O-掺杂石墨电极VO2+/VO2+电对反应活性研究

doi:10.61558/2993-074X.2944

电化学（中英文） ›› 2013, Vol. 19 ›› Issue (2): 120-124. doi: 10.61558/2993-074X.2944

O-掺杂石墨电极VO²⁺/VO₂⁺电对反应活性研究

张焕, 秦琳琳, 施一宁, 郑明森, 董全峰^*, 田昭武^*

厦门大学固体表面物理化学国家重点实验室，化学化工学院化学系，福建厦门 361005

收稿日期:2012-04-30 修回日期:2012-05-10 出版日期:2013-04-28 发布日期:2012-05-15
通讯作者: 董全峰, 田昭武 E-mail:qfdong@xmu.edu.cn, zwtian@xmu.edu.cn
基金资助:
国家自然科学基金项目(No. 200933005, No. 20903077)和国家973计划项目（No. 2009CB220102）资助

Electrochemical Activities of Oxygen-Doped Carbon Surface for V(IV)/V(V) Redox Couple

ZHANG Huan, QIN Lin-Lin, SHI Yi-Ning, ZHENG Ming-Sen, DONG Quan-Feng^*, TIAN Zhao-Wu^*

State Key Lab of Physical Chemistry of Solid Surfaces, Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, Fujian, China

Received:2012-04-30 Revised:2012-05-10 Published:2013-04-28 Online:2012-05-15
Contact: DONG Quan-Feng, TIAN Zhao-Wu E-mail:qfdong@xmu.edu.cn, zwtian@xmu.edu.cn

摘要/Abstract

摘要： 采用氧气等离子体处理石墨电极表面，实现氧及含氧官能团的掺杂，以改善VO²⁺/VO₂⁺电对的反应活性. FT-IR和EDS测试结果表明，氧气等离子体处理石墨表面引入了含氧官能团，从而提高了VO²⁺/VO₂⁺电对的电化学活性. 在本文实验条件下20 min等离子体处理的电极活性最好，8 mA cm^-2电流密度恒流充放电，石墨电极VO2+/VO2+电对库仑效率达到91%，比未处理电极的库仑效率提高了19%.

关键词: 全钒电池正极, 氧气等离子体, 电化学活性

Abstract: Graphite plate electrodes were treated with oxygen plasma and doped with oxygen as well as oxygen functional groups. With the treatment, the activities of graphite plate electrodes toward VO²⁺/VO₂⁺ redox reactions were improved. FT-IR and EDS analysis results indicated that oxygen functional groups were introduced to the surface of graphite plates after oxygen plasma treatment. In this paper, the graphite plate treated for 20 min showed the highest activity. The average charge efficiency reached 91%, suggesting an increase of 19%, compared with that of the untreated graphite plate under a current density of 8 mA·cm^-2.

Key words: positive electrode of all-vanadium, oxygen plasma, electrochemical activity

中图分类号:

O646
TM912.9

张焕, 秦琳琳, 施一宁, 郑明森, 董全峰, 田昭武. O-掺杂石墨电极VO²⁺/VO₂⁺电对反应活性研究[J]. 电化学（中英文）, 2013, 19(2): 120-124.

ZHANG Huan, QIN Lin-Lin, SHI Yi-Ning, ZHENG Ming-Sen, DONG Quan-Feng, TIAN Zhao-Wu. Electrochemical Activities of Oxygen-Doped Carbon Surface for V(IV)/V(V) Redox Couple[J]. Journal of Electrochemistry, 2013, 19(2): 120-124.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2944

https://electrochem.xmu.edu.cn/CN/Y2013/V19/I2/120

参考文献

[1] Shao Y, Wang X, Engelhard M, et al. Nitrogen-doped mesoporous carbon for energy storage in vanadium redox flow batteries[J]. Journal of Power Sources, 2010, 195(13): 4375-4379.
[2] Zhu H, Zhang Y, Yue L, et al. Graphite-carbon nanotube composite electrodes for all vanadium redox flow battery[J]. Journal of Power Sources, 2008, 184(2): 637-640.
[3] Wang W H, Wang X D. Investigation of Ir-modified carbon felt as the positive electrode of an all-vanadium redox flow battery[J]. Electrochimica Acta, 2007, 52(24): 6755-6762.
[4] Sun B, Skyllas-Kazacos M. Chemical modification of graphite electrode materials for vanadium redox flow battery application—part II. Acid treatments[J]. Electrochimica Acta, 1992, 37(13): 2459-65.
[5] Sun B, Skyllas-Kazacos M. Modification of graphite electrode materials for vanadium redox flow battery application—I. Thermal treatment[J]. Electrochimica Acta, 1992, 37(7): 1253-1260.
[6] Yue L, Li W, Sun F, et al. Highly hydroxylated carbon fibres as electrode materials of all-vanadium redox flow battery[J]. Carbon, 2010, 48(11): 3079-3090.
[7] Han P, Wang H, Liu Z, et al. Graphene oxide nanoplatelets as excellent electrochemical active materials for VO2+/VO2+ and V2+/V3+ redox couples for a vanadium redox battery[J]. Carbon, 2011, 49(2): 693-700.
[8] Ago H, Kugler T, Cacialli F, et al. Work functions and surface functional groups of multiwall carbon nanotubes[J]. The Journal of Physical Chemistry B, 1999, 103(38): 8116-8121.
[9] Honda K, Rao T N, Tryk D, et al. Electrochemical characterization of the nanoporous honeycomb diamond electrode as an electrical double-layer capacitor[J]. Journal Electrochemical Society, 2000, 147(2): 659-664.
[10] Bismarck A, Kumru M E, Springer J. Influence of oxygen plasma treatment of PAN-based carbon fibers on their electrokinetic and wetting properties[J]. Journal of Colloid and Interface Science, 1999, 210(1): 60-72.
[11] Okajima K, Ohta K, Sudoh M. Capacitance behavior of activated carbon fibers with oxygen-plasma treatment[J]. Electrochimica Acta, 2005, 50(11): 2227-22231.
[12] Park J M, Kim D S, Kim S R. Improvement of interfacial adhesion and nondestructive damage evaluation for plasma-treated PBO and Kevlar fibers/epoxy composites using micromechanical techniques and surface wet ability[J]. Journal of Colloid and Interface Science, 2003, 264(2): 431-445.
[13] Wu G. Oxygen plasma treatment of high performance fibers for composites[J]. Materials Chemistry and Physics, 2004, 85(1): 81-87.

O-掺杂石墨电极VO²⁺/VO₂⁺电对反应活性研究

Electrochemical Activities of Oxygen-Doped Carbon Surface for V(IV)/V(V) Redox Couple

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 9

Metrics

[1]	崔爱林, 白洋, 俞宏英, 孟惠民. Pt/TiO₂-CN_x催化剂中纳米TiO₂ (A)/(R)相含量的电催化“火山形”效应[J]. 电化学（中英文）, 2022, 28(5): 2110021-.
[2]	吉维肖, 王功伟, 王强, 白力军, 屈德扬. 多孔电极在电化学体系中的应用[J]. 电化学（中英文）, 2020, 26(5): 576-595.
[3]	杨防祖, 陈明辉, 黄夏菁, 田中群, 周绍民, . 无铅镉化学镍沉积及其表征[J]. 电化学（中英文）, 2010, 16(4): 430-435.
[4]	杨国锋, 贾能勤, 王志勇, . 碳纳米管尺寸对电化学反应活性的影响[J]. 电化学（中英文）, 2007, 13(1): 63-66.
[5]	王廷勇,许立坤,陈光章. 混合金属氧化物阳极在海水中的电化学性能[J]. 电化学（中英文）, 2002, 8(2): 172-176.
[6]	颜流水,魏洽,王承宜,史蓉蓉,马晓通. 电聚吡咯固定化酪氨酸酶电极的制备及性能[J]. 电化学（中英文）, 2000, 6(2): 222-226.
[7]	王廷勇, 许立坤, 陈光章. 铱钽钛金属氧化物阳极的电化学特性[J]. 电化学（中英文）, 2000, 6(1): 72-77.
[8]	刘玲,夏熙. 纳米电极材料的制备及其电化学性质研究(Ⅲ)——微乳液中通氧气制备MnO_2及其性能[J]. 电化学（中英文）, 1998, 4(3): 328-333.
[9]	罗瑾,吴玲玲,黄少华,林仲华. 细胞色素c在经预处理的金电极上电化学行为的研究[J]. 电化学（中英文）, 1996, 2(4): 385-385.