羟基磷灰石涂层的电化学可控制备及生物性能的初步表征

电化学（中英文） ›› 2005, Vol. 11 ›› Issue (4): 440-445.

羟基磷灰石涂层的电化学可控制备及生物性能的初步表征

时海燕;胡仁;林昌健;

固体表面物理化学国家重点实验室厦门大学化学系,固体表面物理化学国家重点实验室厦门大学化学系,固体表面物理化学国家重点实验室厦门大学化学系福建厦门361005,福建厦门361005,福建厦门361005

收稿日期:2005-11-28 修回日期:2005-11-28 出版日期:2005-11-28 发布日期:2005-11-28

Electrochemical Controllable Preparation of Hydroxyapatite Coating with Different Morphologies and Preliminary in Vitro Tests

SHI Hai-yan,HU Ren,LIN Chang-jian~

(*)(State Key Laboratory for Physical Chemistry of Solid Surfaces,Department of Chemistry,Xiamen University,Xiamen 361005,China

Received:2005-11-28 Revised:2005-11-28 Published:2005-11-28 Online:2005-11-28

摘要/Abstract

摘要： 控制不同沉积条件制备不同结构形貌的羟基磷灰石涂层,主要获得3种由不同尺寸晶粒构成的直立状、花簇状和多孔状典型形貌特征的涂层;XRD物相分析显示,该涂层主要由结晶良好的羟基磷灰石组成;FT-IR组分分析未检测到其他钙磷盐成分的存在.体外细胞培养试验表明,以上各种形貌的羟基磷灰石涂层均具有良好的生物相容性,但其生物活性则因形貌而异,其中纳米有序多孔状羟基磷灰石涂层表现出最高的生物活性,而花簇状的涂层生物活性相对较低.

关键词: 羟基磷灰石涂层, 结构有序, 电化学沉积

Abstract: The Controllable electrochemical deposition has been developed to prepare the hydroxyapatite(HA) coatings on Ti substrate with different morphologies and structures.Three kinds of typical topography of HA coatings,i.e.standing-up,flower and ordered porous structures have been obtained.The XRD and FTIR results demonstrate high crystallinity of the coating and exclusion of other forms of calcium phosphates.In vitro tests reveal that the biological property is largely dependent on the structure and morphology of the HA coating.It has been found that all pure HA coating show good biocompatibilities,while only the HA coating with ordered porous structures exhibits best bioactivities.

Key words: HA coating, Different morphology, Electrochemical deposition, Bioproperty

中图分类号:

O627.51

时海燕;胡仁;林昌健;. 羟基磷灰石涂层的电化学可控制备及生物性能的初步表征[J]. 电化学（中英文）, 2005, 11(4): 440-445.

SHI Hai-yan,HU Ren,LIN Chang-jian~. Electrochemical Controllable Preparation of Hydroxyapatite Coating with Different Morphologies and Preliminary in Vitro Tests[J]. Journal of Electrochemistry, 2005, 11(4): 440-445.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2005/V11/I4/440

参考文献

[1]Them istoc leous GS,Katopod isH,Sourla A,Three-d i-m ensional typeⅠcollagen cell cu lture system s for thestudy of bone pathophysiology[J].In V ivo,2004(18)6:687-696. [2]Verdonk PCM,W ang J,A lmgvist KF,et al.Chondro-gen ic d ifferentiation of adu lt hum an bone m arrow derivedm esenchym al stem cell cu ltured on a collagen scaffold oras m icropellet[J].Annals of the Rheum atic D iseases2003(62)Supp l:129. [3]M ieno H,Kuroda K,Tajim a S.Bone morphogeneticprote in-m ed iated type II collagen expression in p i-lom atricom a and cutaneous m ixed tumor[J].Journalof Cutaneous Pathology 2005(32)3:206-211. [4]Feng QL,Cu i FZ,ZhangW,Nano-hydroxyapatite/col-lagen composite for bone repair[J].Acta Academ iaeM ed ic inae S in icae(Ch inese),2002,24:124. [5]Fe i Chen,Zhoucheng W ang,Changjian L in.Prepara-tion and characterization of nano-sized hydroxyapaititepartic les and hydroxyapatite/ch itosan nano-compositefor use in b iom ed icalm aterials[J].M ater.Lett,2002,57:858. [6]S.Ban,S.M aruno.E ffect of temperature on electro-chem ical deposition of calc ium phosphate coatings in asimu lated body flu id[J].B iom aterials,1995,16:977. [7]X ianghu iHou,X in L iu,Jianm in Xu,et al.A self-opti-m izing electrodeposition process for fabrication of calc i-um phosphate coatings[J].M ater.Lett.,2001(50):103-107. [8]Hu R,Sh iHY,L in CJ,et.al.The crystal growth behav-ior of hydroxyapatite coating on titan ium substrate underelectrochem ical deposition cond itions[J].Acta Physi-co-Ch im ica S in ica(Ch inese),2005(21)2:197-201. [9]L iu Rongfang,X iao X iufeng,Zuo Yousong,Study onelectrodeposited N i-HA composite coatings[J].M ate-rials Protection(Ch inese),2003,36(8):28-30. [10]Haob ing Hu,Changjian L in,Ren Hu,et al.A Studyon HH hubrid b ioceram ic coatings of HA/Poly(V inylAcetate)Co-deposited electrochem ically on Ti-6A l-4Valloy surface[J].M aterials Sc ience and EngineeringC,2002,20(1-2):209-214. [11]Chen Jida,W ang Yuan liang,Cai shaoxi,et al.Studyon preparation for nano-hydroxyapatite/collagen com-posite[J].Acta B iophysica S in ica(Ch inese),2001,17(4):778-785. [12]Redepenn ing,J.M cIssac,J P.E lectrocrystallization ofbrush ite coatings on prothetic alloys[J].Chem.M a-ter.,1990,2:625. [13]Kuo,M C.Yen,S K.The process of electrochem icaldeposited hydroxyapatite coatings on b iom ed ical titan i-um at room temperature[J].M aterials Sc ience andEngineering C,2002(20):153. [14]Huang L iye,Han Yong,Xu Kewe i,Experim entalstudy of fabrication of hydroxyapatite b iocoatings byelectrochem ical deposition and hydrotherm al synthesis[J].Journal of the Ch inese Ceram ic Soc iety(Ch i-nese),1998(26):87-91. [15]Sh irkhanzadeh,M.B ioactive calc ium phosphate coat-ings prepared by electrodeposition on titan ium and tita-n ium alloy[J].J.M ater.Sc i.Lett,1991(10):1 415-1 417. [16]Sh irkhanzadeh,M.Calc ium phosphate coatings pre-pared by electrocrystallization from aqueous electro-lytes[J].J.M ater.Sc i.M ater.M ed,1995(6):90-95. [17]Sh irkhanzadeh,M.E lectrochem ical Preparation of b io-active calc ium phosphate coatings on porous substratesby the period ic pu lse techn ique[J].M ater.Lett.,1993,12:16-19 [18]Sh irkhanzadeb.D irect form ation of nanophasehydroxyapatite on cathod ically polarized electrodes[J].Journal of M aterials Sc ience:M aterials inM ed ic ine 1998(9):67-72. [19]Hu Hao-b ing,L in Chang-jian,Chen Fe i,et al.PureHAP film prepared by d irect electrodepositing on m e-tallic surface and its m echan ism[J].E lectrochem istry(Ch inese),2002(8)3:288-294. [20]Montanaro L,Arc iola C R,Campocc ia D,et al,Invitro effects on MG63 osteob last-like cells follow ingcontactw ith two roughness-d iffering fluorohydroxy apa-tite-coated titan ium alloys,[J].B iom aterials,2002(23):3651-3659. [21]L iu Yanp ing,Rong L i,M eng X iangcai,et al.Observa-tion of surface u ltram icrostructure and quantitative a-nalysis of bone density in imp lant-bone interface aftersurface mod ification of titan ium imp lant[J].He i-longjiang M ed ic ine And Pharm acy(Ch inese),2000,2:2-5.