Cr_2O_3粉末在CaCl_2熔盐中直接电化学还原的金属通腔电极研究

电化学（中英文） ›› 2006, Vol. 12 ›› Issue (3): 304-309.

Cr_2O_3粉末在CaCl_2熔盐中直接电化学还原的金属通腔电极研究

邱国红;汪的华;金先波;胡晓宏;陈政;

武汉大学化学与分子科学学院,武汉大学化学与分子科学学院,武汉大学化学与分子科学学院,武汉大学化学与分子科学学院,武汉大学化学与分子科学学院湖北武汉430072,湖北武汉430072,湖北武汉430072,湖北武汉430072,湖北武汉430072

收稿日期:2006-08-28 修回日期:2006-08-28 出版日期:2006-08-28 发布日期:2006-08-28

Investigation of the Direct Electrochemical Reduction of Cr_(2)O_(3) Powder in Molten CaCl_(2) by a Metallic Cavity Electrode

QIU Guo-hong,WANG Di-hua,JIN Xian-bo,HU Xiao-hong,CHEN Zheng~*

(College of Chemistry and Molecular Sciences,Wuhan University,Wuhan 430072,Hubei,China

Received:2006-08-28 Revised:2006-08-28 Published:2006-08-28 Online:2006-08-28

摘要/Abstract

摘要： 应用金属通腔电极研究Cr2O3粉末于熔盐中的电化学行为,验证了900℃下Cr2O3粉末在含镁量<0.005%氯化钙熔盐中的分步还原机理,估算其电化学还原动力学参数;并由扫描电镜观察产物形貌,分析电解电位和时间对金属颗粒尺寸的影响.

关键词: 金属通腔电极, 直接电化学还原, 氧化铬粉末, 循环伏安法, 计时电流法, 熔盐

Abstract: A metallic cavity electrode is used for further investigation of the electrochemical behaviour of(Cr_(2)O_3) powder in molten CaCl_(2)(Na: ~0.02% by mass,Mg: < 0.005% by mass) at 900 ℃.The Cr_(2)O_(3) powder reduction mechanism was confirmed in line with EDX and SEM analysis of the potentiostatic electrolysis products.The correlations between the particle size of metallised product and the electrolysis potential,or electrolysis time were analysed.

Key words: Metallic cavity electrode, Direct electrochemical reduction, Chromium oxide powder, Cyclic voltammetry, Chronoamperometry, Molten salt

中图分类号:

O646.5

邱国红;汪的华;金先波;胡晓宏;陈政;. Cr_2O_3粉末在CaCl_2熔盐中直接电化学还原的金属通腔电极研究[J]. 电化学（中英文）, 2006, 12(3): 304-309.

QIU Guo-hong,WANG Di-hua,JIN Xian-bo,HU Xiao-hong,CHEN Zheng~*. Investigation of the Direct Electrochemical Reduction of Cr_(2)O_(3) Powder in Molten CaCl_(2) by a Metallic Cavity Electrode[J]. Journal of Electrochemistry, 2006, 12(3): 304-309.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2006/V12/I3/304

参考文献

[1]Chen G Z,Fray D J,Farth ing T W.D irect electro-chem ical reduction of titan ium d ioxide to titan ium inmolten calc ium chloride[J].Nature,2000,407:361~364. [2]W ang D ihua(汪的华),Chen Zheng(陈政).Innova-tion in molten salt electrochem istry[J].E lectrochem is-try(in Ch inese),2005,11(2):119~124. [3]Yan X Y,Fray D J.E lectrochem ical stud ies on reduc-tion of solid Nb2O5in molten CaC l2-NaC l eutectic[J].J.E lectrochem.Soc.,2005,152(1):D12~D21. [4]Chen G.Z,Gordo E,Fray D J.D irect electrolyticpreparation of chrom ium powder[J].M etall.M ater.Trans.B.,2004,35:223~233. [5]Gordo E,Chen G Z,Fray D J.Toward optim isation ofelectrolytic reduction of solid chrom ium oxide to chrom i-um powder in molten chloride salts[J].E lectroch im.Acta,2004,49:2195~2208. [6]Noh ira T,Yasuda K,Ito Y.P inpoint and bu lk electro-chem ical reduction of insu lating silicon d ioxide to sili-con[J].Nat.M ater.,2003,2:397~401. [7]Jin X ianbo,Gao Pe i,W ang D ihua,et al.E lectrochem-ical preparation of silicon and its alloys from solid ox-ides in molten calc ium chloride[J].Angew.Chem.Int.Ed.,2004,43:733~736. [8]Chen G Z,Fray D J.Voltamm ertic stud ies of the oxy-gen-titan ium b inary system in molten calc ium chloride[J].J.E lectrochem.Soc.,2002,149(11):E455~E467. [9]CHA C.S.(查全性).Introduction to E lectrode K inet-ics[M].3rdEd.,Be ijing:Sc ience Press,2002. [10]Q iu Guohong,M aM eng,W ang D ihua,et al.M etalliccavity electrode for investigation of powders:electro-chem ical reduction of N iO and Cr2O3powder in moltenCaC l2[J].J.E lectrochem.Soc.,2005,152:E328~E336. [11]Gao Pe i,Jin X ianbo,W ang D ihua,et al.A quartzsealed Ag/AgC l reference electrode for CaC l2basedmolten salts[J].J.E lectroanal.Chem.,2005,579:321~328. [12]L iu H,Stack M M,Lyon S B.Reactive elem enteffects on the ion ic transport processes in Cr2O3scales[J].Solid State Ion ics,1998,109:247~257. [13]Bard A J,Fau lkner L R.E lectrochem icalM ethods—Fundam entals and App lications[M].1 st and 2ndEd.,New York:John W iley&Sons,Inc.,1980~2001.

[1]	蔡雪凡, 孙升. 多孔电极电池的循环伏安法模拟[J]. 电化学（中英文）, 2021, 27(6): 646-657.
[2]	邢逸飞, 李娜, 温晓芳, 韩宏彦, 崔敏, 张聪, 任聚杰, 籍雪平. 基于取代型多酸复合材料的多巴胺电化学检测[J]. 电化学（中英文）, 2020, 26(6): 890-899.
[3]	邓博文, 尹华意, 汪的华. CO₂高效资源化利用的高温熔盐电化学技术研究[J]. 电化学（中英文）, 2020, 26(5): 628-638.
[4]	李明雪, 史杭, 刘佳, 张檬, 周剑章, 吴德印, 田中群. 金电极上偶氮腺嘌呤的电化学行为研究[J]. 电化学（中英文）, 2019, 25(6): 651-659.
[5]	凌云, 汤儆, 刘国坤, 宗铖. 暂态电化学表面增强拉曼光谱研究对硝基苯硫酚分子的电化学还原过程[J]. 电化学（中英文）, 2019, 25(6): 731-739.
[6]	董鹏飞, 李娜, 赵海燕, 崔敏, 张聪, 任聚杰, 藉雪平. Keggin 型磷钨酸盐修饰碳糊电极传感多巴胺的研究[J]. 电化学（中英文）, 2018, 24(5): 555-562.
[7]	郑艳洁，姚宏，翁少煌，彭花萍，龚仕文，黄莉，戴强，林新华. 硫酸特布他林在聚铬黑T修饰电极上的电化学行为及其测定[J]. 电化学（中英文）, 2016, 22(6): 617-623.
[8]	杨少华，王君，赖晓晖，王浩然. LiF-BaF₂-LiCl熔盐体系中Li⁺的电化学行为[J]. 电化学（中英文）, 2016, 22(3): 306-310.
[9]	杨星，陈平*. 对磺酸基苯偶氮杯[4]芳烃电化学行为研究[J]. 电化学（中英文）, 2016, 22(1): 37-42.
[10]	宋秀丽, 贾瑞龙, 董文燕, 梁镇海. 乙炔电催化氧化制备草酸的机理研究[J]. 电化学（中英文）, 2015, 21(4): 353-361.
[11]	陈华林，王志勇，金先波*，陈政. 固态氧化物阴极过程的离子扩散模型及其Ta₂O₅熔盐电解验证[J]. 电化学（中英文）, 2014, 20(3): 266-271.
[12]	M. Rostom Ali*, Md. Ziaur Rahman, S. SankarSaha. 基于氯化胆碱离子液体的铜电沉积研究（英文）[J]. 电化学（中英文）, 2014, 20(2): 139-145.
[13]	李凯, 陈棽, 刘深娜, 陈碧桑, 林珩, 陈国良, 汪庆祥. 玻碳电极肉桂酸添加剂对锌电沉积的影响[J]. 电化学（中英文）, 2013, 19(3): 267-274.
[14]	肖巍, 朱华, 尹华意, 汪的华. 熔盐电化学低碳冶金新技术研究[J]. 电化学（中英文）, 2012, 18(3): 193-200.
[15]	程玉龙, 孙杰, 李吉刚, 张立功, 周添, 常耕, 董中朝. Pt/MO2/CNTs催化剂上乙醇电氧化研究[J]. 电化学（中英文）, 2012, 18(2): 131-134.