电化学(中英文) ›› 2017, Vol. 23 ›› Issue (4): 435-440.  doi: 10.13208/j.electrochem.160419

• 研究论文 • 上一篇    下一篇

四丁基六氟磷酸铵作为锂离子电池阻燃添加剂的研究

赵青1,张倩2,范镜敏2*,郑明森2,董全峰2*   

  1. 1. 淮安市科技情报研究所,淮安 223001; 2. 厦门大学化学化工学院化学系,厦门 361005
  • 收稿日期:2016-04-19 修回日期:2016-05-26 出版日期:2017-08-25 发布日期:2016-08-11
  • 通讯作者: 范镜敏,董全峰 E-mail:qfdong@xmu.edu.cn; jmfan@xmu.edu.cn
  • 基金资助:

    本项目由国家973项目(No. 2015CB251102),国家自然科学基金项目(No. U1305246, No. 21321062)资助

Tetrabutylammonium Hexafluorophosphate as Flame Retardant Additive for Lithium Ion Batteries

ZHAO Qing1, ZHANG Qian2, FAN Jing-min2*, ZHENG Ming-sen2, DONG Quan-feng2*   

  1. 1. Huai An Institute of Science and Technology Information, Huai'an, 223001; 2. Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, Fujian, China
  • Received:2016-04-19 Revised:2016-05-26 Published:2017-08-25 Online:2016-08-11
  • Contact: Jingmin Fan, Quanfeng Dong E-mail:qfdong@xmu.edu.cn; jmfan@xmu.edu.cn

摘要:

近年来关于锂离子电池造成的安全问题甚至事故的报道屡见不鲜,锂离子电池的安全问题已经成为人们关注的焦点. 我们用四丁基六氟磷酸铵(TBAPF6)作为锂离子电池电解液阻燃添加剂,研究发现添加了TBAPF6的电解液具有明显的阻燃效果,同时电解液电导率下降并不明显. LiCoO2/Graphite全电池在添加了TBAPF6的电解液中可逆容量会略有降低,但具有更优异的循环稳定性. 主要是由于TBAPF6添加量的增加会影响石墨电极的库伦效率,延长活化时间. 通过对LiCoO2/Graphite全电池绝热加速量热仪(ARC)测试,表明添加TBAPF6对电池的燃烧有明显的抑制作用. 在TBAPF6添加量至5%时,电池在300 oC内自放热速率不超过0.1oC/min,电池的安全性显著提高.

关键词: 锂离子电池, 阻燃添加剂, 石墨, 四丁基六氟磷酸铵

Abstract: Safety issues have been attracted more and more attentions due to the wide applications of lithium ion batteries. Introducing flame retardant additives are one of the effective strategies to improve the safety of lithium-ion batteries. In this paper, the tetrabutylammonium hexafluorophosphate (TBAPF6) as a flame retardant additive was added to the electrolyte as a flame retardant additive to enhance the safety of lithium ion batteries. The self-extinguishing time (SET) and ionic conductivities of the electrolytes with different TBAPF6 contents were investigated. It is found that TBAPF6 dramatically reduced the flammability of the electrolyte while slightly decreasing ionic conductivitiesconductivity. The electrochemistry electrochemical performances of graphite half cells with higher content of TBAPF6 showed poor compatibility between TBAPF6 additive and graphite anode due to the lack of stable SEI layer formation. But However, the LiCoO2/Graphite graphite full battery with 5% TBAPF6 showed good electrochemical performance and extraordinary thermal stability within 300 oC, representing demonstrating a good flame retardant additive of TBAPF6.