聚乙烯醇基水凝胶聚合物电解质超级电容器的研究

doi:10.61558/2993-074X.2088

电化学（中英文） ›› 2011, Vol. 17 ›› Issue (2): 190-194. doi: 10.61558/2993-074X.2088

聚乙烯醇基水凝胶聚合物电解质超级电容器的研究

许开卿，范乐庆，吴季怀*，冷晴，钟欣，林建明，黄妙良，兰章

华侨大学材料科学与工程学院，福建泉州 362021

收稿日期:2010-12-04 修回日期:2011-01-10 出版日期:2011-05-28 发布日期:2011-05-06
通讯作者: 吴季怀; Tel: 0595-22693899 E-mail:jhwu@hqu.edu.cn
基金资助:
国家863项目：2009AA03Z217，国家自然科学基金重大研究计划：90922028

Investigation of Supercapacitors Based on Polyvinyl Alcohol Hydrogel-Polymer Electrolyte

XU Kai-qing, FAN Leq-ing, WU Ji-huai*, LENG Qing, ZHONG Xin, LIN Jian-ming, HUANG Miao-liang, LAN Zhang

Academy of Material Science and Engineering, Huaqiao University, Quanzhou 362021, China

Received:2010-12-04 Revised:2011-01-10 Published:2011-05-28 Online:2011-05-06
Contact: WU Ji-huai; Tel: 0595-22693899 E-mail:jhwu@hqu.edu.cn

摘要/Abstract

摘要： 以2-丙烯酰胺基-2-甲基丙磺酸（AMPS）作引发剂引发交联聚乙烯醇（PVA）-戊二醛（GA）制备水凝胶聚合物电解质并组装成超级电容器.分别由红外光谱、交流阻抗、循环伏安与恒电流充放电曲线测定该凝胶聚合物电解质及超级电容器的电化学性能.结果表明，该聚合物电解质电导率可达1.23 mS/cm（室温）.而且，以1.0 g AMPS引发0.05mL GA（5 %）与1.0 g PVA交联，制得的凝胶聚合物电解质超级电容器比电容可达139F/g，50次充放电后其值仍于80%以上.

关键词: 2-丙烯酰胺基-2-甲基丙磺酸（AMPS）, 聚乙烯醇（PVA）, 水凝胶聚合物电解质, 超级电容器

Abstract: For the first time, the supercapacitor based on the hydrogel-polymer electrolyte which consisted of the cross-linking of polyvinyl alcohol-glutaraldehyde (PVA-GA) using 2-acrylamido-2-methyl propane sulfonic acid (AMPS) as solicitation reagent was assembled. The gel polymer electrolyte was characterized by FTIR and AC impedance. The maximum ionic conductivity is 1.23 mS/cm at room temperature. The electrochemical properties of the supercapacitor were investigated by cyclic voltammetry, AC impedance spectra and constant current charge-discharge curve. The results show that the specific capacitance reachs 139 F/g with AMPS of 1.0 g and 0.05 mL of 5 %(by mass) GA. And the specific capacitance still retained above 80% after 50 times of charge-discharge.

Key words: 2-Acrylamido-2-methyl propane sulfonic acid (AMPS), polyvinyl alcohol, hydrogel-polymer electrolyte, supercapacitors

中图分类号:

TM53

许开卿, 范乐庆, 吴季怀, 冷晴, 钟欣, 林建明, 黄妙良, 兰章. 聚乙烯醇基水凝胶聚合物电解质超级电容器的研究[J]. 电化学（中英文）, 2011, 17(2): 190-194.

XU Kai-qing, FAN Leq-ing, WU Ji-huai, LENG Qing, ZHONG Xin, LIN Jian-ming, HUANG Miao-liang, LAN Zhang. Investigation of Supercapacitors Based on Polyvinyl Alcohol Hydrogel-Polymer Electrolyte[J]. Journal of Electrochemistry, 2011, 17(2): 190-194.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2088

https://electrochem.xmu.edu.cn/CN/Y2011/V17/I2/190

参考文献

[1] Zheng J P, Cygan P J, Jow T R. Hydrous ruthenium oxide as an eleetrode material for electrochemical capacitors [J]. J Eleetroehem Soe, 1995, 142(8): 2699-2703.

[2] Tang Zhi-yuan(唐致远), Xu Guo-xiang(徐国祥). Application of electronically conducting polymer in electrochemical capacitors [J]. Chemical Industry and Engineering Progress (化工进展), 2002, 21(9): 652-655.

[3] Kotz R, Carlen M. Principles and applications of electrochemical capacitors [J]. Electrochim Acta, 2000, 45: 2483-2498.

[4] Li Jin-ling(李建玲), Ling JI(梁吉), Xu Jing-ming(徐景明), et al. Progress on the studies on organic electrolytes for electric double-layer capacitor [J]. Chinese Journal of Power Sources (电源技术), 2001, 25(3): 229-234.

[5] Wang Qing-wei(王庆伟), Xie De-min(谢德民). Progress in gel electrolyte [J]. Progress in Chemistry (化学进展), 2002, 14(3): 167-173.

[6] Meng Xiang-li(孟祥利), Yin Jin-ling(殷金玲), Zhang Bao-hong(张宝宏). Investigations on supercapacitors using PAN-based gel polymer electrolytes [J]. Applied Science and Technol- ogy (应用科学技术), 2006, 33(11): 61-65.

[7] Wada H, Yoshikawa K, Nohara S, et al. Electrochemical characteristics of new electric double layer capacitor with acidic polymer hydrogel electrolyte [J]. J Power Sources, 2006, 159(2): 1464-1467.

[8] Choudhury N A, Shukla A K, Sampath S, et al. Cross-linked polymer hydrogel electrolytes for electrochemical capacitors [J]. J Electrochem.Soc, 2006, 153(3): A614-A620.

[9] Choudhury N A, Shukla A K, Sampath S. Hydrogel membrane electrolyte for electro- chemical capacitors [J]. J Chem Sci, 2009, 121(5): 727-734.

[10] Kumar M S, Bhat D K. Polyvinyl alcohol–polystyrene sulphonic acid blend electrolyte for supercapacitor application [J]. Physica B,2009, 404: 1143-1147.

[11] Yu Na(余娜). Study on P(AA/AMPS) and PVA-P(AA/AMPS) intelligent hydrogel [D]. Hua qiao university（华侨大学）, 2007

[12] Wang Yan-li(王艳丽), Yang Hu(杨虎), Xu Zhen-liang(许振良). Effects of chemical cross- linking and heat treatment on polyvinyl alcohol membrane performance [J]. Chemical Engineering (化学工程)，2006, 34(8): 36-39.

[13] Wang Zhan-xu(王展旭), Sun Wei(孙伟), Zhang Ke(张科). Synthesis and properties of AMPS copolymers as filtrate reducer for fixing well [J]. Journal of Qingdao University of Science and Technology (青岛科技大学学报自然科学版). 2004, 25(4): 308-310.

[14] Hong Zhang-chuan(洪璋传). The effect of AMPS’s structure, performance in enhancing the quality of acrylic[J]. Petrochemical Technology in Jinshan (金山油化纤). 2003, 22(4): 6-8.

[1]	叶珍珍, 张抒婷, 陈鑫祺, 王瑾, 金鹰, 崔超婕, 张磊, 钱陆明, 张刚, 骞伟中. 基于离子液体的超级电容在3 V及65 ^oC老化条件下的铝碳界面效应[J]. 电化学（中英文）, 2022, 28(12): 2219005-.
[2]	李丹丹, 纪翔宇, 陈明, 杨燕茹, 王晓东, 冯光. 低聚离子液体的体相与界面及其电化学储能应用[J]. 电化学（中英文）, 2022, 28(11): 2219002-.
[3]	王佳, 黄秋安, 李伟恒, 王娟, 庄全超, 张久俊. 电化学阻抗谱弛豫时间分布基础[J]. 电化学（中英文）, 2020, 26(5): 607-627.
[4]	杨裕生. 电化学储能研究22年回顾[J]. 电化学（中英文）, 2020, 26(4): 443-463.
[5]	周岳珅, 李梦, 吴双, 李照磊, 高延敏. ZnCo₂O₄电极材料的形貌调控制备与超级电容特性的研究[J]. 电化学（中英文）, 2019, 25(6): 740-748.
[6]	张韩方, 魏风, 孙健, 荆梦莹, 何孝军. 离子液体辅助条件下由稻壳合成超级电容器用多孔炭[J]. 电化学（中英文）, 2019, 25(6): 764-772.
[7]	夏永康, 顾明远, 杨红官, 于馨智, 鲁兵安. CVD 法制备三维石墨烯的电化学储能性能[J]. 电化学（中英文）, 2019, 25(1): 89-103.
[8]	苏秀丽, 董晓丽, 刘瑶, 王永刚, 余爱水. 基于钛酸锂负极和聚三苯胺正极的电池电容体系[J]. 电化学（中英文）, 2018, 24(4): 324-331.
[9]	邵雯柯，赵雷，刘超，董艳莹，朱元杰，王秋凡. WO₃/碳布柔性非对称超级电容器的组装及性能研究[J]. 电化学（中英文）, 2018, 24(4): 351-358.
[10]	杨波，金直航，赵亚萍，蔡再生. 自支撑柔性氮掺杂碳织物电极的制备与性能研究[J]. 电化学（中英文）, 2018, 24(4): 359-366.
[11]	荆鑫，张旭，王玮，郎俊伟. 兼具高质量和高体积能量密度的水系全金属氧化物不对称超级电容器[J]. 电化学（中英文）, 2018, 24(4): 332-343.
[12]	周田田，邬冰，邓超，高颖. 锰氧化物聚苯胺复合电极材料的制备与性能[J]. 电化学（中英文）, 2018, 24(2): 137-142.
[13]	张秋红，申保收，左宋林，卫歆雨. 离子液体电解质种类对活性炭电极超级电容器电化学性能的影响[J]. 电化学（中英文）, 2017, 23(6): 684-693.
[14]	林顿，张熙悦，曾银香，于明浩，卢锡洪，童叶翔. 高性能碳基与过渡金属化合物基超级电容器电极材料的研究进展[J]. 电化学（中英文）, 2017, 23(5): 560-580.
[15]	赵井文，李佳佳，韩鹏献，崔光磊. 水系锌离子电容器[J]. 电化学（中英文）, 2017, 23(5): 581-585.

聚乙烯醇基水凝胶聚合物电解质超级电容器的研究

Investigation of Supercapacitors Based on Polyvinyl Alcohol Hydrogel-Polymer Electrolyte

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics