天然海水中绿色碳钢缓蚀剂的研究

电化学（中英文） ›› 2003, Vol. 9 ›› Issue (4): 416-421.

天然海水中绿色碳钢缓蚀剂的研究

公平,杜敏,王庆璋,穆振军

中国海洋大学化学化工学院,中国海洋大学化学化工学院,中国海洋大学化学化工学院,中国海洋大学化学化工学院山东青岛266003 ,山东青岛266003 ,山东青岛266003 ,山东青岛266003

收稿日期:2003-11-28 修回日期:2003-11-28 出版日期:2003-11-28 发布日期:2003-11-28

The Study of Green Corrosion Inhibitors for Mild Steel 907 in Natural Seawater Environment

GONG Ping,DU Min*,WANG Qing_zhang,MU Zhen_jun

(College of Chemistry and Chemical Engineering Ocean University of China, Qingdao 266003,China)

Received:2003-11-28 Revised:2003-11-28 Published:2003-11-28 Online:2003-11-28

摘要/Abstract

摘要： 　根据分子设计和官能团剪裁方法,结合有机缓蚀剂分子在金属表面和氧化膜表面的配位理论,选择葡萄酸钙,葡萄糖酸锌,硫酸锌,蒜素,丙烯酸聚合物,椰子油基烷醇酰胺,APG,OCTA,多聚磷酸钠等多种缓蚀剂成分,利用极化曲线法和重量法研究了上述缓蚀剂复配后对海水中碳钢的缓蚀作用,并由正交实验对筛选出的葡萄酸钙,硫酸锌和OCTA研究确定其以及相互之间的最佳复配比和协同效应,然后通过分段实验法再研究其最佳配方的后效能性,从而得到一种可生物降解的无磷高效绿色缓蚀剂.

关键词: 碳钢, 缓蚀剂, 绿色, 海水

Abstract: Nine green compounds,including calcium gluconate,zinc gluconate,zinc sulfate,garlic,ACUSOL 445N,OS_15,APG,OCTA and STPP were selected according to the methods of molecule design and function groups prune. The functions of combined corrosion inhibitors mixed by the compounds mentioned above for mild steel in seawater were studied in this work using the methods of polarization curve and weight_loss.The best weight ratio and distinct synergistic effect of calcium gluconate,zinc sulfate and OCTA were studied by Latin experiment. The afgereffects of the best weight ratio corrosoin inhibitor were studied by subsection experiment. In this way, a kind of high effect green corrosion inhibitor was obtained.

中图分类号:

TG174.42

公平, 杜敏, 王庆璋, 穆振军. 天然海水中绿色碳钢缓蚀剂的研究[J]. 电化学（中英文）, 2003, 9(4): 416-421.

GONG Ping, DU Min, WANG Qing_zhang, MU Zhen_jun. The Study of Green Corrosion Inhibitors for Mild Steel 907 in Natural Seawater Environment[J]. Journal of Electrochemistry, 2003, 9(4): 416-421.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2003/V9/I4/416

参考文献

[1]　ZhengJia＿sheng,HuangKui＿yuan.Reviewandprospectofcorrosioninhibitordevelopment[J].MaterialsProtection,2000,33(5):11～15. [2]　WeiGang,XiongRong＿chun.Greenchemistryandperspectivesoncorrosionprotection[J].CorrosionScienceandProtectionTechnology,2001,13(1):346. [3]　XuShou＿chang.TheTechnologyofIndustrialWaterDisposal[M].Beijing:ChemicalIndustryPress,1984:272～275. [4]　MorED,WrublW.Zincgluconateasaninhibitorofthecorrosionofmildsteelinseawater[J].Br.Corros.,1976,11(4):199～203. [5]　YangZhao＿hui,WangQing＿zhang.Studiesoncorrosioninhibitorsofmildsteelinseawater[J].MarineScience,1998,(1):62～64. [6]　GaoYan＿min,ChenJia＿jian,LeiLiang＿cai,etal.Adsorptionoforganicmoleculeonmetalsurfaceandmoleculardesignoforganicinhibitors[J].JournalofChineseSocietyforCorrosionandProtection,2000,20(3):141～148. [7]　ChenShang＿bing,WangJing＿yun.Structuralanalysisoflauroy＿typecorrosioninhibitorssystemanditseffectevaluation[J].JournalofJianghanPetroleumInstitute,1996,18(9):26～29. [8]　FeiXiu＿zhong,ZhangYong＿guang,LiYong＿chang.ThesynthesisandevaluationofthenovelsurfactantAPG[J].JournalofChinaInstituteofMetallurgy,1996,13(2):23～25. [9]　Latha,RajeswariG.Evalutionofnon＿ionicsurfactantascorrosioninhibitorsinseawater[J].Anti＿CorrosionMethodsMater.,1996,43(5):19～23. [10]　ShalabyMN,OsmanMM,ElFekyAA.Effectofsomeorganicsurfactantsoncorrosioninhibitionofsteelinseawater[J].Anti＿CorrosionMethodsandMaterials,1999,46(4):254～260. [11]　KrastVH,KadekS,TrusovN,etal.Thedevelopment,applicationandmechanismofcorrosioninhibitorsinneutralwaterenvironment[D].ThePapersCollectionofthe12thInternationalCorrosionConference,PetroleumIndustryPublishingCompany,1993. [12]　CuiWei＿han,TangMeng＿qi,XuChun＿chun.TheWholePracticalTechnologyofChineseAnti＿CorrosionEngineers[M].Taiyuan:ShanxiScienceandTechnologyPress,2001.

[1]	王小丽, 何为, 陈先明, 曾红, 苏元章, 王翀, 李高升, 黄本霞, 冯磊, 黄高, 陈苑明. PCB酸性蚀刻液中缓蚀剂对厚铜线路制作的影响[J]. 电化学（中英文）, 2022, 28(7): 2213007-.
[2]	戴昭霞, 郑大江, 宋光铃, 冯丹青, 苏培. 不同电位下极化后的纯钛表面生物污损行为[J]. 电化学（中英文）, 2022, 28(5): 2109061-.
[3]	张涛, 刘一蒲, 叶齐通, 范红金. 工业级碱性海水电解:近期进展和展望[J]. 电化学（中英文）, 2022, 28(10): 2214006-.
[4]	涂扬帆，冯立明，方志刚，刘海涛，井明华，管勇. 海水环境中典型阴离子对5083铝合金腐蚀行为的影响[J]. 电化学（中英文）, 2017, 23(4): 466-472.
[5]	钱朋，毕美香，王玉康，查正根，汪志勇. 电化学条件下α-C—H键的官能团化的研究进展[J]. 电化学（中英文）, 2017, 23(3): 262-275.
[6]	张小娟, 王静静, 董士刚, 林昌健. 锌铝层状双金属氢氧化物焙烧物对钢筋的缓蚀作用研究[J]. 电化学（中英文）, 2013, 19(3): 256-265.
[7]	张哲, 贾明子, 阮乐. 铁表面银纳米粒子自组装膜及其缓蚀性能的研究[J]. 电化学（中英文）, 2012, 18(1): 89-93.
[8]	徐海波, 芦永红, 张伟, 于砚廷, 严川伟, 孙亚萍, 钟莲, 刘建国, 郑轶, 韩冰, 王永良. 海水超级电容溶解氧电池[J]. 电化学（中英文）, 2012, 18(1): 24-30.
[9]	徐群杰, 李春香, 倪钰宏, 周国定, . 3-氨基-1,2,4-三氮唑和Na_2WO_4复合缓蚀剂对黄铜的缓蚀协同作用[J]. 电化学（中英文）, 2009, 15(2): 190-193.
[10]	胡骞, 邱于兵, 郭兴蓬, . Q235碳钢缝隙腐蚀的电化学噪声研究[J]. 电化学（中英文）, 2009, 15(2): 184-189.
[11]	董俊华, 柯伟, . 低碳钢大气腐蚀室内模拟加速腐蚀试验与锈蚀规律[J]. 电化学（中英文）, 2009, 15(2): 170-178.
[12]	唐益, 许立坤, 辛永磊, 王均涛, 龙萍, . 嵌中间层金属氧化物电极[J]. 电化学（中英文）, 2009, 15(2): 146-151.
[13]	王天德, 王荣, 吴霞琴, 郭志钢, 季魏魏, . 锆离子改善十烷基磷酸组装膜结构及性能研究[J]. 电化学（中英文）, 2008, 14(2): 175-179.
[14]	程明焱, 吴伟明, 刘鹤鸣, 杜海燕, . 氨基酸缓蚀剂在盐酸溶液中对钢的缓蚀作用[J]. 电化学（中英文）, 2008, 14(2): 200-204.
[15]	赵景茂, 刘鹤霞, 肖超, 陆原, . 咪唑啉衍生物在H_2S水溶液中的腐蚀抑制机理(英文)[J]. 电化学（中英文）, 2008, 14(1): 18-23.