应力对低合金钢焊接接头相电化学行为的影响

电化学（中英文） ›› 1999, Vol. 5 ›› Issue (1): 49-54.

应力对低合金钢焊接接头相电化学行为的影响

吴荫顺,刘德宇,曹备,王凤丽,方智,张琳,张峥嵘,杨海

北京科技大学表面科学与腐蚀工程系

收稿日期:1999-02-28 修回日期:1999-02-28 出版日期:1999-02-28 发布日期:1999-02-28

Effect of Stress on Electrochemical Behaviour of Various Thermal History Zones and Different Phase Structures on the Weldment for Low Alloy Steel

Wu Yinshun Liu Deyu Cao Bei Wang Fengli Fang Zhi Zhang Lin Zhang Zhengrong Yang Hai

(Univ. of Science and Technology Beijing, Beijing 100083, China

Received:1999-02-28 Revised:1999-02-28 Published:1999-02-28 Online:1999-02-28

摘要/Abstract

摘要： 采用微区相电化学测试技术，测量和研究了１６Ｍｎ钢焊接接头上不同热经历区在硝酸盐溶液中的微区相电化学行为（包括自腐蚀电位、自腐蚀电流密度和极化曲线）以及外加载荷（应力）的影响．此外，还分别测量了各区中铁素体和珠光体的电化学行为，尤其是加载状态下的行为．结果表明，加载后各热经历区以及各区中铁素体和珠光体的自腐蚀电位均比未加载前负移，相应的自腐蚀电流密度增大，铁素体和珠光体之间电位差明显减小．加载后各热经历区中自腐蚀电位最负和次负的仍处在熔合线区和不完全正火区，从而成为焊接接头腐蚀电池中的率先腐蚀区．应力促进腐蚀并非是通过增大铁素体和珠光体之间的电位差，而是通过提高各微区相组织自身的电化学活性来实现的．

关键词: 低合金钢, 焊接接头, 相电化学, 应力, 硝酸盐溶液

Abstract: The electrochemical behaviour of various thermal history zones on the weldment for steel 16Mn and also of the ferrite,pearlite in various zones was measured by use of a self-developed measuring technique for investigating the electrochemicl behaviour of single and mixed phase structures in metal materials.Especially the effect of stress on this electrochemical behaviour was investigated.The results showed that by comparison with non-stress condition,the free corrosion potential of the various thermal history zones and of the ferrite,pearlite under stress condition was shifted in negative direction,correspondingly their free corrosion current density was increased,the free corrosion potential difference between ferrite and pearlite was decreased obviously. After applying stress the negativest and the second negativest free corrosion potentiats between vavious thermal history zones were still for the fusion line zone and the incomplete normallized zone,which thereby were become the preferrentially corroded locations on the weldment as a corrosion cell.The stress accelerated corrosion course that did act not through inceasing free corrsion potential difference between ferrite and pearlite,but through enhancing the electrochemical activity of the relevant micro zone and/or phase strueture.

Key words: Low alloy steel, Weldment, Phase electrochemistry, Stress, Nitrate solution

中图分类号:

吴荫顺,刘德宇,曹备,王凤丽,方智,张琳,张峥嵘,杨海. 应力对低合金钢焊接接头相电化学行为的影响[J]. 电化学（中英文）, 1999, 5(1): 49-54.

Wu Yinshun Liu Deyu Cao Bei Wang Fengli Fang Zhi Zhang Lin Zhang Zhengrong Yang Hai . Effect of Stress on Electrochemical Behaviour of Various Thermal History Zones and Different Phase Structures on the Weldment for Low Alloy Steel[J]. Journal of Electrochemistry, 1999, 5(1): 49-54.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y1999/V5/I1/49

[1]	罗宇, 马如琴, 龚正良, 杨勇. 固态锂硫电池研究进展[J]. 电化学（中英文）, 2023, 29(3): 2217007-.
[2]	王大为, 李东江, 李军, 杨勇. 锂离子电池电化学反应模型研究进展浅析[J]. 电化学（中英文）, 2011, 17(4): 355-362.
[3]	刘智勇, 董超芳, 李晓刚, 王立贤, . H_2S环境中UNS J91540不锈钢的电化学行为对SCC的影响[J]. 电化学（中英文）, 2009, 15(2): 157-162.
[4]	赵茹, 宋诗哲, 张正, . 预制裂纹304SS试样慢拉伸过程EN和SKP表征[J]. 电化学（中英文）, 2009, 15(2): 141-145.
[5]	曾传铭,罗亦旋,蔡文达. 双相不锈钢在水溶液中之腐蚀疲劳与动态应变时效[J]. 电化学（中英文）, 2003, 9(3): 265-271.
[6]	张新生,许淳淳,胡钢. 亚稳态304不锈钢应力腐蚀影响因素探讨[J]. 电化学（中英文）, 2003, 9(3): 320-326.
[7]	郭建伟, 梁成浩. 高温高浓度溴化锂溶液对低合金钢的电化学行为作用[J]. 电化学（中英文）, 2000, 6(4): 451-457.
[8]	王庆飞,隋静,苏润西,孔德英,宋诗哲. 模拟生物膜方法研究钢在海水中的腐蚀行为[J]. 电化学（中英文）, 1999, 5(1): 55-58.
[9]	苏光耀,高德淑,张长青. 聚苯胺粒子悬浮液的电流变特性[J]. 电化学（中英文）, 1997, 3(3): 325-329.
[10]	林昌健，冯祖德，林福龄，王发扬，谭建光，王元辉. 18／8型不锈钢在受力形变条件下腐蚀电化学行为的研究[J]. 电化学（中英文）, 1995, 1(4): 439-445.