Al掺杂尖晶石LiMn2O4正极材料的性能

doi:10.61558/2993-074X.2954

电化学（中英文） ›› 2013, Vol. 19 ›› Issue (3): 232-236. doi: 10.61558/2993-074X.2954

• 锂离子和燃料电池近期研究专辑（厦门大学董全峰教授主编） • 上一篇下一篇

Al掺杂尖晶石LiMn₂O₄正极材料的性能

王永龙，王文阁，张倩，王昕，曹建胜，叶世海*

南开大学新能源材料化学研究所，天津 300071

收稿日期:2012-10-12 修回日期:2013-01-16 出版日期:2013-06-28 发布日期:2013-01-21
基金资助:
国家自然科学基金项目（No. 21273119）资助

Electrochemical Performance of Al-Doped Spinel LiMn₂O₄ Cathode Material for Li-ion Batteries

WANG Yong-Long, WANG Wen-Ge, ZHANG Qian, WANG Xin, CAO Jian-Sheng, YE Shi-Hai*

Institute of New Energy Material Chemistry, Nankai University, Tianjin 300071, China

Received:2012-10-12 Revised:2013-01-16 Published:2013-06-28 Online:2013-01-21

摘要/Abstract

摘要： 尖晶石LiMn₂O₄作为锂离子电池正极可大电流放电，且成本低、环境友好. 采用溶胶-凝胶法制备尖晶石LiMn₂O₄及Al掺杂材料. 使用X-射线衍射（XRD）和扫描电子显微镜（SEM）观察材料结构与形貌. 结果表明，复合材料颗粒尺寸300 ~ 500 nm，呈类球形. 电化学恒流充放电测试表明，Al掺杂尖晶石LiMn₂O₄电极的循环性明显提高，Al掺杂5%LiMn₂O₄（by mass，下同）正极在1C倍率充放电100周期循环后的容量保持率为98.2%，1C倍率充电、5C倍率放电下，100周期循环后其容量保持率为99.0%，表现出较优的电化学循环性能.

关键词:

锂离子电池, 正极, 尖晶石结构, Al掺杂, 循环性能

Abstract: Spinel LiMn₂O₄, a cathode material for Li-ion batteries, is featured as good high-rate performance, low cost and environmental friendly. The pristine and Al-doped LiMn₂O₄ samples were prepared by sol-gel method. The structure and micromorphology of the as-prepared samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results demonstrated that the as-prepared LiMn₂O₄ samples had a typical cubic spinel structure and were composed of sphere-like particles with a diameter range of 300 ~ 500 nm. Galvanostatic charge-discharge tests showed that the LiMn₂O₄ samples doped with Al element exhibited an enhanced cycling performance. Especially, in the case of LiMn₂O₄ with 5% Al-doped, the discharge capacity retention was about 98.2% at the rate of 1C discharge and was 99% at the rate of 5C discharge, based on the same charge rate of 1C.

Key words:

Li-ion batteries, cathode, spinel structure, Al-doping, cycling performance

中图分类号:

O646

王永龙, 王文阁, 张倩, 王昕, 曹建胜, 叶世海. Al掺杂尖晶石LiMn₂O₄正极材料的性能[J]. 电化学（中英文）, 2013, 19(3): 232-236.

WANG Yong-Long, WANG Wen-Ge, ZHANG Qian, WANG Xin, CAO Jian-Sheng, YE Shi-Hai. Electrochemical Performance of Al-Doped Spinel LiMn₂O₄ Cathode Material for Li-ion Batteries[J]. Journal of Electrochemistry, 2013, 19(3): 232-236.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2954

https://electrochem.xmu.edu.cn/CN/Y2013/V19/I3/232

参考文献

[1] Cao Y J(曹艳军), Long X Y(龙翔云), Cheng Y F(程云峰). Research development of cathode electrode material for lithium-ion batteries[J]. Technology & Development of Chemical Industry (化工技术与开发), 2007, 36(03): 16-18.
[2] Ohzuku T, Brodd R J, An overview of positive-electrode materials for advanced lithium-ion batteries[J]. Journal of Power Sources, 2007, 174(2): 449-456.
[3] Aoshima T, Okahara K, Kiyohara C, et al. Mechanisms of manganese spinels dissolution and capacity fade at high temperature[J]. Journal of Power Sources, 2001, 97-98: 377-380.
[4] Tang S B, Lai M O, Lu L. Electrochemical studies of low-temperature processed nano-crystalline LiMn₂O₄ thin film cathode at 55 °C[J]. Journal of Power Sources, 2007, 164(1): 372-378.
[5] Ouyang C Y, Shi S Q, Lei M S. Jahn-Teller distortion and electronic structure of LiMn₂O₄[J]. Journal of Alloys and Compounds, 2009, 474(1/2): 370-374.
[6] Aurbach D. Review of selected electrode-solution interactions which determine the performance of Li and Li ion batteries[J]. Journal of Power Sources, 2000, 89(2): 206-218.
[7] Xiao L F, Zhao Y Q, Yang Y Y, et al. Enhanced electrochemical stability of Al-doped LiMn₂O₄ synthesized by a polymer-pyrolysis method[J]. Electrochimica Acta, 2008, 54(2): 545-550.
[8] Lee C W, Kim H S, Moon S I. Effects on surface modification of spinel LiMn₂O₄ material for lithium-ion batteries[J]. Materials Science and Engineering: B, 2005, 123(3): 234-237.
[9] Liu Z L, Wang H B, Fang L, et al. Improving the high-temperature performance of LiMn₂O₄ spinel by micro-emulsion coating of LiCoO₂[J]. Journal of Power Sources, 2002, 104(1): 101-107.
[10] Skapin A S, Gaberscek M, Dominko R, et al. Detection of highly conductive pathways in LiMn₂O₄-carbon black composites for Li ion batteries by microcontact impedance spectroscopy[J]. Solid State Ionics, 2004, 167(3/4): 229-235.
[11] Arumugam D, Kalaignan G P. Synthesis and electrochemical characterizations of nano-SiO₂-coated LiMn₂O₄ cathode materials for rechargeable lithium batteries[J]. Journal of Electroanalytical Chemistry, 2008, 624(1/2)： 197-204.
[12] Liu D Q, Liu X Q, He Z Z. Surface modification by ZnO coating for improving the elevated temperature performance of LiMn₂O₄[J]. Journal of Alloys and Compounds, 2007, 436(1/2): 387-391.
[13] Chung K Y, Ryu C W, Kim K B. Onset mechanism of Jahn-Teller distortion in 4 V LiMn₂O₄ and its suppression by LiM_0.05Mn_1.95O₄ (M = Co, Ni) coating[J]. Journal of The Electrochemical Society, 2005, 152(4): A791-A795.
[14] Zhou D Q(周大桥). Preparation and performance of Co and La Co-doped Li-rich lithium manganate[J]. Journal of Electrochemistry(电化学), 2009, 15(1): 74-78.
[15] He X M, Li J J, Cai Y. Fluorine doping of spherical spinel LiMn₂O₄[J]. Solid State Ionics, 2005, 176(35/36): 2571-2576.
[16] Molenda M, Dziembaj R, Podstawka E. Influence of sulphur substitution on structural and electrical properties of lithium-manganese spinels[J]. Journal of Physics and Chemistry of Solids, 2006, 67(5/6): 1347-1350.
[17] Ye S H, Bo J K, Li C Z, et al. Improvement of the high-rate discharge capability of phosphate-doped spinel LiMn₂O₄ by a hydrothermal method[J]. Electrochimica Acta, 2010, 55(8): 2972-2977.

Al掺杂尖晶石LiMn₂O₄正极材料的性能

Electrochemical Performance of Al-Doped Spinel LiMn₂O₄ Cathode Material for Li-ion Batteries

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	方建军, 杜宇豪, 李子健, 樊文光, 任恒宇, 易浩聪, 赵庆贺, 潘锋. 高电压LiCoO₂的表面结构与性能：回顾与展望[J]. 电化学（中英文）, 2024, 30(6): 2314005-.
[2]	陈露露, 李浩冉, 刘维祎, 王伟. 锂离子电池正极材料原位漫反射光谱电化学研究[J]. 电化学（中英文）, 2024, 30(6): 2314006-.
[3]	丑佳, 王雅慧, 王文鹏, 辛森, 郭玉国. 面向高性能锂-硫二次电池应用的非对称电极-电解质界面[J]. 电化学（中英文）, 2023, 29(9): 2217009-.
[4]	温波, 朱卓, 李福军. 锂-氧气电池：正极催化剂的最新进展与挑战[J]. 电化学（中英文）, 2023, 29(2): 2215001-.
[5]	赵刚, 龚正良, 李益孝, 杨勇. 氧化钨和磷钨酸对LiNi_0.96Co_0.02Mn_0.02O₂材料的表面包覆改性研究[J]. 电化学（中英文）, 2023, 29(10): 2204281-.
[6]	胡炳文, 李超, 耿福山, 沈明. 金属离子电池中的磁共振：从核磁共振(NMR)到电子顺磁共振(EPR)[J]. 电化学（中英文）, 2022, 28(2): 2108421-.
[7]	王加义, 郭胜楠, 王新, 谷林, 苏东. 锂离子电池高镍层状氧化物正极结构失效机制[J]. 电化学（中英文）, 2022, 28(2): 2108431-.
[8]	李西尧, 赵长欣, 李博权, 黄佳琦, 张强. 锂硫电池复合正极研究进展[J]. 电化学（中英文）, 2022, 28(12): 2219013-.
[9]	骆晨旭, 师晨光, 余志远, 黄令, 孙世刚. 富锂锰基层状正极材料的合成及其首周过充下的结构演化[J]. 电化学（中英文）, 2022, 28(1): 2006131-.
[10]	滕久康, 王庆杰, 张亮, 张红梅, 陈晓涛, 张鹏, 赵金保. 热处理时间对锂电池正极材料Cr₈O₂₁的影响[J]. 电化学（中英文）, 2021, 27(6): 689-697.
[11]	王东浩, 晏鹤凤, 龚正良. 复合导电添加剂对全固态锂硫电池性能影响的研究[J]. 电化学（中英文）, 2021, 27(4): 388-395.
[12]	王存, 张维江, 何腾飞, 雷博, 史尤杰, 郑耀东, 罗伟林, 蒋方明. NCA三元锂离子电池分荷电状态循环的热特性和容量衰退研究[J]. 电化学（中英文）, 2020, 26(6): 777-788.
[13]	王璐, 高学平. 基于钴酸锂载体构筑高体积比容量硫基复合材料[J]. 电化学（中英文）, 2020, 26(5): 750-758.
[14]	邵钦君, 陈剑. 锂硫电池硫正极催化转换反应的研究进展[J]. 电化学（中英文）, 2020, 26(5): 694-715.
[15]	王杜丹, 王非, 翟欢欢, 李玉鹏, 杨纳川, 陈康华. 富锂层状正极材料Li₂MnO₃的表面改性及其电化学性能研究[J]. 电化学（中英文）, 2020, 26(2): 289-297.