铅镧和铅钐合金在硫酸溶液中生长的阳极膜性质的研究

电化学（中英文） ›› 2001, Vol. 7 ›› Issue (4): 439-444.

铅镧和铅钐合金在硫酸溶液中生长的阳极膜性质的研究

柳厚田,杨春晓,梁海河,杨炯,周伟舫

复旦大学化学系,复旦大学化学系,复旦大学化学系,复旦大学化学系,复旦大学化学系上海200433 ,上海200433 ,上海200433 ,上海200433 ,上海200433

收稿日期:2001-11-28 修回日期:2001-11-28 出版日期:2001-11-28 发布日期:2001-11-28

Studies on the Properties of the Anodic Films Formed on Lead- Lanthanum and Lead-Samarium Alloys in Sulfuric Acid Solution

LIU Hou tian *,YANG Chun xuao,LIANG Hai heng,YANG Jiong,Zhou Wei fang

(Dept. of Chem., Fudan Univ., Shanghai 200433, China

Received:2001-11-28 Revised:2001-11-28 Published:2001-11-28 Online:2001-11-28

摘要/Abstract

摘要： 应用交流伏安法和线性电位扫描法研究了Pb ,Pb 1.0at%La和Pb 1.0at%Sm电极在硫酸溶液中以 0 .9V(vs .Hg/Hg2 SO4 )生长的阳极Pb(Ⅱ )膜增长率和膜的阻抗实部变化 ,并采用循环伏安法研究了它们在 0 .6～ 1.6V(vs.Hg/Hg2 SO4 )间的循环伏安特性 ,结果表明 :在铅中添加Sm有利于抑制铅的阳极腐蚀和降低阳极Pb(Ⅱ )膜的阻抗 ,La亦可降低阳极Pb(Ⅱ )膜的阻抗 ,但其作用不如Sm明显

关键词: Pb, PbLa, PbSm, 阳极Pb(Ⅱ)膜

Abstract: AC voltammetry,linear sweep voltammetry,and cyclic voltammetry were applied to study the anodic corrosion of Pb,Pb 1.0at%La and Pb 1.0at%Sm electrodes in 4.5 mol·dm -3 H 2SO 4 solution (25 ℃).The experiment results show that samarium can inhibit the anodic corrosion of lead and decrease the impedance of anodic Pb(Ⅱ) film. Lanthanum can also decrease the impedance of the anodic Pb(Ⅱ)film, but the effect is smaller.

Key words: Pb, Pb La, Pb Sm, Anodic Pb(Ⅱ) film

中图分类号:

O646.6

柳厚田,杨春晓,梁海河,杨炯,周伟舫. 铅镧和铅钐合金在硫酸溶液中生长的阳极膜性质的研究[J]. 电化学（中英文）, 2001, 7(4): 439-444.

LIU Hou tian *,YANG Chun xuao,LIANG Hai heng,YANG Jiong,Zhou Wei fang . Studies on the Properties of the Anodic Films Formed on Lead- Lanthanum and Lead-Samarium Alloys in Sulfuric Acid Solution[J]. Journal of Electrochemistry, 2001, 7(4): 439-444.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2001/V7/I4/439

参考文献

[1]　GiessHerbert.Theinfluenceofcalciumtinandgridthicknessoncorrosioninducedgridgrowth[J].J.PowerSources,1995,53(1):31. [2]　TakahashiK .,YasudaH .,TakamiN .,etal.Analysisoftheconditionsthatpromotepassivationoncalcium-alloygridsinlead/acidbetteries[J].J .PowerSources,1991,36(4):451. [3]　CaillerieJ.-L .,AlbertL ..Lead-calciumalloydevelopment:qualityimprovement[J].J .PowerSources,1997,67(1-2):279. [4]　LiuHoutian,WangFengwen,XuPindi,etal.Anodiccorrosionbehavioroflead-strontiumalloysinsulfuricacidsolution[J].J .FudanUniversity(NaturalScience),1995,34(1):25. [5]　LiuYifei,XuPindi,LiuHoutian.StudyonelectrochemicalbehaviorofPbBaalloyinH2SO4 solution[J].XuDianChi,1995,(2):3. [6]　BuiNam,MattescoPatrick,SimonPatrice.etal.Thetineffectinlead-calciumalloys[J].J .PowerSources,1997,67(1-2):61. [7]　PavlovD .PowerSourcesforElectricVehicles(ed.byMcNicolBD ,RandRAJ)[M].Amsterdam:Elsevier,1984:243;254. [8]　LiuHoutian,YangJiong,LiangHai-he,etal.TheeffectofceriumontheanodicbehaviorofPbCaSnalloyinsulfuricacidsolution[J].Electrochemistry(inChinese),2000,6(3):265. [9]　LiuHoutian,ZhouWeifang.Effectofchargevoltageonperformanceofleadacidstoragebatteryanditselec trodes[J].J .FudanUniversity(NaturalScience),1988,27(1):45. [10]　HanJun,PuCong,ZhouWeifang.Determinationofthephasecompositonofanodiclead(Ⅱ)filmformedinsulfuricacidsolution[J].J .Electroanal.Chem.,1994,368(1-2):43. [11]　LiuHoutian,XuPindi,ZhouWeifang.Effectofcorrosionperformanceoflowantimony-leadalloysoncy clelifeoflead-acidbattery[J].ChineseJournalofAppliedChemistry,1991,8(4):60. [12]　ZhouWeifang,LiuHoutian,WeiChang,etal.Theanodicfilmoflead-antimonyalloysinsulfuricacidso lution,Ⅲ.Theeffectofcyclictriangularwavepotentialsweeponthegrowthoftheanodicfilm[J].ActachimicaSinica,1986,44(4):399. [13]　ZhouWeifang,ChengXialing.Theanodicfilmoflead-antimonyalloysinsulfuricacidsolution,I.Theki neticsoftheearlystageanodicfilm growth[J].ActaChimicaSinica,1985,43(4):333

[1]	王伟国, 白天, 薛高飞, 叶美丹. CsPbIBr₂钙钛矿太阳能电池中通过氧气诱导Spiro-OMeTAD快速氧化[J]. 电化学（中英文）, 2021, 27(2): 216-226.
[2]	王鸿辉，马明洁，冯婕，康黄雅，黄文杰. 钕掺杂二氧化铅复合阳极的电化学性能研究[J]. 电化学（中英文）, 2018, 24(4): 367-374.
[3]	张媛媛，易清风，左葛琨琨，邹涛，刘小平，周秀林. 铅修饰的纳米多孔铂催化剂对甲酸氧化的电活性[J]. 电化学（中英文）, 2018, 24(3): 270-278.
[4]	乔文磊，杜晓，高凤凤，郑君兰，李莎莎，郝晓刚. 一步共沉积法制备ZSM-5/PANI/PSS电活性膜及其电控选择性分离重金属Pb²⁺的动力学特性[J]. 电化学（中英文）, 2018, 24(2): 143-153.
[5]	王磊, 薛娟琴, 于丽花, 唐长斌, 毕强. 温度对PbO₂电沉积形核生长过程的影响研究[J]. 电化学（中英文）, 2017, 23(4): 480-488.
[6]	李鹏，赵跃民，王立章*，张延乐，芦兆青. β-PbO₂/Sb-SnO₂/Ti电极的苯酚电催化性能研究[J]. 电化学（中英文）, 2014, 20(5): 493-498.
[7]	高云芳*, 王艳平, 姚秋实, 王福华, 任冬雷, 徐新. 氧化铅/石墨烯/活性炭的制备及电化学行为（英文）[J]. 电化学（中英文）, 2014, 20(5): 486-492.
[8]	陈飞翔, 杨初引, 周明明, 王家德. 印染废水的电化学深度处理及回用研究[J]. 电化学（中英文）, 2013, 19(4): 341-344.
[9]	刘晓蕾, 丹媛媛, 陆海彦, 林海波, 欧阳明丽, 袁传军. 不同掺杂元素的钛基PbO₂电极对苯酚电催化氧化性能的影响[J]. 电化学（中英文）, 2013, 19(1): 59-64.
[10]	王佳, 姜晶, . 分散液膜气/液/固三相线界面区宽度在金属大气腐蚀中的作用(英文)[J]. 电化学（中英文）, 2010, 16(4): 385-392.
[11]	褚道葆, 王峰, 肖英, 张雪娇, . L-胱氨酸在Pb/nanoTiO_2膜电极上的电催化还原[J]. 电化学（中英文）, 2010, 16(1): 85-89.
[12]	孙红艳, 梁镇海, . 电合成2,2-二羟甲基丙酸[J]. 电化学（中英文）, 2009, 15(1): 96-101.
[13]	郭士元;张爱丽;周集体;. 不同惰性填料复极性固定床电解槽处理对硝基酚钠废水行为比较[J]. 电化学（中英文）, 2006, 12(2): 165-169.
[14]	李党国;周根树;姚靓;郑茂盛;. 稀土铅钙合金与传统铅钙合金在硫酸溶液中的阳极行为研究[J]. 电化学（中英文）, 2006, 12(1): 46-49.
[15]	柳厚田,杨炯,梁海河,庄继华,周伟舫. 铈对铅钙锡合金在硫酸溶液中阳极行为的影响[J]. 电化学（中英文）, 2000, 6(3): 265-271.