富锂Li1.23Ni0.09Co0.12Mn0.56O2材料的水溶-蒸发法合成及其初始1.5周充放电过程的原位XRD研究

doi:10.13208/j.electrochem.130359

电化学（中英文） ›› 2013, Vol. 19 ›› Issue (6): 537-543. doi: 10.13208/j.electrochem.130359

• 锂离子电池近期研究专辑 (厦门大学杨勇教授主编) • 上一篇下一篇

富锂Li_1.23Ni_0.09Co_0.12Mn_0.56O₂材料的水溶-蒸发法合成及其初始1.5周充放电过程的原位XRD研究

沈重亨¹，沈守宇¹，林舟¹，郑小美¹，苏航¹，黄令^1*，李君涛²，孙世刚¹

1. 厦门大学化学化工学院化学系，福建厦门 361005；2. 厦门大学能源研究院，福建厦门 361005

收稿日期:2013-05-31 修回日期:2013-07-01 出版日期:2013-12-28 发布日期:2013-12-23
通讯作者: 黄令 E-mail:huangl@xmu.edu.cn
基金资助:
国家自然科学基金（No. 21273184）、科技部863（No. 2011AA11A254）和973（No. 2009CB220102）项目资助

Aqueous Solution-Evaporation Route Synthesis and Phase Structural Research of the Li-Rich Cathode Li_1.23Ni_0.09Co_0.12Mn_0.56O₂ by In-Situ XRD

SHEN Chong-Heng¹, SHEN Shou-Yu¹, LIN Zhou¹, ZHENG Xiao-Mei¹, SU Hang1, HUANG Ling^1*, LI Jun-Tao², SUN Shi-Gang¹

1. Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Fujian Xiamen 361005; 2. School of Energy Research, Xiamen University, Fujian Xiamen 361005

Received:2013-05-31 Revised:2013-07-01 Published:2013-12-28 Online:2013-12-23
Contact: HUANG Ling E-mail:huangl@xmu.edu.cn

摘要/Abstract

摘要： 采用水溶-蒸发法成功合成了锂离子电池Li_1.23Ni_0.09Co_0.12Mn_0.56O₂正极材料. 通过扫面电镜(SEM)、非原位XRD、原位XRD观察材料形貌表征材料结构，并测试电极电化学性能. 结果显示，材料为粒径330 nm的多边形结构，是层状的固溶体—Li₂MnO₃结构，该正极0.1C首周期放电比容量250.8 mAh·g^-1，40周期循环容量保持率86.5%. 通过原位XRD可确证电极在首周期充放电过程产生少量Li_0.9MnO₂新相，在其后多周期循环过程电极层状结构趋于向尖晶石结构发生转变致使电极电化学性能恶化. 此外，晶格参数c首周期充电过程先增后减在4.54 V左右保持稳定，放电与第2周期充电过程其值逐渐下降；晶格参数a则经历了下降平稳再升高的过程，该数值的变化均对应于相应电化学行为.

关键词: 锂离子电池, 正极, 水溶-蒸发法, 原位XRD, 结构转变

Abstract: The Li-rich Li_1.23Ni_0.09Co_0.12Mn_0.56O₂material was synthesized via aqueous solution-evaporation route. The structure and morphology of the material were characterized by means of XRD and SEM. The results indicated that the single particle of the product was polygonal with the size of 330 nm and the structure was layered solid solution with a certain amount of Li₂MnO₃. Electrochemical tests showed that the first discharge capacity of the Li-rich layered material was 250.8 mAh·g^-1 at 0.1C，the capacity retention was 86.5% after 40 cycles. Through in-situ XRD study a new phase Li_0.9MnO₂ which would cause electrochemical properties deteriorated due to its structure transformation from layered to spinel came out with a small amount during the first charge-discharge cycle. Moreover, the value of c-parameter increased first and decreased before 4.54 V, and remained stable till the end of the first charge, and then reduced from the first discharge to the second charge continually. However, the value of a-parameter underwent a falling-steady-rising course. The change in the values of the lattice parameters corresponded to the variation of electrochemical behaviors.

Key words: Li-ion battery, cathode, aqueous solution-evaporation route, in-situ XRD, structure transformation

中图分类号:

TM912.9

沈重亨，沈守宇，林舟，郑小美，苏航，黄令*，李君涛，孙世刚. 富锂Li_1.23Ni_0.09Co_0.12Mn_0.56O₂材料的水溶-蒸发法合成及其初始1.5周充放电过程的原位XRD研究[J]. 电化学（中英文）, 2013, 19(6): 537-543.

SHEN Chong-Heng, SHEN Shou-Yu, LIN Zhou, ZHENG Xiao-Mei, SU Hang, HUANG Ling*, LI Jun-Tao, SUN Shi-Gang. Aqueous Solution-Evaporation Route Synthesis and Phase Structural Research of the Li-Rich Cathode Li_1.23Ni_0.09Co_0.12Mn_0.56O₂ by In-Situ XRD[J]. Journal of Electrochemistry, 2013, 19(6): 537-543.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.130359

https://electrochem.xmu.edu.cn/CN/Y2013/V19/I6/537

参考文献

[1] Mohanty D, Kalnaus S, Meisner R A, et al. Structural transformation of a lithium-rich Li1.2Co0.1Mn0.55Ni0.15O2 cathode during high voltage cycling resolved by in situ X-ray diffraction[J]. Journal of Power Sources, 2013, 229: 239-248.
[2] Thackeray M M, Kang S H, Johnson C S, et al. Li2MnO3-stabilized LiMO2 (M = Mn, Ni, Co) electrodes for lithium-ion batteries[J]. Journal of Materials Chemistry, 2007, 17(30): 3112-3125.
[3] Li J, Kl?psch R, Stan M C, et al. Synthesis and electrochemical performance of the high voltage cathode material Li[Li0.2Mn0.56Ni0.16Co0.08]O2 with improved rate capability[J]. Journal of Power Sources, 2011, 196(10): 4821-4825.
[4] Park K S, Song C H, Stephan A M, et al. Influence of solvents on the synthesis and electrochemical properties of Li[Li1/5Ni1/10Co1/5Mn1/2]O2 for the applications in lithium-ion batteries[J]. Journal of Materials Science, 2006, 41(22): 7628-7635.
[5] Zhao Y J, Zhao C S, Sun Z Q, et al. Synthesis and characterization of Li-rich cathode materials Li[Li(1/3-x/3)CoxMn(2/3-2x/3)]O2 by modified pechini method[J]. Acta Chimica Sinica, 2011, 69(2): 117-121.
[6] Hong Y S, Park Y J, Ryu K S, et al.Synthesis and electrochemical properties of nanocrystalline LiNi0.20Li0.20Mn0.60O2. Electrochemical and Solid State Letters, 2003, 6(8): A166-A169.
[7] Du K, Zhou W Y, Hu G R, et al. Synthesis and electrochemical properties of Li[Li0.2Mn0.54Ni0.13Co0.13]O2 as cathode material for Li-ion batteries[J]. Acta Chimica Sinica, 2010, 68(14): 1391-1398.
[8] Du K, Huang X, Hu G R, et al. Synthesis and electrochemical properties of Li[Li0.2Ni0.2Mn0.6]O2 as high capacity cathode material[J]. The Chinese Journal of Nonferrous Metals, 2012, 22(4): 1201-1208.
[9] Yang X Q, Sun X, McBreen J. New findings on the phase transitions in Li1-xNiO2: in situ synchrotron X-ray diffraction studies[J]. Electrochemistry Communications, 1999, 1(6): 227-232.
[10] Yang X Q, Sun X, McBreen J. Structural changes and thermal stability: In situ X-ray diffraction studies of a new cathode material LiMg0.125Ti0.125Ni0.75O2[J]. Electrochemistry Communications, 2000, 2(10): 733-737.
[11] Yang X Q, Sun X, McBreen J.New phases and phase transitions observed in Li1-xCoO2 during charge: In situ synchrotron X-ray diffraction studies[J]. Electrochemistry Communications, 2000, 2(2): 100-103.
[12] Yang X Q, McBreen J, Yoon W S, et al. Crystal structure changes of LiMn0.5Ni0.5O2 cathode materials during charge and discharge studied by synchrotron based in situ XRD[J]. Electrochemistry Communications, 2002, 4(8): 649-654.
[13] Liao P Y, Duh J G, Lee J F, et al. Structural investigation of Li1?xNi0.5Co0.25Mn0.25O2 by in situ XAS and XRD measurements[J]. Electrochimica Acta, 2007, 53(4): 1850-1857.
[14] Liao P Y, Duh J G, Sheu H S. Structural and thermal properties of LiNi0.6?xMgxCo0.25Mn0.15O2 cathode materials[J]. Journal of Power Sources, 2008, 183(2): 766-770.
[15] Nam K W, Yoon W S, Shin H J, et al. In situ X-ray diffraction studies of mixed LiMn2O4-LiNi1/3Co1/3Mn1/3O2 composite cathode in Li-ion cells during charge-discharge cycling[J]. Journal of Power Sources, 2009, 192(2): 652-659.
[16] Yoon W S, Nam K W, Jang D H, et al.The kinetic effect on structural behavior of mixed LiMn2O4-LiNi1/3Co1/3Mn1/3O2 cathode materials studied by in situ time-resolved X-ray diffraction technique[J]. Electrochemistry Communications, 2012, 15(1): 74-77.
[17] Ito A, Li D C, Sato Y, et al. Cyclic deterioration and its improvement for Li-rich layered cathode material Li[Ni0.17Li0.2Co0.07Mn0.56]O2[J]. Journal of Power Sources, 2010, 195(2): 567-573.
[18] Armstrong A R, Holzapfel M, Novak P, et al. Demonstrating oxygen loss and associated structural reorganization in the lithium battery cathode Li[Ni0.2Li0.2Mn0.6]O2[J]. Journal of the American Chemical Society, 2006, 128(26): 8694-8698.
[19] Johnson C S, Li N, Vaughey J T, et al. Lithium-manganese oxide electrodes with layered-spinel composite structures xLi2MnO3·(1-x)Li1+yMn2-yO4 (0[20] Shao H Y, Hackney S A, Armstrong A R, et al. Structural characterization of layered LiMnO2 electrodes by electron diffraction and lattice imaging[J]. Journal of the Electrochemical Society, 1999, 146(7): 2404-2412.
[21] Armstrong A R, Paterson A J, Dupre N, et al. Structural evolution of layered LixMnyO2: Combined neutron, NMR, and electrochemical study[J]. Chemistry of Materials, 2007, 19(5): 1016-1023.
[22] Johnson C S, Li N C, Lefief C, et al. Synthesis, characterization and electrochemistry of lithium battery electrodes: xLi2MnO3·1-xLiMn0.333Ni0.333Co0.333O2(0 <= x <= 0.7)[J]. Chemistry of Materials, 2008, 20(19): 6095-6106.

富锂Li_1.23Ni_0.09Co_0.12Mn_0.56O₂材料的水溶-蒸发法合成及其初始1.5周充放电过程的原位XRD研究

Aqueous Solution-Evaporation Route Synthesis and Phase Structural Research of the Li-Rich Cathode Li_1.23Ni_0.09Co_0.12Mn_0.56O₂ by In-Situ XRD

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	丑佳, 王雅慧, 王文鹏, 辛森, 郭玉国. 面向高性能锂-硫二次电池应用的非对称电极-电解质界面[J]. 电化学（中英文）, 2023, 29(9): 2217009-.
[2]	温波, 朱卓, 李福军. 锂-氧气电池：正极催化剂的最新进展与挑战[J]. 电化学（中英文）, 2023, 29(2): 2215001-.
[3]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[4]	陈思, 郑淞生, 郑雷铭, 张叶涵, 王兆林. 水热法制备锂电池Si@C负极材料的工艺优化研究[J]. 电化学（中英文）, 2022, 28(8): 2112221-.
[5]	王京玥, 王睿, 王诗琦, 王立帆, 詹纯. 一步固相法合成锂离子电池高镍层状正极材料[J]. 电化学（中英文）, 2022, 28(8): 2112131-.
[6]	谯渭川, 李芳儒, 肖瑾林, 屈丽娟, 赵晓, 张梦, 庞春雷, 李子坤, 任建国, 贺雪琴. 硅氧材料的膨胀性能研究和改善[J]. 电化学（中英文）, 2022, 28(5): 2108121-.
[7]	胡炳文, 李超, 耿福山, 沈明. 金属离子电池中的磁共振：从核磁共振(NMR)到电子顺磁共振(EPR)[J]. 电化学（中英文）, 2022, 28(2): 2108421-.
[8]	王加义, 郭胜楠, 王新, 谷林, 苏东. 锂离子电池高镍层状氧化物正极结构失效机制[J]. 电化学（中英文）, 2022, 28(2): 2108431-.
[9]	郭瑞琪, 吴锋, 王欣然, 白莹, 吴川. 多电子反应材料推动高能量密度电池发展：材料与体系创新[J]. 电化学（中英文）, 2022, 28(12): 2219011-.
[10]	朱振威, 邱景义, 王莉, 曹高萍, 何向明, 王京, 张浩. 人工智能在锂离子电池研发中的应用[J]. 电化学（中英文）, 2022, 28(12): 2219003-.
[11]	李西尧, 赵长欣, 李博权, 黄佳琦, 张强. 锂硫电池复合正极研究进展[J]. 电化学（中英文）, 2022, 28(12): 2219013-.
[12]	侯廷政, 陈翔, 蒋璐, 唐城. 当前和下一代锂离子电池电解液的原子尺度微观认识和研究进展[J]. 电化学（中英文）, 2022, 28(11): 2219007-.
[13]	李丹丹, 纪翔宇, 陈明, 杨燕茹, 王晓东, 冯光. 低聚离子液体的体相与界面及其电化学储能应用[J]. 电化学（中英文）, 2022, 28(11): 2219002-.
[14]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.
[15]	蔡雪凡, 孙升. 多孔电极电池的循环伏安法模拟[J]. 电化学（中英文）, 2021, 27(6): 646-657.