锰-氮-碳纳米笼限域的高密度铂纳米颗粒用于高耐久重载质子交换膜燃料电池

doi:10.61558/2993-074X.3618

电化学（中英文）

• 研究论文 •

锰-氮-碳纳米笼限域的高密度铂纳米颗粒用于高耐久重载质子交换膜燃料电池

赵磊^#^,^a,b, 曹振明^#^,^c, 左珈瑜^a, 杨明亮^a, 乔红艳^a, 陈俊松^a, 吴睿^a,*

a. 电子科技大学材料与能源学院，四川成都 611731; b. 成都工业学院材料与环境工程学院，四川成都 611730; c. 中自科技股份有限公司氢能研发中心，四川成都 611731.

发布日期:2026-06-11
通讯作者: 吴睿 E-mail:ruiwu0904@uestc.edu.cn

Dense Platinum Nanoparticles Confined in Mn-N-C Nanocages for Robust Heavy-Duty PEMFCs

Lei Zhao^#,^a^,b, Zhenmin Cao^#,c, Jiayu Zuo^a, Mingliang Yang^a, Hongyan Qiao^c, Junsong Chen^a, Rui Wu^a,^*

a. School of Materials and Energy, University of Electronic Science and Technology of China, Chengdu 611731, P. R. China; b. School of Materials and Environmental Engineering, Chengdu Technological University, Chengdu 611730, P. R. China; c. Hydrogen Energy R&D Center, SINOTECH Company Limited, Chengdu 611731, P. R. China.

Online:2026-06-11
Contact: Rui Wu E-mail:ruiwu0904@uestc.edu.cn

摘要/Abstract

摘要： 高负载铂（Pt）阴极催化层是实现重载型质子交换膜燃料电池（PEMFCs）高性能运行的关键，但其长期面临离聚物磺酸基团毒化与Pt纳米颗粒稳定性难以兼顾的矛盾。本文提出一种空间限域策略，通过将高含量Pt纳米颗粒（约51.8 wt%）封装于锰-氮-碳（Mn-N-C）纳米笼中，构筑了具有离聚物屏蔽微环境的Pt-MnNC催化剂。该介孔笼状结构可有效阻隔离聚物进入其内部，显著降低了磺酸基团对Pt活性位点的吸附毒化；同时，Mn–N_x位点与Pt之间的强金属-载体相互作用能够稳定锚定Pt纳米颗粒，抑制其迁移与团聚。在5 × 5 cm²膜电极测试中，Pt-MnNC催化剂在2.0 A·cm^-²电流密度下实现1.26 W·cm^-²的峰值功率密度。经过30000次加速耐久性测试后，其质量活性仅下降20.8%，显著优于商业Pt/C催化剂（衰减61.6%）。研究结果表明，空间限域构筑的离聚物屏蔽微环境能够有效缓解离聚物磺酸基团对Pt的毒化，并协同增强Pt纳米颗粒稳定性，为高功率密度、长寿命重载型PEMFC阴极催化剂的设计提供了新的思路。

关键词: 质子交换膜燃料电池, 介孔碳纳米笼, 磺酸基团毒化, 高载量

Abstract: High-loading Pt cathodes are essential for heavy-duty proton exchange membrane fuel cells (PEMFCs) but suffer from a critical trade-off between ionomer sulfonate poisoning and nanoparticle instability. Herein, we report a spatial confinement strategy to encapsulate dense Pt nanoparticles (~51.8 wt%) within Mn/N-co-doped mesoporous carbon nanocages (denoted as Pt-MnNC). This architecture excludes bulky ionomers to create an ionomer-shielded environment against sulfonate poisoning, while Mn-N_x-mediated strong metal-support interactions anchor the Pt nanoparticles to prevent agglomeration and further boost durability. In 5×5 cm² membrane electrode assembly (MEA) tests, the Pt-MnNC catalyst delivers an exceptional peak power density of 1.26 W·cm^-² at 2.0 A·cm^-². Notably, it exhibits superior durability with only a 20.8% mass activity loss after 30,000 cycles, significantly outperforming commercial Pt/C, which suffers a 61.6% loss. This work provides a robust pathway to decouple ionomer poisoning from catalyst loading, advancing the development of high-power, durable heavy-duty fuel cells.

Key words: Proton exchange membrane fuel cells, Mesoporous carbon nanocages, Sulfonate poisoning, High-loading

赵磊, 曹振明, 左珈瑜, 杨明亮, 乔红艳, 陈俊松, 吴睿. 锰-氮-碳纳米笼限域的高密度铂纳米颗粒用于高耐久重载质子交换膜燃料电池[J]. 电化学（中英文）, doi: 10.61558/2993-074X.3618.

Lei Zhao, Zhenmin Cao, Jiayu Zuo, Mingliang Yang, Hongyan Qiao, Junsong Chen, Rui Wu. Dense Platinum Nanoparticles Confined in Mn-N-C Nanocages for Robust Heavy-Duty PEMFCs[J]. Journal of Electrochemistry, doi: 10.61558/2993-074X.3618.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.3618

[1]	周石, Muhammad Tariq, Asif Nadeem Tabish, Muhammad Salman, 宁凡迪, Muhammad Rayyan Tayyab, 彭冉冉, 郝梦庚, 李文木, 周小春. 制备含有Fe-N-C催化剂的无贵金属阴极催化剂层以提升质子交换膜燃料电池性能[J]. 电化学（中英文）, 2026, 32(4): 2511141-.
[2]	丰紫薇, 陈海忠, 段骁, 唐玲, 赵云昆, 黄龙. 碳载铂镍八面体纳米粒子作为质子交换膜燃料电池阴极催化剂的性能研究[J]. 电化学（中英文）, 2026, 32(1): 2515009-.
[3]	兰畅, 柏景森, 关欣, 王烁, 张楠淑, 程雨晴, 陶金晶, 楚宇逸, 肖梅玲, 刘长鹏, 邢巍. 协同硼掺杂显著提升Co-N-C催化剂的氧还原反应活性[J]. 电化学（中英文）, 2025, 31(9): 2506181-.
[4]	陈浩杰, 唐美华, 陈胜利. 质子交换膜燃料电池阴极催化层疏水性优化[J]. 电化学（中英文）, 2023, 29(9): 2207061-.
[5]	黄龙, 徐海超, 荆碧, 李秋霞, 易伟, 孙世刚. 质子交换膜燃料电池铂基催化剂研究进展[J]. 电化学（中英文）, 2022, 28(1): 2108061-.
[6]	王睿卿, 隋升. PEMFC阴极催化层结构分析[J]. 电化学（中英文）, 2021, 27(6): 595-604.
[7]	魏荣强, 李世安, 刘艺辉, 杨治, 沈秋婉, 杨国刚. 流道与肋宽比对气体扩散层性能影响的数值研究[J]. 电化学（中英文）, 2021, 27(5): 579-585.
[8]	张焰峰, 肖菲, 陈广宇, 邵敏华. 基于非贵金属氧还原催化剂的质子交换膜燃料电池性能[J]. 电化学（中英文）, 2020, 26(4): 563-572.
[9]	杨智, 沈亚云, 周娥, 魏成玲, 秦好丽, 田娟. 前驱体中N含量对FeN/C催化剂氧还原活性的影响研究[J]. 电化学（中英文）, 2020, 26(1): 130-135.
[10]	刘勇, 丁涵, 司德春, 彭杰, 张剑波. 静电纺丝制备质子交换膜燃料电池催化剂层综述[J]. 电化学（中英文）, 2018, 24(6): 639-654.
[11]	郭建伟, 王建龙. 电化学阻抗谱在质子交换膜燃料电池动态的先导应用[J]. 电化学（中英文）, 2018, 24(6): 687-696.
[12]	何大平, 木士春. 质子交换膜燃料电池铂电催化剂稳定策略[J]. 电化学（中英文）, 2018, 24(6): 655-663.
[13]	池滨, 叶跃坤, 江世杰, 廖世军. 低温质子交换膜燃料电池自增湿膜电极研究进展[J]. 电化学（中英文）, 2018, 24(6): 628-638.
[14]	高燕燕，侯明，姜永燚，梁栋，艾军，郑利民. 质子交换膜燃料电池催化层化学稳定性研究[J]. 电化学（中英文）, 2018, 24(3): 227-234.
[15]	肖燕，常英杰，张伟，贾秋红. 启动工况下质子交换膜燃料电池动态性能仿真分析[J]. 电化学（中英文）, 2018, 24(2): 166-173.

锰-氮-碳纳米笼限域的高密度铂纳米颗粒用于高耐久重载质子交换膜燃料电池

Dense Platinum Nanoparticles Confined in Mn-N-C Nanocages for Robust Heavy-Duty PEMFCs

PDF (PC)

评审附件

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics