The Effects of Magnetic Field onthe Electropolymerization of Aniline

Cai Lintao; Yao Shibing; Zhou Shaomin

(Dept. of Chem., Xiamen Univ. , Xiamen 361005

Received:1995-05-28 Revised:1995-05-28 Published:1995-05-28 Online:1995-05-28

摘要/Abstract

摘要： 本文研究了外加磁场对苯胺电聚合过程的影响．在Ｈ＿２ＳＯ＿４介质中，当磁场方向垂直电极表面时，在０．５８Ｔ处聚合速度最大，约为无磁场影响下的２倍；当磁场方向平行电极表面时，随磁场强度的增加聚合速度也增大，在０．７Ｔ时约为无磁场影响下的２．４倍；膜的成核生长是在动力学控制下的二维瞬时成核过程．此外，在ＨＣｌ、ＨＣｌＯ＿４、ＨＢＦ＿４介质中，也观察到磁场的增强现象．

关键词: 导电高分子, 聚苯胺, 电聚合, 成核生长, 磁场效应

Abstract: The aniline electropolyinerization under the magnetic field was studied by cyclicvoltammetry and potentiostatic step techniques. Theinaximum peak current was obtained at 0. 58 Twhen the magnetic flux was perpendicular to the surface of the working electrede in H_2SO_4 solution.These were speculated in terins of magnetic dircctional effect. But when the magneic flux directed inparallcl with the surface of elcctrode, the peak current obviously increased as the magnetic flux densityrised. The results uere explained as the enhancement of mass transfer by magnetohydredynamic(MHD) mechanism. The PAN film growth via a two-dimentional (2-D) instantaneous nucleationunder the electron transfer kinetic controlled. The enhanced effects were also obtained in HCl、 HClO_4、HBF_4 solutions.

Key words: Conducting polymer, Polyaniline, Electropolymerization, Nucleation, Magnetic field effect

中图分类号:

O633.2

蔡林涛，姚士冰，周绍民. 磁场对苯胺电聚合的影响[J]. 电化学（中英文）, 1995, 1(2): 159-165.

Cai Lintao; Yao Shibing; Zhou Shaomin. The Effects of Magnetic Field onthe Electropolymerization of Aniline[J]. Journal of Electrochemistry, 1995, 1(2): 159-165.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y1995/V1/I2/159

参考文献

1HoffAJandLuusEJ．BiophysicalEffectsofSteadyMagneticFields，edbyMaretG，KiepenhourerJandBoccaraN，Spring－Verlag．1986：742WakasaM，SakaguchiY，HayashiH．Magneticfieldeffectonphotodecompositionofp－aminophenyldisulfideinamicellarsolution．J．Phys．Chem．．1993，97：17333TurroNJ，ChowMF，ChungCJetal．Magneticfieldandmagneticisotopeeffectsoncagereactionsinmicellarsolutions．J．Am．Chem．Soc．，1980，102：48434MurayamaM．Orientationofsicklederythrocytesinaniagneticfield．Nature．，1965，206：4205StuppIetal．Pullingpolyniersintoline．ScienceNews，1986，129：2976FahidyTZ．Magnetoelectrolysis．J．APPl．Electrochem．，1983，13：5537KellyEJ．Magneticfieldeffectsonelectochemicalreactionsoccuringatmetal／flowing－electrolyteinterfaces．J．Electrochem．Soc．，1977，124：9878FahidyTZ．Hydredynamicmodelsinmagnetoelectrolysis．Electrochim．Acta．，1973，18：6079IsmailMIandFahidyTZ．Morphologiealcharacteristicsofcopperdepositiononstainlesssteelcathodes．J．Appl．Electrochem．，1981，11：54310TakahashiFTorniiKandTakahashiH．Theelectrochemicalasvmmetricreductionofα－ketoacidsinthemagneticfields．ElectrochimActa．1986，31：12711KalajiM，NyholmL，PeterLM．AmicroelectredestudyoftheinfluenceofpHandsolutioncompositionontheelectrochemicalbehaviourofpolyanilinefilms．，J．Electroanal．Chem．，1991，313：27112MohilnerDM．AdamsRN，ArgersingerWJ．Investigatinofthekineticsandmechanismoftheanodicoxidationofanilineinaqueoussulfuricacidsolutionsataplatintimelectrode．J．Electronal．Chem．，1986，215：40113TurroNJ，ChowMF，ChungCJetal．Anefficient，highconversionhotoinducedemulsionpolyrnerization．Magneticfieldeffectsonpolymerizationefficiencyandpolymermolecularweight．J．Am．Chem．Soc．，1980，102：739314MoriK，TabataY，OshimaK．Effectofmagneticfieldonradiationinducedsolidstatepolymerizationofacetaldenydeatlowtemperatures．工业化学杂志（日本），1970，73：81515AaboubiO，ChopartJP，OlivierAetal．Magneticfieldeffectsonmasstransport．J．Electrochem．Soc．，1990，137：179616ThirskHR，HarrisonA．AGuidetotheStudyofElectrodeKinetics．LondonandNewYork：Academicpress，1972：11517蔡林涛，姚士冰，周绍民．聚苯胺的成核及生长机理．化学学报，待发表．

[1]	徐坤, 周开岭, 汪浩, 刘晶冰, 严辉. 聚苯胺电致变色薄膜在不同颜色区间的电化学循环稳定性研究[J]. 电化学（中英文）, 2019, 25(6): 690-698.
[2]	李张峰, 王晓锐, 田文生, 杨津泽, 张平, 马丽萍, 陈阳, 崔晓莉, 江志裕. 利用升华物质2,4,6-三异丙基-1,3,5-三氧杂环己烷作模板剂制备聚苯胺包覆的中空硫电极材料[J]. 电化学（中英文）, 2019, 25(6): 645-650.
[3]	周田田，邬冰，邓超，高颖. 锰氧化物聚苯胺复合电极材料的制备与性能[J]. 电化学（中英文）, 2018, 24(2): 137-142.
[4]	栾琼，薛春峰，祝红叶，杨复娟，马旭莉，郝晓刚. 以金属有机骨架材料HKUST-1为模板制备多孔聚苯胺电极及其超级电容器性能研究[J]. 电化学（中英文）, 2017, 23(1): 13-20.
[5]	吉维肖，王凤，钱江锋，曹余良，艾新平，杨汉西. 3, 4-乙烯二氧噻吩单体用作锂离子电池安全性改善添加剂的研究[J]. 电化学（中英文）, 2016, 22(3): 271-277.
[6]	段舒怡，张伟，朴俊宇，曹安民，万立骏. 具有均匀壳层的纳米功能材料：构筑与应用[J]. 电化学（中英文）, 2016, 22(3): 260-270.
[7]	徐惠*，蒲金娟，陈泳，刘健. Ag⁺掺杂聚苯胺的制备及其电容特性研究[J]. 电化学（中英文）, 2016, 22(1): 64-69.
[8]	廖森梁，李修敏，郝晓刚，王艳红，薛春峰，王永洪. 单极脉冲一步合成聚苯胺/铁氰化镍杂化膜及其过氧化氢电催化还原活性[J]. 电化学（中英文）, 2014, 20(6): 563-570.
[9]	左阳，时康*. 由苯胺二聚体电化学制备聚苯胺的形貌可控性初探[J]. 电化学（中英文）, 2014, 20(1): 17-21.
[10]	杨宇娇, 郝晓刚, 马旭莉, 王忠德, 张忠林, 韩念琛. 聚苯胺/铁氰化镍纳米复合颗粒的制备及电控分离Cd的EQCM研究[J]. 电化学（中英文）, 2013, 19(5): 493-498.
[11]	冯艳婷, 肖俊强, 郝晓刚, 马旭莉, 王忠德, 韩念琛. PANI-SnP复合膜电极在镍镉废水中电控离子交换性能[J]. 电化学（中英文）, 2013, 19(4): 322-327.
[12]	翁少煌, 周剑章, 林仲华, 林新华. 多级树状纳米结构聚苯胺的电化学制备[J]. 电化学（中英文）, 2013, 19(2): 130-134.
[13]	张光辉, 沈培康, 桑革, 熊仁金. PAni/Si/G/C复合材料的制备及电化学性能[J]. 电化学（中英文）, 2013, 19(2): 184-188.
[14]	周晓航, 陈政. 钛双极片上网印导电聚合物——碳纳米管复合物及其在水型不对称超级电容器中的电化学性能[J]. 电化学（中英文）, 2012, 18(6): 548-565.
[15]	高艳新, 孙丽超, 谢素原, 时康. 电化学制备有序聚苯胺纳米线阵列[J]. 电化学（中英文）, 2012, 18(1): 51-55.