类溶胶-凝胶法制备LiMn_2O_(4-δ)Cl_δ正极材料

电化学（中英文） ›› 2001, Vol. 7 ›› Issue (1): 132-135.

类溶胶-凝胶法制备LiMn_2O_(4-δ)Cl_δ正极材料

陈召勇,贺益,刘兴泉,李志结,于作龙

中国科学院成都有机化学所功能材料开发中心!四川成都,610041,中国科学院成都有机化学所功能材料开发中心!四川成都,610041,中国科学院成都有机化学所功能材料开发中心!四川成都,610041,中国科学院成都有机化学所功能材料开发中心!四川成都,610041,中国科学院成都有机化学所功

收稿日期:2001-02-28 修回日期:2001-02-28 出版日期:2001-02-28 发布日期:2001-02-28

Synthesis of LiMn_2O_(4-δ) Cl_δ Cathode Material by Like-Sol-Gel Methode

CHEN zhao yong *, HE Yi, LIU xing quan, LI zhi jie, YU zuo long

(R & D Center for Functional Materials, Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu,610041,China

Received:2001-02-28 Revised:2001-02-28 Published:2001-02-28 Online:2001-02-28

摘要/Abstract

摘要： 本文以水合氢氧化锂 (LiOH .H2 O)、水合硝酸锰 (Mn(No3) 2 .6H2 O) ,水合氯化锂 (LiCl.H2 O)为原料 ,用类溶胶凝胶法制备了LiMn2 O4 δClδ,并且以此作正极进行了电化学测试 .结果表明 ,掺氯的尖晶石LiMn2 O4 正极材料具有优异的稳定性 ,且循环稳定后 ,容量几乎没有衰减 .

关键词: 类溶胶凝胶法, LiMn2O4δClδ, 正极材料

Abstract: LiMn 2O 4 δ Cl δ was synthesized by like sol gel methode, with calculated LiOH.H 2O, Mn(No 3) 2.6H 2O and LiCl.H 2O, and made electrochemical test with these compounds as positive materials. Result demostrated that LiMn 2O 4 δ Cl δ cathode material has exellent stability and nearly no capacity loss after reaching stability.

Key words: Like sol gel methode, LiMn 2O 4 δ Cl δ, Cathode material

中图分类号:

TM911
O646

陈召勇,贺益,刘兴泉,李志结,于作龙. 类溶胶-凝胶法制备LiMn_2O_(4-δ)Cl_δ正极材料[J]. 电化学（中英文）, 2001, 7(1): 132-135.

CHEN zhao yong *, HE Yi, LIU xing quan, LI zhi jie, YU zuo long . Synthesis of LiMn_2O_(4-δ) Cl_δ Cathode Material by Like-Sol-Gel Methode[J]. Journal of Electrochemistry, 2001, 7(1): 132-135.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2001/V7/I1/132

参考文献

[1]　P .Arora ,B .N .Popov ,R .E .White .Electrochemicalinvestigationsofcobalt dopedLiMn2 O4 ascathoedma terialsforlithium ionbatteries[J].J .Electrochem .Soc .,1998,145,80 7. [2 ]　J .M .Tarascon ,D .Guyomand .TheLi1+xMn2 O4 /Crocking chairsystem :areview[J].Electrochemica .Ac ta .,1993,38,12 2 1 12 31. [3]　A .D .Roberson ,S .H .Lu ,W .F .Howard .M3+ modifiedLiMn2 O4 spinelintercalationcathodes[J].J.Elec trochem .Soc .,1999,146 ,1351. [4 ]　N .Hayashi,H .ikuta ,M .Wakihara .CathodeofLiMgyMn2 yO4 andLiMgyMn2 yO4 spinelphasesforlithiumsecondarybatteries[J].J .Electrochem .Soc .,1998,146 ,1351. [5]　P .Arora ,B .N .Popov ,R .E .White .Electrochemicalinvestigationsofcobalt dopedLiMn2 O4 ascathodema terialsforlithium ionbatteries[J].J .Electrochem .Soc .,1998,145,84 7. [6 ]　J .R .Dahn ,Taozheng ,C .L .Thomas .StructureandelectrochemistryofLiCrxMn2 xO4 for 1.0 .x .1.5[J].J .Electrochem .Soc .,1998,145,851. [7]　Qimingzhong ,ArmanBonakarpour,Meijiezhang ,YuanGao .synthesisandelectrochemistryofLiNixMn2 xO4 [J].J .electrochem .Soc .,1997,144 ,2 0 5. [8]　YongyaoXia ,YasufumiHideshima ,NaokiKumada .StudiesonLi Mn Ospinelsystemasacathodefor 4vlithiumbatteries[J].JournalofPowerSources74 ,1998,2 4 2 8. [9]　M .R .Palacin ,F .LeCras,L .Seguin .Insitustrucualstudyof 4v rangelithiumextration/insertioninflu oeine substitutedLiMn2 O4 [J].JournalofSolidStateChemistry 144 ,1999,36 1 371. [10 ]　G .G .Amatucci,N .Pereira ,T .Zheng .EnhancementoftheelectrochemicalpropertiesofLi1Mn2 O4 throughchemicalsubstitution[J].JournalofPowerSources81 82 ,1999,39 4 3. [11]　ZhaoyongChen ,XinquanLiu ,ZuolongYu .ElectrochemicalpropertiesofspinelLiMn2 O4 δFδforcathodematerialsofsecondaryLithium ionbatter[J].chinesechemicalletters ,2 0 0 0 ,11,4 55 4 58. [12 ]　W .Liu ,K .Kowal,G .C .Farrington .MechanismoftheelectrochemicalinsertionoflithiumintoLiMn2 O4spinels[J].J .Electrochem .Soc .,1998,145,4 59.

[1]	陈露露, 李浩冉, 刘维祎, 王伟. 锂离子电池正极材料原位漫反射光谱电化学研究[J]. 电化学（中英文）, 2024, 30(6): 2314006-.
[2]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[3]	胡炳文, 李超, 耿福山, 沈明. 金属离子电池中的磁共振：从核磁共振(NMR)到电子顺磁共振(EPR)[J]. 电化学（中英文）, 2022, 28(2): 2108421-.
[4]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.
[5]	滕久康, 王庆杰, 张亮, 张红梅, 陈晓涛, 张鹏, 赵金保. 热处理时间对锂电池正极材料Cr₈O₂₁的影响[J]. 电化学（中英文）, 2021, 27(6): 689-697.
[6]	王存, 张维江, 何腾飞, 雷博, 史尤杰, 郑耀东, 罗伟林, 蒋方明. NCA三元锂离子电池分荷电状态循环的热特性和容量衰退研究[J]. 电化学（中英文）, 2020, 26(6): 777-788.
[7]	王杜丹, 王非, 翟欢欢, 李玉鹏, 杨纳川, 陈康华. 富锂层状正极材料Li₂MnO₃的表面改性及其电化学性能研究[J]. 电化学（中英文）, 2020, 26(2): 289-297.
[8]	王非, 翟欢欢, 王杜丹, 李玉鹏, 陈康华. Sn-Cl共掺杂的锂离子正极材料Li₂MnO₃的结构及电化学性能研究[J]. 电化学（中英文）, 2020, 26(1): 148-155.
[9]	黄云辉. 钴酸锂正极材料与锂离子电池的发展 ——2019年诺贝尔化学奖解读[J]. 电化学（中英文）, 2019, 25(5): 609-613.
[10]	王凡凡, 刘晓斌, 陈龙, 陈程成, 刘永畅, 范丽珍. 室温钠离子电池关键材料研究进展[J]. 电化学（中英文）, 2019, 25(1): 55-76.
[11]	谢永纯，王成，蒋芳，杨洋，苏静，龙云飞，文衍宣. 钠锰比对Na_xMnO₂的性能和钠离子脱嵌过程的影响[J]. 电化学（中英文）, 2018, 24(4): 375-384.
[12]	关小云，洪朝钰，朱建平，王伟立，李益孝，杨勇. 高首效富镍正极材料LiNi_0.6Co_0.2Mn_0.2O₂的合成及电化学性能研究[J]. 电化学（中英文）, 2018, 24(1): 56-62.
[13]	魏雪霞，黄嘉祺，刘施阳，程璇，张颖. 不同羧酸对钒改性硅酸铁锂结构性能的影响[J]. 电化学（中英文）, 2018, 24(1): 72-80.
[14]	胡燚，何湘柱, 邓忠德，孔令涌，尚伟丽. 锂离子电池正极材料LiNi _0.5Co_0.2Mn _0.3O₂和LiNi_0.5Co _0.2Mn _0.3O₂/LiFePO₄容量衰减原因分析[J]. 电化学（中英文）, 2017, 23(6): 675-683.
[15]	张广瑞，胡利强，张宝珠. 一种新型的碳复合钼掺杂的钒氧化物纳米线钠离子电池正极材料[J]. 电化学（中英文）, 2017, 23(4): 456-465.