功率型锂离子电池负极材料TiO2/石墨烯的制备及其电化学性能研究

doi:10.61558/2993-074X.2904

电化学（中英文） ›› 2012, Vol. 18 ›› Issue (3): 201-204. doi: 10.61558/2993-074X.2904

功率型锂离子电池负极材料TiO₂/石墨烯的制备及其电化学性能研究

秦琳琳, 张焕, 刘晓静, 许剑辉, 施一宁, 郑明森, 董全峰*

厦门大学固体表面物理化学国家重点实验室，化学化工学院化学系，福建厦门 361005

收稿日期:2012-04-30 修回日期:2012-05-10 出版日期:2012-06-28 发布日期:2012-05-15
通讯作者: 董全峰 E-mail:qfdong@xmu.edu.cn
基金资助:
国家自然科学基金项目（No. 200933005, No. 02903077），国家972项目（No. 2009CB220102）资助和厦门市纯电动汽车重大科技专项（I期）（No. 3502Z20121002）

Preparation and Electrochemical Performance of TiO₂/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries

QIN Lin-Lin, ZHANG Huan, LIU Xiao-Jing, XU Jian-Hui, SHI Yi-Ning, ZHENG Ming-Sen, DONG Quan-Feng*

State Key Lab of Physical Chemistry of Solid Surfaces, Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, Fujian, China

Received:2012-04-30 Revised:2012-05-10 Published:2012-06-28 Online:2012-05-15
Contact: DONG Quan-Feng E-mail:qfdong@xmu.edu.cn

摘要/Abstract

摘要： 采用回流法制备出了蜂窝状的TiO2/石墨烯（GNs）复合材料.扫描电子显微镜（SEM）及透射电子显微镜（TEM）表征结果表明，TiO2颗粒约5~10 nm，均匀地分散在石墨烯的表面.锂电池测试显示，1C充电容量稳定在240.1 mAh?g-1；30C充电容量为169.5 mAh?g-1；当电流调回1C时，其充电容量仍可完全恢复（241.7 mAh?g-1）；10C 300周期循环电极容量保持率为89.8%.

关键词: 锂离子电池, 负极材料, TiO2, 石墨烯

Abstract: The honeycomb-like porous TiO2/graphenes (TiO2/GNs) nanocomposite was prepared by a reflux method. SEM and TEM results showed that nanosized anatase TiO2 (about 5~10 nm) were dispersed uniformly on the surface of the GNs. The TiO2/GNs composite showed excellent rate and cycling performance: A stable charge capacity of 169.5 mAh?g-1 was obtained at 30C, and can restore to 241.7 mAh?g-1 while current went back to 1C. The stable charge capacity of TiO2/GNs nanocomposite electrode up to 201.9 mAh?g-1 was achieved at 10C in the first cycle, and could be maintained at 181.4 mAh?g-1 after 300 times of cycling.

Key words: lithium-ion battery, anode materials, TiO2, graphene

中图分类号:

O646
TM912.9

秦琳琳, 张焕, 刘晓静, 许剑辉, 施一宁, 郑明森, 董全峰. 功率型锂离子电池负极材料TiO₂/石墨烯的制备及其电化学性能研究[J]. 电化学（中英文）, 2012, 18(3): 201-204.

QIN Lin-Lin, ZHANG Huan, LIU Xiao-Jing, XU Jian-Hui, SHI Yi-Ning, ZHENG Ming-Sen, DONG Quan-Feng. Preparation and Electrochemical Performance of TiO₂/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries[J]. Journal of Electrochemistry, 2012, 18(3): 201-204.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2904

https://electrochem.xmu.edu.cn/CN/Y2012/V18/I3/201

参考文献

[1] Linsebigler A L, Lu G, Yates J T. Photocatalysis on TiO2 surfaces: principles, mechanisms, and selected results[J]. Chemical Review, 1995, 95(3): 735-758.
[2] Bach U, Lupo D, Comte P, et al. Solid-state dye-sensitized mesoporous TiO2 solar cells with high photon-to-electron conversion efficiencies[J]. Nature, 1998, 395(6702): 583-585.
[3] Xia Y Y. Review: Ti-based compounds as anode materials for Li-ion batteries[J]. Energy & Environmental Science, 2012, 5(5): 6652-6657.
[4] Sudant G, Baudrin E, Larcher D, et al. Electrochemical lithium reactivity with nanotextured anatase-type TiO2[J]. Journal of Materials Chemistry, 2005, 15(12): 1263-1269.
[5] Hu Y S, Kienle L, Guo Y G, et al. High lithium electroactivity of nanometer-sized rutile TiO2[J]. Advanced Materials, 2006, 18(11): 1421-1426.
[6] Lee D H, Park J G, Jin C K, et al. Preparation of brookite-type TiO2/carbon nanocomposite electrodes for application to Li ion batteries[J]. European Journal of Inorganic Chemistry, 2008, 2008(6): 878-882.
[7] Moriguchi I, Hidaka R, Yamada H, et al. A mesoporous nanocomposite of TiO2 and carbon nanotubes as a high-rate Li-intercalation electrode material[J]. Advanced Materials, 2006, 18(1): 69-73.
[8] Chen P C, Tsai M C, Chen H C, et al. Self-carbonized lamellar nano/micro hierarchical structure C/TiO2 and its Li-ion intercalation performance[J]. Journal of Materials Chemistry, 2012, 22(12): 5349-5355.
[9] Ding Y-H, Zhang P, Ren H-M, et al. Preparation of graphene/TiO2 anode materials for lithium-ion batteries by a novel precipitation method[J]. Materials Research Bulletin, 2011, 46(12): 2403-2407.
[10] Bong S, Kim Y R, Kim I, et al. Graphene supported electrocatalysts for methanol oxidation[J]. Electrochemistry Communications, 2010, 12(1): 129-131.
[11] Kamat P V. Graphene-based nanoassemblies for energy conversion[J]. The Journal of Physical Chemistry Letters, 2011, 2(3): 242-251.
[12] Wang C, Li D, Too C O, et al. Electrochemical properties of graphene paper electrodes used in lithium batteries[J]. Chemistry of Materials, 2009, 21(13): 2604-2606.
[13] Ding S, Chen J S, Luan D, et al. Graphene-supported anatase TiO2 nanosheets for fast lithium storage[J]. Chemical Communications, 2011, 47(20): 5780-5782.
[14] Wang D, Kou R, Choi D, et al. Ternary self-assembly of ordered metal oxide-graphene nanocomposites for electrochemical energy storage[J]. ACS Nano, 2010, 4(3): 1587-1595.

[1]	左东旭, 李培超. 基于电化学-热-力耦合模型的快速充电下锂离子电池的老化特性分析[J]. 电化学（中英文）, 2024, 30(9): 2402061-.
[2]	陈露露, 李浩冉, 刘维祎, 王伟. 锂离子电池正极材料原位漫反射光谱电化学研究[J]. 电化学（中英文）, 2024, 30(6): 2314006-.
[3]	崔苗苗, 韩联欢, 曾兰平, 郭佳瑶, 宋维英, 刘川, 吴元菲, 罗世翊, 刘云华, 詹东平. 单层石墨烯微米尺度图案化和功能化：调控电子传输特性[J]. 电化学（中英文）, 2024, 30(3): 2305251-.
[4]	范佳琪, 宋焕巧, 安佳莹, 阿依达娜·阿曼太, 陈默. 碳限域Li₃VO₄纳米材料的制备及其储锂性能[J]. 电化学（中英文）, 2023, 29(11): 211203-.
[5]	殷秀平, 赵玉峰, 张久俊. 钠离子电池硬碳基负极材料的研究进展[J]. 电化学（中英文）, 2023, 29(10): 2204301-.
[6]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[7]	陈思, 郑淞生, 郑雷铭, 张叶涵, 王兆林. 水热法制备锂电池Si@C负极材料的工艺优化研究[J]. 电化学（中英文）, 2022, 28(8): 2112221-.
[8]	王京玥, 王睿, 王诗琦, 王立帆, 詹纯. 一步固相法合成锂离子电池高镍层状正极材料[J]. 电化学（中英文）, 2022, 28(8): 2112131-.
[9]	谯渭川, 李芳儒, 肖瑾林, 屈丽娟, 赵晓, 张梦, 庞春雷, 李子坤, 任建国, 贺雪琴. 硅氧材料的膨胀性能研究和改善[J]. 电化学（中英文）, 2022, 28(5): 2108121-.
[10]	王加义, 郭胜楠, 王新, 谷林, 苏东. 锂离子电池高镍层状氧化物正极结构失效机制[J]. 电化学（中英文）, 2022, 28(2): 2108431-.
[11]	郭瑞琪, 吴锋, 王欣然, 白莹, 吴川. 多电子反应材料推动高能量密度电池发展：材料与体系创新[J]. 电化学（中英文）, 2022, 28(12): 2219011-.
[12]	朱振威, 邱景义, 王莉, 曹高萍, 何向明, 王京, 张浩. 人工智能在锂离子电池研发中的应用[J]. 电化学（中英文）, 2022, 28(12): 2219003-.
[13]	侯廷政, 陈翔, 蒋璐, 唐城. 当前和下一代锂离子电池电解液的原子尺度微观认识和研究进展[J]. 电化学（中英文）, 2022, 28(11): 2219007-.
[14]	李丹丹, 纪翔宇, 陈明, 杨燕茹, 王晓东, 冯光. 低聚离子液体的体相与界面及其电化学储能应用[J]. 电化学（中英文）, 2022, 28(11): 2219002-.
[15]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.

功率型锂离子电池负极材料TiO₂/石墨烯的制备及其电化学性能研究

Preparation and Electrochemical Performance of TiO₂/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics