新型Fe_3O_4-Fe复合阳极的研制

电化学（中英文） ›› 2005, Vol. 11 ›› Issue (2): 157-161.

新型Fe_3O_4-Fe复合阳极的研制

熊信勇,范列朋,王茂华,郭琦龙,洪艳萍,黄长辉,吴佳林

中国科学院福建物质结构研究所,中国科学院福建物质结构研究所,福州市煤气公司,中国科学院福建物质结构研究所,中国科学院福建物质结构研究所,中国科学院福建物质结构研究所,中国科学院福建物质结构研究所福建厦门361012 ,福建厦门361012 ,福建福州350002 ,福建厦门361012 ,福建厦门361012 ,福建厦门361012 ,福建厦门361012

收稿日期:2005-05-28 修回日期:2005-05-28 出版日期:2005-05-28 发布日期:2005-05-28

Study on the New Type Fe_3O_4 composite Anode

XIONGXin-yong~

(1), FANLie-peng~(1), WANG Mao-hua~(2), GUOQi-long~(1), HONGYan-ping~(1), HUANGChang-hui~(1), WU Jia-lin~(1) (1.Fujian Institute of Research on the Structure of Matter,Chinese Academy of Sciences,Xiamen 361012,China,2. Fuzhou Gas Company, Fuzhou 350002, China

Received:2005-05-28 Revised:2005-05-28 Published:2005-05-28 Online:2005-05-28

摘要/Abstract

摘要： 制备超细Fe3O4颗粒,然后与还原铁粉混合烧结制成Fe3O4-Fe复合阳极,分别进行析氯电位、循环伏安和强化电解寿命等实验测试,优化该复合阳极的最佳烧结温度和最佳Fe含量,为实用型Fe3O4-Fe复合阳极的制作提供了可行性依据.

关键词: 四氧化三铁, 烧结, 析氯电位, 极化曲线, 循环伏安

Abstract: An ultrafine powder of magnetite has been prepared, and used to prepare the composite anode of Fe_(3)O_(4)-Fe by sintering method. The voltage of chlorine evolution、polarization curves、service life and mass loss, and the optimum sintering temperature and the weight ratio of the sintered powder have been investigated. All results showed that the method of preparing the practical Fe_(3)O_(4)-Fe composite uniform anode is feasible.

Key words: Sinter, Magnetite, Chlorine evolution voltage, Polarization curves

中图分类号:

TG174

熊信勇,范列朋,王茂华,郭琦龙,洪艳萍,黄长辉,吴佳林. 新型Fe_3O_4-Fe复合阳极的研制[J]. 电化学（中英文）, 2005, 11(2): 157-161.

XIONGXin-yong~. Study on the New Type Fe_3O_4 composite Anode[J]. Journal of Electrochemistry, 2005, 11(2): 157-161.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2005/V11/I2/157

参考文献

[1]　JiangHanxiang(蒋汉祥),WangShaonuo(王少娜),LiXueyao(李雪瑶),etal.Researchonthescarifical anodeFCofmagneticironoxide[J].Journalof ChongqingUniversity(NaturalScienceEdition),2002,25(4):141～143. [2]　DaLijun(达丽君).ThePrimaryDiscussionofaNew TypeAnodeMaterialsofFe3O4,CorrosionandAnodeMaterials[C].YiNan:YiHongPress,1984. [3]XiongXinyong(熊信勇),FanLiepeng(范列朋).A Methodofpreparingultrafinemagnetiteparticles[P].CN:200310103713.2,2003. [4]HuoChunguang(霍春光).Thechlorineevolutionvolt ageofmetalanode[J].Chlor AlkaliIndustry,1996,8:30～33. [5]SesigurH,AcmaE,AddemirO,etal.Thepreparation ofmagneticironoxide[J].MaterialsResearchBulle tin,1996,31(12):1573～1579. [6]MaZhenwei(马振伟),ZhangHongguo(张洪国),ZhouLi(周丽),etal.Investigationoflow temperature sinteringNi Zn Cuferriteswithultra highpermeability[J].FunctionalMaterials,2000,31(4):396～397. [7]XuXia(徐霞),YuanZhengying(袁正英),LuPeiwen(陆佩文).Effectofaddtivesonsinteringpropertiesof leadmetaniobate[J].JournalofNanjingUniversityof ChemicalTechnology,2000,22(6):31～33. [8]ZhuLinhua(祝琳华),LiaoXuepin(廖学品),Lang Xiaochuan(郎小川),etal.Theaffectionofsintering conditionstomechaniccharacterofphosphateceramic Ca1xBaxZr4(PO4)6[J].JournalofKunmingUniversity ofScienceandTechnology,2000,25(6):97～102. [9]SunZhaoqi(孙兆奇),LiAixia(李爱侠),XuZhiyuan(徐志元),etal.Sinteringconditionsandmicrostruc tureofAg MgF2cermet[J].FunctionalMaterials,2000,31(3):308～309. [10]TsuchidaT.Preparationofhighsurfacearea(r Al2O3)anditssurfaceproperties[J].Appl.Catal.,1993,105:141. [11]HuoChunguang(霍春光).Thechlorineevolution voltageofmetalanode[J].Chlor AlkaliIndustry,1996,8:30～33. [12]KroonDavidH.Cathodicprotectionanodesundergroud[J].MaterialsPerformance,1991,28(1):17.

[1]	王昊, 曹晓舟, 薛向欣. 锑在氯化胆碱-乙二醇低共熔溶剂中的电沉积研究[J]. 电化学（中英文）, 2022, 28(4): 2103071-.
[2]	蔡雪凡, 孙升. 多孔电极电池的循环伏安法模拟[J]. 电化学（中英文）, 2021, 27(6): 646-657.
[3]	邢逸飞, 李娜, 温晓芳, 韩宏彦, 崔敏, 张聪, 任聚杰, 籍雪平. 基于取代型多酸复合材料的多巴胺电化学检测[J]. 电化学（中英文）, 2020, 26(6): 890-899.
[4]	韩平, 冯海涛, 董亚萍, 田森, 张波, 李武. 氢氧化钠水溶液体系中金属铬的电化学氧化过程[J]. 电化学（中英文）, 2020, 26(3): 413-421.
[5]	郭佳瑶, 陈煅, 张杰, 詹东平. 法拉第吸脱附偶联过程循环伏安行为的有限元分析[J]. 电化学（中英文）, 2020, 26(2): 281-288.
[6]	李明雪, 史杭, 刘佳, 张檬, 周剑章, 吴德印, 田中群. 金电极上偶氮腺嘌呤的电化学行为研究[J]. 电化学（中英文）, 2019, 25(6): 651-659.
[7]	凌云, 汤儆, 刘国坤, 宗铖. 暂态电化学表面增强拉曼光谱研究对硝基苯硫酚分子的电化学还原过程[J]. 电化学（中英文）, 2019, 25(6): 731-739.
[8]	M. Rostom Ali, S Sankar Saha, Md Ziaur Rahman. 共晶基离子液体的钴电化学沉积[J]. 电化学（中英文）, 2018, 24(5): 546-554.
[9]	董鹏飞, 李娜, 赵海燕, 崔敏, 张聪, 任聚杰, 藉雪平. Keggin 型磷钨酸盐修饰碳糊电极传感多巴胺的研究[J]. 电化学（中英文）, 2018, 24(5): 555-562.
[10]	黄帅帅，刘诚，金磊，杨防祖，田中群，周绍民. 玻碳电极表面复合配位银电结晶机理研究[J]. 电化学（中英文）, 2018, 24(4): 344-350.
[11]	秦建新，林峰，刘文平，陈超，任孟德. 酸性溶液中Fe²⁺ /Fe³⁺相互转换对电极还原行为的影响[J]. 电化学（中英文）, 2017, 23(6): 702-707.
[12]	M. Rostom Ali, R. K. Biswas, Md. Golam Zakaria. 海沙钛铁矿在硫酸溶液中的电化学溶解研究[J]. 电化学（中英文）, 2017, 23(4): 420-428.
[13]	黄先杰，闫慧，黄帅帅，杨防祖，田中群，周绍民. 玻碳电极表面因瓦合金的电化学成核机理[J]. 电化学（中英文）, 2017, 23(1): 7-12.
[14]	郑艳洁，姚宏，翁少煌，彭花萍，龚仕文，黄莉，戴强，林新华. 硫酸特布他林在聚铬黑T修饰电极上的电化学行为及其测定[J]. 电化学（中英文）, 2016, 22(6): 617-623.
[15]	杨星，陈平*. 对磺酸基苯偶氮杯[4]芳烃电化学行为研究[J]. 电化学（中英文）, 2016, 22(1): 37-42.