用于预测高温高浓度溴化锂溶液中碳钢腐蚀行为的BP神经网络(英文)

电化学（中英文） ›› 2003, Vol. 9 ›› Issue (2): 228-234.

用于预测高温高浓度溴化锂溶液中碳钢腐蚀行为的BP神经网络(英文)

黄乃宝,梁成浩

大连理工大学化工学院,大连理工大学化工学院辽宁大连116012 ,辽宁大连116012

收稿日期:2003-05-28 修回日期:2003-05-28 出版日期:2003-05-28 发布日期:2003-05-28

Corrosion Prediction of Carbon Steel in Concentrated Lithium Bromide Solutions at High Temperature Using BP Neural Network

HUANG Nai_bao,LIANG Cheng_hao*

(School of Chemical Engineering,Dalian University of Technology,Dalian 116012,China)

Received:2003-05-28 Revised:2003-05-28 Published:2003-05-28 Online:2003-05-28

摘要/Abstract

摘要： 　本文建立了预测碳钢在LiBr溶液中腐蚀速率的神经网络模型.该模型拟合了碱度,温度,LiBr和Na2MoO4浓度变化对碳钢全面腐蚀速率的影响,可用于准确预测不同温度下,在含有不同缓蚀剂的LiBr溶液中的碳钢腐蚀速率,其预测值和实验值完全吻合,为研究溴冷机中金属材料的腐蚀和现场监测提供了新的思路和方法.

关键词: 腐蚀, 碳钢, LiBr, BP神经网络

Abstract: Neutral network model has been developed for the computation of corrosion rate of carbon steel in LiBr solutions.The results indicate that the model is capable of reproducing the effects of changes in alkalinity,temperatures,LiBr and Na2MoO4 concentrations on the rates of general corrsion and good agreement between calculated and experimental corrosion rate is obtained.The model can be used to satisfactorily predict the corrosion rate of carbon steel in different concentrations of LiBr solutions containing different inhibitors at different temperatures.It also provides a novel method for corrosion monitoring of metals used in LiBr absorption chiller.

中图分类号:

TG174.42

黄乃宝, 梁成浩. 用于预测高温高浓度溴化锂溶液中碳钢腐蚀行为的BP神经网络(英文)[J]. 电化学（中英文）, 2003, 9(2): 228-234.

HUANG Nai_bao, LIANG Cheng_hao. Corrosion Prediction of Carbon Steel in Concentrated Lithium Bromide Solutions at High Temperature Using BP Neural Network[J]. Journal of Electrochemistry, 2003, 9(2): 228-234.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2003/V9/I2/228

参考文献

[1]　KazuoTanno,ShiroSaaito,MasahikoIto,etal.Corrosioninhibitionofcarbonsteel,copperand70/30cupro＿nickelbybenzotriazoleinconcentratedlithiumbromidesolutionatelevatedtemperature[J].BoshokuGijtsu,1984,33:516～519. [2]　MasahikoItoh,AkiraMinato,MichihikoAizawa,etal.Corrosioninhibitionofcarbonsteelandcupro＿nickelbylithiummolybdateinconcentratedlithiumbromidesolutionatelevatedtemperature[J].BoshokuGijtsu,1984,33:504～508. [3]　TannoK,ItohM,TakahashiT,etal.Thecorrosionofcarbonsteelinlithiumbromidesolutionatmoderatetemperatures[J].CorrosionScience,1993,34(9):1441～1451. [4]　TannoK,M.ItonM,HekiyaH,etal.Thecorrosioninhibitionofcarbonsteelinlithiumbromidesolutionbyhydroxideandmolybdateatmoderatetemperatures[J].CorrosionScience,1993,34(9):1453～1461. [5]　HitoshiYashiro,AkijikoSai,NaoakiKumagai,etal.CorrosionbehaviorofcarbonsteelinconcentratedLiBrsolutionsupto473K[J].Zairoy＿to＿Kankoy,1999..48(6):369～374. [6]　GuoJian＿wei,LiangCheng＿hao.Mechanismoftheformationofpassivestatefilmsoncarbonsteelinahightemperatureandhighconcentrationlithiumbromidesolution[J].MaterialsScienceandTechnology(inChinese),2001,9(4):413～416.. [7]　GuoJian＿wei,LiangCheng＿hao.Corrosionbehaviorofcarbonsteelinhightemperatureandhighconcentrationlithiumbromidesolution[J].J.ofDalianUniversityofTechnology(inChinese),2000,40(5):554～556. [8]　GuoJian＿wei.Researchofinhibitionmechanismonabsorptionlithiumbromiderefrigerator[D].Dalian:DalianUniversityofTechnology,2000. [9]　Chun＿genYin,Zhong＿yangLuo,MingjiangNi,etal.Predictingcoalashfusiontemperaturewithaback＿propagationneuralnetworkmodel[J].Fuel,1998,77(15):1777～1782. [10]　SmetsHMG,BogaertsWFL.SCCanalysisofaustieniticstainlessinchloride＿bearingwaterbyneuralnetworktechniques[J].Corrosion,1992,48(8):618～623. [11]　RosenEM,SilvermanDL.Corrosionpredictionfrompolarizationscansusinganartificialneuralnetworkintegratedwithanexpertsystem[J].Corrosion,1992,48(9):734～744. [12]　TrasattiSP,MazzaF.Crevicecorrosion,aneuralnetworkapproach[J].BritishCorrosionJournal,1996,31(2):105～112. [13]　HoskinsJC,HimmelblauDM.Processcontrolviaartificialneuralnetworksandreinforcementlearning[J].Comput.Chem.Eng.,1992,16(4)141～151. [14]　MirchadaniG,CaoW.Onhiddenunitsinneuralnets[J].IEEETransCircuitsSyst,1989,36(15):661～664.

[1]	张芯婉, 孟广源, 方立强, 常定明, 李童, 胡锦文, 陈鹏, 刘勇弟, 张乐华. 基于BP神经网络的电化学还原硝酸盐过程智能控制[J]. 电化学（中英文）, 2023, 29(12): 211215-.
[2]	秦凯旋, 常鹏飞, 黄钰林, 李明, 杭弢. 钴互连化学机械抛光浆料中的界面腐蚀行为研究[J]. 电化学（中英文）, 2022, 28(6): 2104471-.
[3]	杨森, 王文昌, 张然, 秦水平, 吴敏娴, 光崎尚利, 陈智栋. 醇硫基丙烷磺酸钠对电解高性能锂电铜箔的影响[J]. 电化学（中英文）, 2022, 28(6): 2104501-.
[4]	张涛, 刘一蒲, 叶齐通, 范红金. 工业级碱性海水电解:近期进展和展望[J]. 电化学（中英文）, 2022, 28(10): 2214006-.
[5]	况先银, 金少强, 曹艳辉, 张艳梅, 董士刚, 朱龙晖, 林理文, 林昌健. 铝合金表面改性对有机涂层附着力的影响及腐蚀防护性能研究[J]. 电化学（中英文）, 2021, 27(6): 624-636.
[6]	邹振文, 郑大江, 王子明, 宋光铃. 新型单丝电极交流探头在3.5wt.% NaCl中的电化学响应规律研究[J]. 电化学（中英文）, 2020, 26(3): 317-327.
[7]	张翅, 李成飞, 李高仁. 负载于刻蚀镍泡沫上钯纳米粒子作为乙醇氧化高性能电催化剂[J]. 电化学（中英文）, 2019, 25(5): 571-578.
[8]	赫威，燕汝，王瑛琦，高翔，马厚义. 在冷轧钢板表面制备二乙烯三胺五甲叉膦酸-锌化学转化膜及其腐蚀防护性能的研究[J]. 电化学（中英文）, 2018, 24(2): 111-121.
[9]	H. A. Fetouh, B.A. Abd-El-Nabey, Y.M. Goher, M. S. Karam. 银纳米颗粒对铝金属在酸性介质中的耐蚀性能研究[J]. 电化学（中英文）, 2018, 24(1): 89-100.
[10]	陈晓航，陈寞静，闵宇霖，徐群杰. 水热法制备铝合金超疏水表面及电化学性能研究[J]. 电化学（中英文）, 2018, 24(1): 28-35.
[11]	徐天宇，王世颖，王文昌，陈智栋. 镍离子对中磷镍基体氯化胆碱无氰浸金表面的改善[J]. 电化学（中英文）, 2018, 24(1): 36-39.
[12]	王静静，董士刚，张小娟，吕虹玮，伍运昌，杜荣归，林昌健. pH/Cl^-复合探针技术对钢筋混凝土电化学除氯的原位检测[J]. 电化学（中英文）, 2014, 20(2): 95-100.
[13]	叶陈清，胡融刚，侯瑞青，王小平，杜荣归，林昌健*. 敏化处理304不锈钢局部腐蚀行为的扫描微电极法研究[J]. 电化学（中英文）, 2013, 19(6): 507-511.
[14]	曹发和, 夏妍, 刘文娟, 常林荣, 张鉴清. SECM基本原理及其在金属腐蚀中的应用[J]. 电化学（中英文）, 2013, 19(5): 393-401.
[15]	李凌杰, 贺毓玲, 雷惊雷, 张胜涛. 椭圆偏振光谱技术的腐蚀研究应用[J]. 电化学（中英文）, 2013, 19(5): 402-408.