双核双金属酞菁(FeCoPc_2)阴极催化直接硼氢化物燃料电池

马金福;刘艳;赖俊华;柳永宁;

西安交通大学金属强度国家重点实验室;

收稿日期:2009-08-28 修回日期:2009-08-28 出版日期:2009-08-28 发布日期:2009-08-28

A Direct Borohydride Fuel Cell with FeCoPc_2-Catalysed Cathode

MA Jin-fu,LIU Yan,LAI Jun-hua,LIU Yong-ning

(State Key Laboratory for Mechanical Behavior of Materials,Xi'an Jiaotong University,Xi'an 710049,China

Received:2009-08-28 Revised:2009-08-28 Published:2009-08-28 Online:2009-08-28

摘要/Abstract

摘要： 研制一种无膜型直接硼氢化物燃料电池(DBFC).循环伏安测试发现FeCoPc2在碱性溶液中对氧还原具有催化作用.稳态极化曲线表明,由于FeCoPc2结构具有较强的共轭效应以及Fe、Co在催化中的协同作用使它比FePc、CoPc具有更强的氧还原能力,并获得了110mW/cm2的功率密度.恒电流放电测试表明该燃料电池性能具有良好的稳定性.

关键词: 燃料电池, 硼氢化物, 金属酞菁配合物

Abstract: In this paper,a membraneless direct borohydride fuel cell was investigated. Cyclic voltammograms of FeCoPc2-modified glassy carbon electrode in the alkaline solution show that FeCoPc2 was active for oxygen reduction reaction. In addition,the steady-state polarization curve tests indicate that FeCoPc2 had better activity than FePc,CoPc or FePc+CoPc,which is due to its conjugated effect and synergistic effect of Fe and Co. Finally,a maximum power density of 110 mW/cm2 was attained,and the 25-day life test shows that the direct borohydride fuel cell had a good stability.

Key words: fuel cell, borohydride, metal phthalocyanine

中图分类号:

TM911.4

马金福, 刘艳, 赖俊华, 柳永宁, . 双核双金属酞菁(FeCoPc_2)阴极催化直接硼氢化物燃料电池[J]. 电化学（中英文）, 2009, 15(3): 280-283.

MA Jin-fu, LIU Yan, LAI Jun-hua, LIU Yong-ning. A Direct Borohydride Fuel Cell with FeCoPc_2-Catalysed Cathode[J]. Journal of Electrochemistry, 2009, 15(3): 280-283.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.1995

https://electrochem.xmu.edu.cn/CN/Y2009/V15/I3/280

参考文献

[1]Wee J H.Which type of fuel cell is more competitive for portable application:Direct methanol fuel cells or direct borohydride fuel cells?[J].J Power Sources,2006,161(1):1-10. [2]Amendola S C,Onnerud P,Michael T,et al.A novel high power density borohydride-air cell[J].J Power Sources,1999,84(1):130-133. [3]De Leon C P,Walsh F C,Pletcher D,et al.Direct borohydride fuel cells[J].J Power Sources,2006,155(2):172-181. [4]Li Z P,Liu B H,Arai K,et al.Development of the di-rect borohydride fuel cell[J].J Alloys Compounds,2005,404:648-652. [5]Chatenet M,Micoud F,Roche I,et al.Kinetics of so-dium borohydride direct oxidation and oxygen reduction in sodium hydroxide electrolyte-Part I.BH4-electro-ox-idation on Au and Ag catalysts[J].Electrochim Acta,2006,51(25):5459-5467. [6]Feng R X,Dong H,Wang Y D,et al.A simple and high efficient direct borohydride fuel cell with MnO2-catalyzed cathode[J].Electrochem Commun,2005,7(4):449-452. [7]Martins J I,Nunes MC,Koch R,et al.Electrochemi-cal oxidation of borohydride on platinum electrodes:The influence of thiourea in direct fuel cells[J].Electro-chim Acta,2007,52(23):6443-6449. [8]Wang Y G,Xia Y Y.A direct borohydride fuel cell u-sing MnO2-catalyzed cathode and hydrogen storage alloy anode[J].Electrochem Commun,2006,8(11):1775-1778. [9]Verma A,Jha A K,Basu S.Manganese dioxide as a cathode catalyst for a direct alcohol or sodium boro-hydride fuel cell with a flowing alkaline electrolyte[J].J Power Sources,2005,141(1):30-34. [10]Cheng H,Scott K,Lovell K.Material aspects of the design and operation of direct borohydride fuel cells[J].Fuel Cells,2006,6(5):367-375. [11]Ma J F,Liu Y N,Zhang P,et al.A simple direct borohydride fuel cell with a cobalt phthalocyanine cata-lyzed cathode[J].Electrochem Commun,2008,10:100-102. [12]Ma J F,Liu Y N,Wang J.Iron phthalocyanine as a cathode catalyst for a direct borohydride fuel cell[J].J Power Sources,2007,172:220-224. [13]Li X P(李雪萍),Yu D Y(丁大勇),Han X X(韩晓祥),et al.Liquid oxidation of styrene catalyzed by metal phthalocyanines[J].J Petrochemical Universi-ties,1998,11(4):21-24. [14]Wang J(王瑾),Ma J F(马金福),Liu Y N(柳永宁).Electrocatalytic abilities of AB(5)-type hydrogen storage alloy as anode materials of DBAFC[J].Rare Metal Mat Eng,2008,37(8):1483-1486.

[1]	陈浩杰, 唐美华, 陈胜利. 质子交换膜燃料电池阴极催化层疏水性优化[J]. 电化学（中英文）, 2023, 29(9): 2207061-.
[2]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[3]	韦宗楠, 曹敏纳, 曹荣. 瓜环基金属纳米催化剂的电化学研究进展[J]. 电化学（中英文）, 2023, 29(1): 2215008-.
[4]	黄龙, 徐海超, 荆碧, 李秋霞, 易伟, 孙世刚. 质子交换膜燃料电池铂基催化剂研究进展[J]. 电化学（中英文）, 2022, 28(1): 2108061-.
[5]	王睿卿, 隋升. PEMFC阴极催化层结构分析[J]. 电化学（中英文）, 2021, 27(6): 595-604.
[6]	朱从懿, 李笑晖, 甘全全. 乙二醇基冷却液污染对质子交换膜燃料电池电堆的影响及恢复措施[J]. 电化学（中英文）, 2021, 27(6): 698-704.
[7]	魏荣强, 李世安, 刘艺辉, 杨治, 沈秋婉, 杨国刚. 流道与肋宽比对气体扩散层性能影响的数值研究[J]. 电化学（中英文）, 2021, 27(5): 579-585.
[8]	吴志鹏, 钟传建. 钯基氧还原和乙醇氧化反应电催化剂:关于结构和机理研究的一些近期见解[J]. 电化学（中英文）, 2021, 27(2): 144-156.
[9]	庄志华, 陈卫. 原子数精确的金属纳米团簇在电催化领域的应用研究进展[J]. 电化学（中英文）, 2021, 27(2): 125-143.
[10]	胡守训, 李亮, 杨俊豪, 李刘强, 靳志豪. 金属钯插层类水滑石的制备及其电催化乙醇的性能研究[J]. 电化学（中英文）, 2021, 27(1): 100-107.
[11]	俞成荣, 朱建国, 蒋聪盈, 谷宇晨, 周晔欣, 李卓斌, 邬荣敏, 仲政, 官万兵. 基于电-化-热耦合理论对称双阴极固体氧化物燃料电池堆的电流与温度场数值模拟[J]. 电化学（中英文）, 2020, 26(6): 789-796.
[12]	王佳, 黄秋安, 李伟恒, 王娟, 庄全超, 张久俊. 电化学阻抗谱弛豫时间分布基础[J]. 电化学（中英文）, 2020, 26(5): 607-627.
[13]	李启浩, 王英明, 马华隆, 肖丽, 王功伟, 陆君涛, 庄林. 碱性膜燃料电池阳极碳酸化模型研究[J]. 电化学（中英文）, 2020, 26(5): 731-739.
[14]	张焰峰, 肖菲, 陈广宇, 邵敏华. 基于非贵金属氧还原催化剂的质子交换膜燃料电池性能[J]. 电化学（中英文）, 2020, 26(4): 563-572.
[15]	徐明俊, 刘杰, 葛君杰, 刘长鹏, 邢巍. 长春应化所金属氮碳氧还原催化剂的研究进展[J]. 电化学（中英文）, 2020, 26(4): 464-473.

双核双金属酞菁(FeCoPc_2)阴极催化直接硼氢化物燃料电池

A Direct Borohydride Fuel Cell with FeCoPc_2-Catalysed Cathode

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics