磷钼酸修饰炭载Pd电极的H2O2电催化还原

doi:10.13208/j.electrochem.121110

电化学（中英文） ›› 2014, Vol. 20 ›› Issue (1): 56-59. doi: 10.13208/j.electrochem.121110

磷钼酸修饰炭载Pd电极的H₂O₂电催化还原

孙丽美^*，张铖，包英荣，李宏霞

内蒙古民族大学化学化工学院，内蒙古通辽 028000

收稿日期:2012-11-10 修回日期:2013-07-01 出版日期:2014-02-25 发布日期:2014-02-24
通讯作者: 孙丽美 E-mail:sunlimei2000@126.com
基金资助:
国家自然科学基金项目（No. 21003070）和内蒙古自治区自然科学基金(No. 2012MS0208)资助

Study on Carbon Supported Pd Catalysts Modified by Phosphomolybdic Acid for H₂O₂ Electrocatalytic Reduction

SUN Li-mei^*, ZHANG Cheng, BAO Ying-rong, LI Hong-Xia

College of Chemistry and Chemical Engineering, Inner Mongolia University for the Nationalities, TongLiao 028000, Inner Mongolia, China

Received:2012-11-10 Revised:2013-07-01 Published:2014-02-25 Online:2014-02-24
Contact: SUN Li-mei E-mail:sunlimei2000@126.com

摘要/Abstract

摘要： 采用化学还原法制备了炭载钯（Pd/C）催化剂，浸渍修饰磷钼酸（PMA）制备成复合催化剂. 通过XRD和红外谱图（IR）表征催化剂的组分和结构，采用线性扫描曲线及计时电流曲线考察了该电极的电催化性能. 研究表明，室温（20 ^oC）PMA-Pd/C电极的H₂O₂还原电催化活性更优.

关键词: 磷钼酸, 炭载钯催化剂, H₂O₂电还原, 燃料电池

Abstract: The Pd/C catalyst was prepared with the chemical reduction method, and phosphomolybdic acid (PMA) was modified on the Pd/C catalyst using the dipping method. The compositions and structures of the Pd/C and Pd/C modified by phosphomolybdic acid (PMA-Pd/C) catalysts were characterized with X-ray diffraction and Fourier Transform infrared spectroscopy analyses. The electrocatalytic activity and stability of the catalysts for the reduction of hydrogen peroxide (H₂O₂) were studied using cyclic voltammetry and chronoamperometry. The results showed that the phosphomolybdic acid was tightly fixed on the surface of Pd/C catalyst through the chemical interaction. The eletrocatalytic activity of the PMA-Pd/C on H₂O₂ reduction is higher than that of the Pd/C catalyst.

Key words: phosphomolybdic acid, Pd/C catalyst, hydrogen peroxide electroreduction, fuel cell

中图分类号:

O646

孙丽美*，张铖，包英荣，李宏霞. 磷钼酸修饰炭载Pd电极的H₂O₂电催化还原[J]. 电化学（中英文）, 2014, 20(1): 56-59.

SUN Li-mei*, ZHANG Cheng, BAO Ying-rong, LI Hong-Xia. Study on Carbon Supported Pd Catalysts Modified by Phosphomolybdic Acid for H₂O₂ Electrocatalytic Reduction[J]. Journal of Electrochemistry, 2014, 20(1): 56-59.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.13208/j.electrochem.121110

https://electrochem.xmu.edu.cn/CN/Y2014/V20/I1/56

参考文献

[1] Hasvold ?, Johansen K H, Mollestad O, et al. The alkaline aluminium-hydrogen peroxide power source in the Hugin II unmanned underwater vehicle[J]. Journal of Power Sources, 1999, 80: 254-260.
[2] Sun L M (孙丽美), Cao D X (曹殿学), Wang G L (王贵领), et al. Electrocatalytic reduction of hydrogen peroxide on Pd nanoparticles[J]. Acta Physico-Chimica Sinica (物理化学学报), 2008, 24(2): 323-327.
[3] Sun L M (孙丽美), Zhang C (张铖), Li H T (李惠婷), et al. A study of Pd-Ru on nickel foam cathode for magnesium-hydrogen peroxide semi-fuel cells[J]. Precious Metals (贵金属), 2011, 32(4): 1-5.
[4] Morais A L, Salgado J R C, Sljukic B, et al. Electrochemical behaviour of carbon supported ptelectrocatalysts for H2O2 reduction[J]. International Journal of Hydrogen Energy, 2012, 37: 14143-14151.
[5] Zhu D W (朱丁旺), Chen D D (陈丹丹), Li B J (李必进), et al. A study of Pd-Ir on nickel foam cathode for aluminum-hydrogen peroxide semi-fuel cells[J]. Journal of Electrochemistry (电化学), 2008, 14(3): 292-297.
[6] Sun L M, Cao D X, Wang G L. Pd-Ru/C as the electrocatalyst for hydrogen peroxide reduction[J]. Journal of Applied Electrochemistry, 2008, 38(10): 1415-1419.
[7] Cao D X, Gao Y Y, Wang G L, et al. A direct NaBH4-H2O2 fuel cell using Ni foam supported Au nanoparticles as electrodes[J]. International Journal of Hydrogen Energy, 2010, 35: 807-813.
[8] Inoue M, Nakazawa A, Umeda M. Effect of H2O2 on Pt electrode dissolution in H2SO4 solution based on electrochemical quartz crystal microbalance study[J]. International Journal of Hydrogen Energy, 2012, 37(2): 1226-1235.
[9] Satoshi T, Toshiyuki M, Tetsuya O. Electrodeposited Pd-Co catalyst for direct methanol fuel cell electrodes: Preparation and characterization[J]. Electrochimica Acta, 2008, 53(14): 4679-4686.
[10] Wang X, Tang Y W, Gao Y, et al. Carbon-supported Pd-Ir catalyst as anodic catalyst in direct formic acid fuel cell[J]. Journal of Power Sources, 2008, 175(2): 784-788.
[11] Wang R F, Liao S J, Ji S. High performance Pd-based catalysts for oxidation of formic acid[J]. Journal of Power Sources, 2008, 180(1): 205-208.
[12] Zhou W J, Lee J Y. Highly active core-shell Au@Pd catalyst for formic acid electrooxidation[J]. Electrochemistry Communications, 2007, 9(7): 1725-1729.
[13] Yang G X (杨改秀), Deng L J (邓玲娟), Tang Y W (唐亚文), et al. Promote action of phosphotungstic acid for electrooxidation of fomic acid at carbon supported Pd catalyst[J]. Chemical Journal of Chinese Universities (高等学校化学学报), 2009, 30(6): 1173-1176.
[14] Yang G X (杨改秀), Chen T T (陈婷婷), Tang Y W (唐亚文), et al. Electrocatalytic performance of silicotungstic acid modified carbon supported Pd catalyst for oxidation of fomic acid[J]. Acta Physico-Chimica Sinica (物理化学学报), 2009, 25(12): 2450-2454.
[15] Hong Y J (洪玉洁), Yang G X (杨改秀), Tang Y W (唐亚文), et al. Electrocatalytic performance of phosphomolybdic acid modified and carbon supported Pd catalyst for oxidation of formic acid[J]. Scientia Sinica Chimica (中国科学化学), 2010, 41(12): 1811-1816.
[16] Wang E B (王恩波), Hu C W (胡长文), Xu L (许林). Polyacid chemistry introduction[M]. Beijing: Chemical Industry Press (化学工业出版社), 1997: 14-237.
[17] Su Y (苏怡), Liu C P (刘长鹏), Shan Y B (单义斌), et al. Promotion effect of molybdophorsphoric acid on oxygen reduction for cathode of DMFC[J]. Chemical Journal of Chinese Universities (高等学校化学学报), 2005, 26(6): 1114-1117.
[18] Liu X D (刘晓娣), Liu S R (刘士荣). Characterization and catalytic performance of tungstophosphoric acid catalysts supported on activated carbon[J]. Journal of molecular catalysis (分子催化), 2007, 21(6): 503-509.
[19] Figueiredo J L, Pereira M F R, Freitas M M A, et al. Modification of the surface chemistry of activated carbons[J]. Carbon, 1999, 37(9): 1379-1389.
[20] El-Wahab M M M A, Said A A. Phosphomolybdic acid supported on silicagel and promoted with alkali metalions as catalysts for the esterification of acetic acid by ethanol[J]. Journal of Molecular Catalysis A: Chemical, 2005, 240(1/2): 109-118.

磷钼酸修饰炭载Pd电极的H₂O₂电催化还原

Study on Carbon Supported Pd Catalysts Modified by Phosphomolybdic Acid for H₂O₂ Electrocatalytic Reduction

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

[1]	陈发东, 谢卓洋, 李孟婷, 陈四国, 丁炜, 李莉, 李静, 魏子栋. 系列综述（1/4）:重庆大学魏子栋教授课题组在电化学能源转换方面的研究进展：燃料电池高性能氧还原催化剂[J]. 电化学（中英文）, 2024, 30(7): 2314007-.
[2]	陈浩杰, 唐美华, 陈胜利. 质子交换膜燃料电池阴极催化层疏水性优化[J]. 电化学（中英文）, 2023, 29(9): 2207061-.
[3]	郑天龙, 欧明玉, 徐松, 毛信表, 王释一, 和庆钢. 一体式可再生燃料电池双功能氧催化剂的研究进展[J]. 电化学（中英文）, 2023, 29(7): 2205301-.
[4]	韦宗楠, 曹敏纳, 曹荣. 瓜环基金属纳米催化剂的电化学研究进展[J]. 电化学（中英文）, 2023, 29(1): 2215008-.
[5]	黄龙, 徐海超, 荆碧, 李秋霞, 易伟, 孙世刚. 质子交换膜燃料电池铂基催化剂研究进展[J]. 电化学（中英文）, 2022, 28(1): 2108061-.
[6]	王睿卿, 隋升. PEMFC阴极催化层结构分析[J]. 电化学（中英文）, 2021, 27(6): 595-604.
[7]	朱从懿, 李笑晖, 甘全全. 乙二醇基冷却液污染对质子交换膜燃料电池电堆的影响及恢复措施[J]. 电化学（中英文）, 2021, 27(6): 698-704.
[8]	魏荣强, 李世安, 刘艺辉, 杨治, 沈秋婉, 杨国刚. 流道与肋宽比对气体扩散层性能影响的数值研究[J]. 电化学（中英文）, 2021, 27(5): 579-585.
[9]	吴志鹏, 钟传建. 钯基氧还原和乙醇氧化反应电催化剂:关于结构和机理研究的一些近期见解[J]. 电化学（中英文）, 2021, 27(2): 144-156.
[10]	庄志华, 陈卫. 原子数精确的金属纳米团簇在电催化领域的应用研究进展[J]. 电化学（中英文）, 2021, 27(2): 125-143.
[11]	胡守训, 李亮, 杨俊豪, 李刘强, 靳志豪. 金属钯插层类水滑石的制备及其电催化乙醇的性能研究[J]. 电化学（中英文）, 2021, 27(1): 100-107.
[12]	俞成荣, 朱建国, 蒋聪盈, 谷宇晨, 周晔欣, 李卓斌, 邬荣敏, 仲政, 官万兵. 基于电-化-热耦合理论对称双阴极固体氧化物燃料电池堆的电流与温度场数值模拟[J]. 电化学（中英文）, 2020, 26(6): 789-796.
[13]	王佳, 黄秋安, 李伟恒, 王娟, 庄全超, 张久俊. 电化学阻抗谱弛豫时间分布基础[J]. 电化学（中英文）, 2020, 26(5): 607-627.
[14]	李启浩, 王英明, 马华隆, 肖丽, 王功伟, 陆君涛, 庄林. 碱性膜燃料电池阳极碳酸化模型研究[J]. 电化学（中英文）, 2020, 26(5): 731-739.
[15]	张焰峰, 肖菲, 陈广宇, 邵敏华. 基于非贵金属氧还原催化剂的质子交换膜燃料电池性能[J]. 电化学（中英文）, 2020, 26(4): 563-572.