Pd/Fe3O4-C催化剂对甲醇、乙醇和丙醇氧化的电催化活性

doi:10.13208/j.electrochem.161104

电化学（中英文） ›› 2017, Vol. 23 ›› Issue (6): 708-717. doi: 10.13208/j.electrochem.161104

Pd/Fe₃O₄-C催化剂对甲醇、乙醇和丙醇氧化的电催化活性

邹涛¹,易清风^1,2*,张媛媛¹,刘小平¹,徐国荣¹,聂会东¹,周秀林¹

1.湖南科技大学，化学化工学院，中国,湘潭，411201；2.理论有机化学与功能分子教育部重点实验室，中国湖南，湘潭，411201

收稿日期:2016-11-04 修回日期:2017-03-15 出版日期:2017-12-28 发布日期:2017-03-16
通讯作者: 易清风 E-mail:yqfyy2001@hnust.edu.cn
基金资助:
国家自然科学基金项目(21376070)，湖南省研究生科研创新项目(CX2016B567)资助

Electroactivities of Pd/Fe₃O₄-C catalysts for electro-oxidation of methanol, ethanol and propanol

ZOU Tao ¹, YI Qing-feng ^1,2 *, ZHANG Yuan-yuan¹, LIU Xiao-ping¹, XU Guo-rong ¹, NIE Hui-dong ¹and ZHOU Xiu-lin ¹

1.School of Chemistry and Chemical Engineering, Hunan University of Science and Technology, Xiangtan 411201, China; 2.Key Laboratory of Theoretical Organic Chemistry and Functional Molecule, Ministry of Education, Xiangtan 411201, Hunan, China

Received:2016-11-04 Revised:2017-03-15 Published:2017-12-28 Online:2017-03-16
Contact: YI Qing-feng E-mail:yqfyy2001@hnust.edu.cn

摘要/Abstract

摘要：

制备对醇氧化反应具有优异电活性的钯催化剂是醇燃料电池研究的重要内容。本文用硼氢化钠还原法制备了钯纳米颗粒, 然后沉积在Fe3O4/C复合物表面, 得到了不同Fe₃O₄负载量的Pd/Fe₃O₄-C催化剂. 透射电镜（TEM）图显示钯纳米颗粒均匀地分散在Fe₃O₄/C表面. 对制备好的Pd/Fe₃O₄-C催化剂进行了循环伏安法（CV）、计时电流（CA）和电化学阻抗谱（EIS）的测试, 研究了其在碱性介质中对C1-C3醇类（甲醇、乙醇和丙醇）氧化的电催化活性. 结果表明, 所制备的不同Fe₃O₄负载量的Pd/Fe₃O₄(2%)-C,Pd/Fe₃O₄(5%)-C, Pd/Fe₃O₄(10%)-C和Pd/C催化剂中, Pd/Fe₃O₄(5%)-C催化剂表现出最高的醇氧化电流密度. 依据循环伏安（CV）数据，Pd/Fe₃O₄(5%)-C催化剂对甲醇、乙醇、正丙醇和异丙醇氧化的阳极峰电流密度分别是Pd/C催化剂的1.7、1.4、1.7和1.3倍. Pd/Fe₃O₄(5%)-C催化剂对乙醇氧化的电荷传递电阻也远低于Pd/C催化剂. 制备的所有催化剂对C1-C3醇类电氧化的电流密度大小排序如下: 正丙醇﹥乙醇﹥甲醇﹥异丙醇. 此外, 碳粉中Fe₃O₄纳米颗粒的存在提高了钯纳米颗粒的电化学稳定性.

关键词: 钯催化剂; Fe₃O₄, 醇氧化, 电催化

Abstract: Development of palladium (Pd) catalysts with high electroactivity for alcohol oxidation is significant for alcohol fuel cells. In this work, Pd nanoparticles were formed by sodium borohydride (NaBH₄) reduction method and subsequently deposited on the surface of carbon supported ferriferrous oxide (Fe₃O₄/C) composites to obtain the Pd/Fe₃O₄-C catalysts with different Fe₃O₄loadings. Their transmission electron microscopic (TEM) images show that the Pd nanoparticles were uniformly dispersed on the Fe₃O₄/C. Electroactivities of the prepared Pd/Fe₃O₄-C catalysts toward oxidations of C1-C3 alcohols (methanol, ethanol, n-propanol and iso-propanol) in alkaline media were investigated by cyclic voltammetry (CV), chronoamperometry and electrochemical impedance spectroscopy. Among the prepared catalysts (Pd/Fe₃O₄(2%)-C, Pd/Fe₃O₄(5%)-C, Pd/Fe₃O₄(10%)-C and Pd/C), the Pd/Fe₃O₄(5%)-C catalyst presented the highest electro-oxidation current density for oxidations of C1-C3 alcohols. According to the CV data, the anodic peak current densities for oxidations of methanol, ethanol, n-propanol and iso-propanol on the Pd/Fe₃O₄(5%)-C catalyst were over 1.7, 1.4, 1.7 and 1.3 times larger than that on the Pd/C catalyst, respectively. Furthermore, the charge transfer resistance of ethanol oxidation on the Pd/Fe₃O₄(5%)-C catalyst was much lower than that on the Pd/C catalyst. For all of the prepared catalysts, the decreases in electro-oxidation current density of the tested C1-C3 alcohols followed the order of n-propanol >ethanol > methanol >iso-propanol. In addition, the presence of Fe₃O₄ nanoparticles in the carbon powder improved the electrochemical stability of the Pd nanoparticles.

Key words: Pd catalyst, Fe₃O₄, Alcohol oxidation, Electrocatalyst

中图分类号:

O646

邹涛,易清风,张媛媛,刘小平,徐国荣,聂会东,周秀林. Pd/Fe₃O₄-C催化剂对甲醇、乙醇和丙醇氧化的电催化活性[J]. 电化学（中英文）, 2017, 23(6): 708-717.

ZOU Tao, YI Qing-feng, ZHANG Yuan-yuan, LIU Xiao-ping, XU Guo-rong, NIE Hui-dongand ZHOU Xiu-lin. Electroactivities of Pd/Fe₃O₄-C catalysts for electro-oxidation of methanol, ethanol and propanol[J]. Journal of Electrochemistry, 2017, 23(6): 708-717.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.161104

https://electrochem.xmu.edu.cn/CN/Y2017/V23/I6/708

参考文献

[1] García-Cruz L, Casado-Coterillo C, Irabien Á, et al. Performance Assessment of Polymer Electrolyte Membrane Electrochemical Reactor Under Alkaline Conditions-A case study with the electrooxidation of Alcohols [J]. Electrochim. Acta, 2016, 206:165-173.

[2]Cai J D, Huang Y Y, Guo Y L. PdTex/C nanocatalysts with high catalytic activity for ethanol electro-oxidation in alkaline medium [J]. Appl. Catal. B: Environ., 2014, 150–151(9):230-237.

[3]Goel J, Basu S. Pt-Re-Sn as Metal Catalysts for Electro-Oxidation of Ethanol in Direct Ethanol Fuel Cell [J]. Energy Procedia, 2012, 28: 66-77.

[4] Yang G, Zhou Y, Pan H B, et al. Ultrasonic-assisted synthesis of Pd–Pt/carbon nanotubes nanocomposites for enhanced electro-oxidation of ethanol and methanol in alkaline medium[J]. Ultrasonics Sonochemistry, 2016, 28,192-198.

[5]Yi Q F, Zou T, Zhang Y Y, et al. A novel alcohol/iron (III) fuel cell [J]. J. Power Sources,2016, 321: 219-225.

[6] Yi Q F, Chen Q H. In situ preparation and high electrocatalytic activity of binary Pd-Ni nanocatalysts with low Pd-loadings [J]. Electrochim. Acta,2015, 182:96-103.

[7] Yi Q F, Chu H, Chen Q H, et al. High Performance Pd, PdNi, PdSn and PdSnNi

Nanocatalysts Supported on Carbon Nanotubes for Electrooxidation of C2C4 Alcohols[J]. Electroanal., 2015, 27(2): 388-397.

[8] Yang H J, Wang H L, Ji S, et al. Synergy between isolated-Fe₃O₄ nanoparticles and CNx layers derived from lysine to improve the catalytic activity for oxygen reduction reaction [J]. Int. J. Hydrog. Energy, 2014, 39(8): 3739-3745.

[9] Huang Y, Liu Y, Yang Z, et al. Synthesis of yolk/shell Fe₃O₄–polydopamine–graphene–Pt nanocomposite with high electrocatalytic activity for fuel cells [J]. J. Power Sources,2014, 246(3): 868-875.

[10] Hong C Y(洪春艳). Preparation and characterization of Au/Fe₃O₄ nanoparticles and Pt/Au/Fe₃O₄ catalysts, Beijing University of Chemical Technology(北京化工大学), China, Master’s Thesis, 2013, p59-68

[11] Fu Z, Yan L, Li K, et al. The performance and mechanism of modified activated carbon air cathode by non-stoichiometric nano Fe₃O₄ in the microbial fuel cell [J]. Biosens. Bioelectron.,2015,74: 989-995.

[12] Wang Y, Zhao Y, Yin J, et al. Synthesis and electrocatalytic alcohol oxidation performance of Pd-Co bimetallic nanoparticles supported on graphene [J]. Inter. J. Hydrogen Energy, 2014, 39(3): 1325-1335.

[13] Zalineeva A, Serov A, Padilla M, et al. Nano-structured Pd-Sn catalysts for alcohol electro-oxidation in alkaline medium [J]. Electrochem. Commun., 2015, 57: 48-51.

[14] Zhang M, Yan Z, Xie J. Core/shell Ni@Pd nanoparticles supported on MWCNTs at improved electrocatalytic performance for alcohol oxidation in alkaline media [J]. Electrochim. Acta, 2012, 77(9): 237-243.

[15] Yi Q F, Sun L Z, Liu X P, et al. Palladium–nickel nanoparticles loaded on multi-walled carbon nanotubes modified with b-cyclodextrin for electrooxidation of alcohols [J]. Fuel,2013, 111: 88-95.

[16] Yi Q F, Niu F G, Song L H, et al. Electrochemical Activity of Novel Titanium-Supported Porous Binary Pd-Ru Particles for Ethanol Oxidation in Alkaline Media [J]. Electroanal., 2011, 23(9): 2232-2240.

[17] Shen P K, Xu C. Alcohol oxidation on nanocrystalline oxide Pd/C promoted electrocatalysts [J]. Electrochem. Commun.,2006, 8(1): 184-188.

[18] Hu F, Chen C, Wang Z, et al. Mechanistic study of ethanol oxidation on Pd–NiO/C electrocatalyst [J]. Electrochim. Acta,2006, 52(3):1087-1091.

[19] Wang H L(王海丽). Studies on oxygen reduction reaction of Pt/C electro-catalyst modified by Fe₃O₄, Dalian Jiaotong University(大连交通大学), China, Master’s Thesis, 2010, pp.29

[20] Manohara R, Goodenough J B. Methanol Oxidation in Acids on Ordered NiTi [J]. J. Mater. Chem.,1992, 2(8):875-887.

[21] ModibediR M, Masombuka T, Mathe M K. Carbon supported Pd–Sn and Pd–Ru–Sn nanocatalysts for ethanol electro-oxidation in alkaline medium [J]. Inter.J.hydrogen energy, 2011,36(8): 4664-4672.

[22] Liu Z, Guo B, Hong L, et al. Microwave heated polyol synthesis of carbon-supported PtSn nanoparticles for methanol electrooxidation [J]. Electrochem. Commun.,2006, 8(1): 83-90.

[23] Liu Z, Zhang X, Hong L. Physical and electrochemical characterizations of nanostructured Pd/C and PdNi/C catalysts for methanol oxidation [J]. Electrochem. Commun.,2009, 11(4): 925-928.

[24] Liu J, Ye J, Xu C, et al. Kinetics of ethanol electrooxidation at Pd electrodeposited on Ti [J]. Electrochem. Commun., 2007, 9(9): 2334-2339.

Pd/Fe₃O₄-C催化剂对甲醇、乙醇和丙醇氧化的电催化活性

Electroactivities of Pd/Fe₃O₄-C catalysts for electro-oxidation of methanol, ethanol and propanol

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	高梦婷, 卫莹, 霍雪萌, 朱文洁, 刘箐箐, 强晋源, 刘婉婉, 王颖, 李旭, 黄剑锋, 冯永强. 氮掺杂碳纳米管上钴和钌位点之间的电子通信促进碱性析氢反应[J]. 电化学（中英文）, 2024, 30(9): 2403081-.
[2]	王昱喆, 蒋卓良, 温波, 黄耀辉, 李福军. 锂氧电池中钌基电催化剂的研究进展[J]. 电化学（中英文）, 2024, 30(8): 2314004-.
[3]	韦聚才, 易娟, 吴旭. 电化学法深度处理电厂脱硫废水[J]. 电化学（中英文）, 2024, 30(4): 2205041-.
[4]	万紫轩, Aidar Kuchkaev, Dmitry Yakhvarov, 康雄武. 单分散Cu-TCPP/Cu₂O杂化微球:一种具有优异电还原CO₂产C₂性能的级联电催化剂[J]. 电化学（中英文）, 2024, 30(1): 2303271-.
[5]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[6]	杨云锐, 董欢欢, 郝志强, 何祥喜, 杨卓, 李林, 侴术雷. 高性能锂硫电池用钴/碳复合材料硫宿主[J]. 电化学（中英文）, 2023, 29(4): 2217003-.
[7]	冯辛, 刘博文, 郭可鑫, 范林丰, 王根香, 次素琴, 温珍海. 基于阳极甘油氧化电催化的碱/酸混合电解制氢研究[J]. 电化学（中英文）, 2023, 29(2): 2215005-.
[8]	孟庆成, 金林薄, 马梦泽, 高学庆, 陈爱兵, 周道金, 孙晓明. 层状金属氢氧化物中铁位点辅助分散铂纳米颗粒用于高效甲醇氧化[J]. 电化学（中英文）, 2023, 29(2): 2215007-.
[9]	韦宗楠, 曹敏纳, 曹荣. 瓜环基金属纳米催化剂的电化学研究进展[J]. 电化学（中英文）, 2023, 29(1): 2215008-.
[10]	郭鸿波, 王亚妮, 郭凯, 雷海涛, 梁作中, 张学鹏, 曹睿. 吸电子和亲水性Co-卟啉促进电催化氧还原反应的研究[J]. 电化学（中英文）, 2022, 28(9): 2214002-.
[11]	梁宵, 张可新, 沈雨澄, 孙轲, 石磊, 陈辉, 郑克岩, 邹晓新. 钙钛矿型水氧化电催化剂[J]. 电化学（中英文）, 2022, 28(9): 2214004-.
[12]	周澳, 郭伟健, 王月青, 张进涛. 焦耳热快速合成双功能电催化剂用于高效水分解[J]. 电化学（中英文）, 2022, 28(9): 2214007-.
[13]	王英超, 马自在, 吴一凡, 王孝广. GCP载钯颗粒复合材料的制备及其电化学合成氨性能研究[J]. 电化学（中英文）, 2022, 28(5): 2104091-.
[14]	张天恩, 颜雅妮, 张俊明, 瞿希铭, 黎燕荣, 姜艳霞. 调控Pt₃Zn合金化程度改善酸性氧还原活性与稳定性[J]. 电化学（中英文）, 2022, 28(4): 2106091-.
[15]	Jafar Hussain Shah, 谢起贤, 匡智崇, 格日乐, 周雯慧, 刘朵绒, Alexandre I. Rykov, 李旭宁, 罗景山, 王军虎. 原位⁵⁷Fe穆斯堡尔光谱技术及其在Ni-Fe基析氧反应电催化剂中的应用[J]. 电化学（中英文）, 2022, 28(3): 2108541-.