温度对空间用氢镍电池电化学性能的影响

doi:10.13208/j.electrochem.150720

电化学（中英文） ›› 2016, Vol. 22 ›› Issue (1): 49-56. doi: 10.13208/j.electrochem.150720

温度对空间用氢镍电池电化学性能的影响

张海昌*，刁玉琦，明文成，任学颖，丁飞

中国电子科技集团公司第十八研究所，化学与物理电源重点实验室，天津 300384

收稿日期:2015-07-20 修回日期:2015-11-09 出版日期:2016-02-29 发布日期:2015-11-11
通讯作者: 张海昌 E-mail:hchzhang@126.com
作者简介:张海昌

Temperature Effects on Properties of Aerospace Nickel Hydrogen Cells

ZHANG Hai-chang*, DIAO Yu-qi, MING Wen-cheng, REN Xue-ying, DING Fei

National Key Laboratory of Power source, Tianjin Institute of Power Source, Tianjin 300384, China

Received:2015-07-20 Revised:2015-11-09 Published:2016-02-29 Online:2015-11-11
Contact: ZHANG Hai-chang E-mail:hchzhang@126.com
About author:ZHANG Hai-chang

摘要/Abstract

摘要：

以60 Ah氢镍电池为研究对象，研究了温度对电池电性能的影响. 结果表明，电池的放电容量、过充电率随着温度均呈先升后降趋势，最高放电容量可达63.68 Ah（-5 ^oC），电池的适合涓流值及3天自放电率随着温度的升高呈增加趋势，电池的放电容量、过充电率、适合涓流值和自放电率与环境温度之间有近似的代数公式变化关系. -10 ^oC、80%放电深度（DOD）条件下循环3000次后，电池电性能无明显衰降；25 ^oC下循环550次，放电电压跌至0.8 V，电池失效. 结合相关参考文献结果及EIS试验分析可知，25 ^oC下电池循环性能迅速失效主要是由于高温下镍电极更易析氧和发生极板腐蚀，以及高温下镍极板更易粉化所致.

关键词: 空间氢镍电池, 温度, 电性能

Abstract:

This has been done using the 60 Ah nickel-hydrogen cell to investigate the temperature effects on properties of aerospace nickel hydrogen cells. The charge-discharge, trickle charge, overcharge, self-discharge and cycle life tests were carried out at different temperatures. The results show that the discharge capacity and overcharge rate were increased first, and then decreased with the raising temperature. On the other hand, the trickle charge value and the 3 days self-discharge rate were raised with increasing temperature. When the temperature was -5 ^oC, the discharge capacity of cell reached the maximum discharge capacity of 63.68 Ah. Based on the test results, the approximate functions among the discharge capacity, trickle charge rate, overcharge rate, self-discharge rate and temperature can be described. The battery lifetime results at 80% DOD and -15 ^oC indicate no apparent battery deterioration even after 3000 cycles. When the lifetime operating at 80% DOD and 25 ^oC, the cut-off voltage for end discharge of the cell dropped to 0.8 V and the battery failed. Based on the related references and EIS results, it was concluded that the temperature increase resulted in oxygen electrode potential drop, and the early start of oxygen evolution at charge and nickel plate pulverized, which markedly speeds up the cell performance degradation at life cycling.

Key words: aerospace nickel hydrogen cell, temperature, electrochemical property

中图分类号:

TM911
O646

张海昌*，刁玉琦，明文成，任学颖，丁飞. 温度对空间用氢镍电池电化学性能的影响[J]. 电化学（中英文）, 2016, 22(1): 49-56.

ZHANG Hai-chang*, DIAO Yu-qi, MING Wen-cheng, REN Xue-ying, DING Fei. Temperature Effects on Properties of Aerospace Nickel Hydrogen Cells[J]. Journal of Electrochemistry, 2016, 22(1): 49-56.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.150720

https://electrochem.xmu.edu.cn/CN/Y2016/V22/I1/49

参考文献

[1] Thaller L H, Zimmerman A H. Overview of the design, development, and application of nickel-hydrogen batteries[M]. California,NASA Center for AeroSpace Information, 2003:12-13.

[2] Goddard space flight center. Ni-H₂ spacecraft battery handing and storage practice. NASA preferred reliability practices[M]. Practice No. PD-ED-1109.

[3] Zimmerman A H. Low-temperature failure mode for nickel-hydrogen cells[M]. National Technical Information Service (NTIS). Aerospace Report No. TR-2005(8555)-5.

[4] Barnard R, Randell C F, Tye F L. Studies concerning charged nickel hydroxide electrodes I. Measurement of reversible potentials[J]. Journal of Applied Electrochemistry, 1980, 10(1): 109-125.

[5] Corringan D A, Kinigh S L. Electrochemical and spectroscopic evidence on the participation of quadrivalent nickel in the nickel hydroxide redox reaction[J]. Journal of the Electrochemical Society, 1989, 136(3): 613-619.

[6] Faure C, Delmas C, Fouassier M. Characterization of a turbostratic α-nickel hydroxide quantitatively obtained from an NiSO₄ solution[J]. Journal of Power Sources, 1991, 35(3): 279-290.

[7] Sac-Epee N, Palacin M R, Beaudoi B, et al. On the origin of the second low-voltage plateau in secondary alkaline batteries with nickel hydroxide positive electrodes[J]. Journal of the Electrochemical Society, 1997, 144(11): 3896-3907.

[8] Thaller L H, Zimmeran A H, To G A. Understanding the impact of electrolyte and cobalt additive concentrations on the performance of nickel-hydrogen cells[M]. The 2002 NASA Aerospace battery workshop.

[9] Quinzio M V, Zimmeran A H. Dynamic calorimetry for thermal characterization of battery cells[M]. Batteru conference on applications and advances, 2002: 279-284.

[10] Vaidyanathan H, Rao G M. Electrode properties and heat generation rate in Ni-Cd, Ni-H₂, and Ni-MH cells[M]. IECEC, 1997, 1: 83-86.

[11] Chen X L(陈晓玲), Chen F (陈飞), Yang L (杨立), et al. The stack thermal modeling of an individual pressure vessel (IPV) Ni-H₂ battery[J]. Journal of Shanghai Jiaotong University (上海交通大学学报), 2006, 40(12): 2097-2100.

[12] Du H(杜红), Liu Z(刘震), Cao J(曹俊), et al. Research of life and control technology of in-orbit charging of nickel-hydrogen batteries[J]. Spacecraft engineering (航天器工程), 2011, 20(1): 88-94.

[13] Kondratyev D G, Golin Y L, Matryonin V I, et al. Investigation of the causes of nickel-hydrogen battery performance decrease in the process of long life tests[M]. IEEE, 1999: 625-629.

[14] Oshitani M, Takayama T, Takashima K, et al. A study on the swelling of a sintered nickel hydroxide electrode[J]. Journal of Applied Electrochemistry, 1986, 16(3): 403-412.

[15] Delmas C, Faure C, Borthomieu Y. The effect of cobalt on the chemical and electrochemical behaviour of the nickel hydroxide electrode[J]. Materials Science and Engineering: B, 1992, 13(2): 89-96.

[16] Bode H, Dehmelt K, Witte J. Zur kenntnis der nickelhydroxidelektrode—I.Über das nickel(Ⅱ)-hydroxidhydrat[J]. Electrochimica Acta, 1966, 11(8): 1079-1087

温度对空间用氢镍电池电化学性能的影响

Temperature Effects on Properties of Aerospace Nickel Hydrogen Cells

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	李炬, 杨森, 孙建军. 电加热微电极传热模式的结构依赖性研究[J]. 电化学（中英文）, 2023, 29(9): 2203211-.
[2]	张泽阳, 孙岚, 林昌健. RGO-TiO₂纳米管阵列的制备及其光电性能[J]. 电化学（中英文）, 2020, 26(6): 844-849.
[3]	徐坤, 周开岭, 汪浩, 刘晶冰, 严辉. 聚苯胺电致变色薄膜在不同颜色区间的电化学循环稳定性研究[J]. 电化学（中英文）, 2019, 25(6): 690-698.
[4]	肖燕，常英杰，张伟，贾秋红. 启动工况下质子交换膜燃料电池动态性能仿真分析[J]. 电化学（中英文）, 2018, 24(2): 166-173.
[5]	王磊, 薛娟琴, 于丽花, 唐长斌, 毕强. 温度对PbO₂电沉积形核生长过程的影响研究[J]. 电化学（中英文）, 2017, 23(4): 480-488.
[6]	白莉, 怀永建, 艾新平, 贾海. 具有热关断涂层的锂电池隔膜性能表征[J]. 电化学（中英文）, 2015, 21(5): 459-464.
[7]	张永龙，胡学步*，王耀琼，黄东海. 锂离子电池负极材料Li₄Ti₅O₁₂的合成及性能研究[J]. 电化学（中英文）, 2015, 21(2): 181-186.
[8]	张笑，钟赟鑫，颜佳伟，毛秉伟. Au(111)-离子液体界面层状结构与温度关联的原位AFM力曲线研究[J]. 电化学（中英文）, 2014, 20(4): 295-301.
[9]	赵思臣*，王奔，贾秋红，韩明，谢玉洪. 自增湿阴极开放式PEMFC的温度调控[J]. 电化学（中英文）, 2014, 20(2): 184-188.
[10]	崔聪颖, 马学美, 孔德龙, 马厚义. α型和β型PbO₂正极的充放电性能的比较[J]. 电化学（中英文）, 2013, 19(1): 43-52.
[11]	窦衍叶, 晏南富, 李国然, 高学平. 碳纳米管负载Ni₂P作为染料敏化太阳能电池对电极的性能研究[J]. 电化学（中英文）, 2012, 18(4): 301-305.
[12]	张海昌, 檀立新, 呙成, 明文成, 任学颖. 电化学浸渍法制备空间氢镍电池用镍电极的循环寿命研究[J]. 电化学（中英文）, 2012, 18(1): 84-88.
[13]	汤儆, 杜琳, 肖孝建, 张宁. Fe(CN)63-/4-和细胞色素c电化学反应温度影响比较[J]. 电化学（中英文）, 2012, 18(1): 43-50.
[14]	陈飞彪, 吴伯荣, 安伟峰, 杨照军, 吴锋, 陈实, . 掺杂NiO的Ni(OH)_2电化学性能研究[J]. 电化学（中英文）, 2010, 16(1): 39-42.
[15]	艾新平, 曹余良, 杨汉西, . 高比能电池新材料与安全性新技术的研究进展 Ⅰ.锂离子电池自激发安全保护机制[J]. 电化学（中英文）, 2010, 16(1): 6-10.