆, 蒋卓良, 温波, 黄耀辉, 李福军. 锂氧电池中钌基电催化剂的研究进展[J]. 电化学（中英文）, 2024, 30(8): 2314004-.
[3]	陈发东, 谢卓洋, 李孟婷, 陈四国, 丁炜, 李莉, 李静, 魏子栋. 系列综述（1/4）:重庆大学魏子栋教授课题组在电化学能源转换方面的研究进展：燃料电池高性能氧还原催化剂[J]. 电化学（中英文）, 2024, 30(7): 2314007-.
[4]	万紫轩, Aidar Kuchkaev, Dmitry Yakhvarov, 康雄武. 单分散Cu-TCPP/Cu₂O杂化微球:一种具有优异电还原CO₂产C₂性能的级联电催化剂[J]. 电化学（中英文）, 2024, 30(1): 2303271-.
[5]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[6]	黄荣钦, 廖卫平, 晏梦璇, 刘石, 李远明, 康雄武. 磷掺杂的Ru-Pt合金催化剂及其电催化碱性析氢性能[J]. 电化学（中英文）, 2023, 29(5): 2203081-.
[7]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[8]	王振宇, 高学平. 金属和合金作为锂-硫电池硫正极催化载体[J]. 电化学（中英文）, 2023, 29(4): 2217001-.
[9]	孟庆成, 金林薄, 马梦泽, 高学庆, 陈爱兵, 周道金, 孙晓明. 层状金属氢氧化物中铁位点辅助分散铂纳米颗粒用于高效甲醇氧化[J]. 电化学（中英文）, 2023, 29(2): 2215007-.
[10]	刘思淼, 周景娇, 季世军, 文钟晟. FeNi-CoP/NC双功能催化剂的制备及电催化性能研究[J]. 电化学（中英文）, 2023, 29(10): 211118-.
[11]	王健, 轩文辉, 何倩, 蒋金霞, 周圆圆, 聂瑶, 廖强, 邵敏华, 丁炜, 魏子栋. 类超晶格结构：有序性传质赋予燃料电池高品质输出性能[J]. 电化学（中英文）, 2023, 29(1): 2215003-.
[12]	郭鸿波, 王亚妮, 郭凯, 雷海涛, 梁作中, 张学鹏, 曹睿. 吸电子和亲水性Co-卟啉促进电催化氧还原反应的研究[J]. 电化学（中英文）, 2022, 28(9): 2214002-.
[13]	周澳, 郭伟健, 王月青, 张进涛. 焦耳热快速合成双功能电催化剂用于高效水分解[J]. 电化学（中英文）, 2022, 28(9): 2214007-.
[14]	甘团杰, 武建平, 刘石, 区文俊, 凌彬, 康雄武. 低结晶度AuPt-Ru/CNTs合金异质结作为高效多功能电催化剂[J]. 电化学（中英文）, 2022, 28(8): 2201241-.
[15]	缪桦, 李明瑞, 邹文中, 周国云, 王守绪, 叶晓菁, 朱凯. Sn-Ag-Cu三元合金焊料电沉积中添加剂的影响研究[J]. 电化学（中英文）, 2022, 28(6): 2104411-.