壳聚糖/硝酸铁凝胶制备铁氮掺杂多孔碳片作为高效氧还原电催化剂的研究

doi:10.13208/j.electrochem.151231

电化学（中英文） ›› 2016, Vol. 22 ›› Issue (6): 624-630. doi: 10.13208/j.electrochem.151231

壳聚糖/硝酸铁凝胶制备铁氮掺杂多孔碳片作为高效氧还原电催化剂的研究

孟凡陆^1，2，张新波²，鄢俊敏^1*

1. 吉林大学材料科学与工程学院，汽车材料教育部重点实验室，吉林长春 130022；2. 中国科学院长春应用化学研究所，稀土资源利用国家重点实验室，吉林长春 130022

收稿日期:2015-12-30 修回日期:2016-03-15 出版日期:2016-12-28 发布日期:2016-04-05
通讯作者: 鄢俊敏 E-mail:junminyan@jlu.edu.cn
基金资助:
基金委优青 (21422108)资助

Chitosan/Nonahydrate Gel Derived Fe-N-Doped Porous Carbon Sheet as High-Efficient ORR Electrocatalyst

MENG Fan-Lu^{1, 2}, ZHANG Xin-Bo ², YAN Jun-Min ^1*

(1. Key Laboratory of Automobile Materials, Ministry of Education and College of Materials Science and Engineering, Jilin University, Changchun 130012, China; 2. State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130012, China)

Received:2015-12-30 Revised:2016-03-15 Published:2016-12-28 Online:2016-04-05
Contact: YAN Jun-Min E-mail:junminyan@jlu.edu.cn

摘要/Abstract

摘要：

以壳聚糖/硝酸铁凝胶为前躯体，实现了含氮高分子与金属盐的均匀混合，将凝胶冷冻干燥处理后，经过热处理和酸刻蚀得到了成分及微结构更加均匀的铁氮掺杂多孔碳片. 铁氮掺杂多孔碳片与商业铂碳相比，具有更高的起始电位，半波电位和优秀的循环性能，在碱性燃料电池的测试中实现了更高的功率密度. 铁氮掺杂多孔碳片出色的氧还原电催化性能归因于铁在壳聚糖中的原子级分散所导致的均匀分布的铁氮碳催化活性位，大的比表面积和均匀的孔道分布.

关键词: 铁氮掺杂多孔碳片, 氧还原, 凝胶, 多孔结构

Abstract:

The chitosan/nonahydrate gel was used as a precursor to realize the uniform mixture of N-polymer and metal salt. After lyophilization treatment, the gel went through heat treatment and acid etch. Accordingly, the Fe-N-doped porous carbon sheet with homogenous composition and microstructure was prepared. Compared with the commercial Pt/C catalyst, the Fe-N-doped porous carbon sheet exhibited more positive onset potential and half-wave potential, higher current density, and especially, excellent durability. The power density of 318 mW·cm^-2 was obtained in alkaline fuel cell with the Fe-N-doped porous carbon sheet as a cathode catalyst, which is higher than 267 mW·cm^-2with the Pt/C as a cathode catalyst. The improved cell perforence with the Fe-N-doped porous carbon sheet might be contributed to the atomicaly dispersed iron in chitosan, which results in the homogenous dispersion of Fe-N-C active site, high specific surface area and pore size distribution.

Key words: Fe-N-doped porous carbon sheet, oxygen reduction reaction, gel, porous structure

中图分类号:

O646

孟凡陆, 张新波, 鄢俊敏. 壳聚糖/硝酸铁凝胶制备铁氮掺杂多孔碳片作为高效氧还原电催化剂的研究[J]. 电化学（中英文）, 2016, 22(6): 624-630.

MENG Fan-Lu, ZHANG Xin-Bo, YAN Jun-Min. Chitosan/Nonahydrate Gel Derived Fe-N-Doped Porous Carbon Sheet as High-Efficient ORR Electrocatalyst[J]. Journal of Electrochemistry, 2016, 22(6): 624-630.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.151231

https://electrochem.xmu.edu.cn/CN/Y2016/V22/I6/624

参考文献

[1] Zhang S, Hao Y, Su D, et al. Monodisperse core/shell Ni/FePt nanoparticles and their conversion to Ni/Pt to catalyze oxygen reduction[J]. Journal of the American Chemical Society, 2014, 136(45): 15921-15924.

[2] Wang D, Xin H L, Hovden R, et al. Structurally ordered intermetallic platinum–cobalt core–shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts[J]. Nature materials, 2013, 12(1): 81-87.

[3] Ruan L, Zhu E, Chen Y, et al. Biomimetic synthesis of an ultrathin platinum nanowire network with a high twin density for enhanced electrocatalytic activity and durability[J]. Angewandte Chemie International Edition, 2013, 52(48): 12577-12581. [4] Nesselberger M, Roefzaad M, Hamou R F, et al. The effect of particle proximity on the oxygen reduction rate of size-selected platinum clusters[J]. Nature materials, 2013, 12(10): 919-924.

[5] Lu Y, Jiang Y, Gao X, et al. Strongly Coupled Pd Nanotetrahedron/Tungsten Oxide Nanosheet Hybrids with Enhanced Catalytic Activity and Stability as Oxygen Reduction Electrocatalysts[J]. Journal of the American Chemical Society, 2014, 136(33): 11687-11697.

[6] Hoque M A, Hassan F M, Higgins D, et al. Multigrain Platinum Nanowires Consisting of Oriented Nanoparticles Anchored on Sulfur-Doped Graphene as a Highly Active and Durable Oxygen Reduction Electrocatalyst[J]. Advanced Materials, 2015, 27(7): 1229-1234.

[7] Guo S, Zhang S, Su D, et al. Seed-mediated synthesis of core/shell FePtM/FePt (M= Pd, Au) nanowires and their electrocatalysis for oxygen reduction reaction[J]. Journal of the American Chemical Society, 2013, 135(37): 13879-13884.

[8] Guo S, Li D, Zhu H, et al. FePt and CoPt nanowires as efficient catalysts for the oxygen reduction reaction[J]. Angewandte Chemie International Edition, 2013, 52(12): 3465-3468.

[9] Zhao X, Chen S, Fang Z, et al. Octahedral Pd@ Pt1. 8Ni Core–Shell Nanocrystals with Ultrathin PtNi Alloy Shells as Active Catalysts for Oxygen Reduction Reaction[J]. Journal of the American Chemical Society, 2015, 137(8): 2804-2807.

[10] Shui J, Chen C, Li J. Evolution of nanoporous Pt–Fe alloy nanowires by dealloying and their catalytic property for oxygen reduction reaction[J]. Advanced Functional Materials, 2011, 21(17): 3357-3362.

[11] Zhu Y, Zhang B, Liu X, et al. Unravelling the Structure of Electrocatalytically Active Fe–N Complexes in Carbon for the Oxygen Reduction Reaction[J]. Angewandte Chemie International Edition, 2014, 53(40): 10673-10677.

[12] Wu G, More K L, Johnston C M, et al. High-performance electrocatalysts for oxygen reduction derived from polyaniline, iron, and cobalt[J]. Science, 2011, 332(6028): 443-447.

[13] Chang S T, Wang C H, Du H Y, et al. Vitalizing fuel cells with vitamins: pyrolyzed vitamin B12 as a non-precious catalyst for enhanced oxygen reduction reaction of polymer electrolyte fuel cells[J]. Energy & Environmental Science, 2012, 5(1): 5305-5314.

[14] Zhao Y, Watanabe K, Hashimoto K. Self-supporting oxygen reduction electrocatalysts made from a nitrogen-rich network polymer[J]. Journal of the American Chemical Society, 2012, 134(48): 19528-19531.

[15] Yuan S, Shui J L, Grabstanowicz L, et al. A Highly Active and Support‐Free Oxygen Reduction Catalyst Prepared from Ultrahigh‐Surface‐Area Porous Polyporphyrin[J]. Angewandte Chemie International Edition, 2013, 52(32): 8349-8353.

[16] Wu Z S, Chen L, Liu J, et al. High‐Performance Electrocatalysts for Oxygen Reduction Derived from Cobalt Porphyrin‐Based Conjugated Mesoporous Polymers[J]. Advanced Materials, 2014, 26(9): 1450-1455.

[17] Liang H W, Wei W, Wu Z S, et al. Mesoporous metal–nitrogen-doped carbon electrocatalysts for highly efficient oxygen reduction reaction[J]. Journal of the American Chemical Society, 2013, 135(43): 16002-16005.

壳聚糖/硝酸铁凝胶制备铁氮掺杂多孔碳片作为高效氧还原电催化剂的研究

Chitosan/Nonahydrate Gel Derived Fe-N-Doped Porous Carbon Sheet as High-Efficient ORR Electrocatalyst

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	陈发东, 谢卓洋, 李孟婷, 陈四国, 丁炜, 李莉, 李静, 魏子栋. 系列综述（1/4）:重庆大学魏子栋教授课题组在电化学能源转换方面的研究进展：燃料电池高性能氧还原催化剂[J]. 电化学（中英文）, 2024, 30(7): 2314007-.
[2]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[3]	李春艳, 张蕊, 巴笑杰, 姜晓乐, 阳耀月. 氮掺杂多孔碳包覆铁纳米粒子催化剂用于高效碱性介质中氧还原反应[J]. 电化学（中英文）, 2023, 29(5): 2210241-.
[4]	刘思淼, 周景娇, 季世军, 文钟晟. FeNi-CoP/NC双功能催化剂的制备及电催化性能研究[J]. 电化学（中英文）, 2023, 29(10): 211118-.
[5]	王健, 轩文辉, 何倩, 蒋金霞, 周圆圆, 聂瑶, 廖强, 邵敏华, 丁炜, 魏子栋. 类超晶格结构：有序性传质赋予燃料电池高品质输出性能[J]. 电化学（中英文）, 2023, 29(1): 2215003-.
[6]	郭鸿波, 王亚妮, 郭凯, 雷海涛, 梁作中, 张学鹏, 曹睿. 吸电子和亲水性Co-卟啉促进电催化氧还原反应的研究[J]. 电化学（中英文）, 2022, 28(9): 2214002-.
[7]	张天恩, 颜雅妮, 张俊明, 瞿希铭, 黎燕荣, 姜艳霞. 调控Pt₃Zn合金化程度改善酸性氧还原活性与稳定性[J]. 电化学（中英文）, 2022, 28(4): 2106091-.
[8]	冯雅辰, 王翔, 王宇琪, 严会娟, 王栋. 电催化氧还原反应的原位表征[J]. 电化学（中英文）, 2022, 28(3): 2108531-.
[9]	袁会芳, 张越, 翟兴吾, 胡立兵, 葛桂贤, 王刚, 于锋, 代斌. 氮掺杂碳原位锚定铜纳米颗粒用于高效氧还原反应催化剂[J]. 电化学（中英文）, 2021, 27(6): 671-680.
[10]	周莉, 吴勰, 薛照明. 热塑性聚氨酯基聚合物电解质的制备与表征[J]. 电化学（中英文）, 2021, 27(4): 439-448.
[11]	林华, 吴艺津, 李君涛, 周尧. 一锅法制备Fe₂O₃@Fe-N-C氧还原电催化剂及其锌-空气电池的性能研究[J]. 电化学（中英文）, 2021, 27(4): 366-376.
[12]	李文杰, 田东旭, 杜红, 燕希强. ORR催化剂Ni_m@Pt₁Au_n_-_m_-1(n = 19, 38, 55, 79; m = 1, 6, 13, 19)的密度泛函研究[J]. 电化学（中英文）, 2021, 27(4): 357-365.
[13]	刘芳艳, 张倩, 李玥琨, 黄丰, 王梦晔. Co_1-_xS-MnS@CNTs/CNFs的制备及其氧还原电催化性能[J]. 电化学（中英文）, 2021, 27(3): 301-310.
[14]	吴志鹏, 钟传建. 钯基氧还原和乙醇氧化反应电催化剂:关于结构和机理研究的一些近期见解[J]. 电化学（中英文）, 2021, 27(2): 144-156.
[15]	徐明俊, 刘杰, 葛君杰, 刘长鹏, 邢巍. 长春应化所金属氮碳氧还原催化剂的研究进展[J]. 电化学（中英文）, 2020, 26(4): 464-473.