电化学（中英文） ›› 2009, Vol. 15 ›› Issue (2): 163-169. doi: 10.61558/2993-074X.1973

硅烷化学改性环氧涂层的耐蚀性能

刘倞;季卫刚;胡吉明;张鉴清;曹楚南;

浙江大学化学系;中国人民解放军第三军医大学化学教研室;中国科学院金属研究所金属腐蚀与防护国家重点实验室;

收稿日期:2009-05-28 修回日期:2009-05-28 出版日期:2009-05-28 发布日期:2009-05-28

Corrosion Performance of Epoxy Coatings by Chemical Modification with Silanes

LIU Liang1,JI Wei-gang1,2,HU Ji-ming1,ZHANG Jian-qing1,3,CAO Chu-nan1,3

(1.Department of Chemistry,Zhejiang University,Hangzhou 310027,China;2.Department of Chemistry,Third Military Medicine University,Chongqing 400038,China;3.State Key Laboratory for Corrosion and Protection,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China

Received:2009-05-28 Revised:2009-05-28 Published:2009-05-28 Online:2009-05-28

摘要/Abstract

摘要： 利用"活性"与"非活性"硅烷化学改性环氧涂层以提高其耐蚀性."活性"硅烷指含有可以与环氧树脂的环氧端基发生开环反应官能团的硅烷,通常为氨基硅烷;"非活性"硅烷指不与环氧端基发生反应,但在有机锡催化剂存在下可与环氧树脂骨架上的羟基发生缩合反应的硅烷.红外光谱显示,两类硅烷均可成功接枝在环氧树脂上.电化学阻抗谱(EIS)和加速腐蚀试验(Machu试验)测试表明,经硅烷化学改性后的环氧涂层均能提高其耐蚀性能.

关键词: 环氧涂层, 化学改性, 硅烷, 耐蚀性能

Abstract: The improvement of corrosion performance of epoxy coatings by modification with "active" and "non-active" silanes is presented."Active" silanes are defined as ones having functional groups that can react with the epoxy groups in the epoxy resin,usually amino-silanes."Non-active" silanes are defined as ones not reacting with the epoxy groups,but can react with the hydroxyl groups in the epoxy backbone by the condensation reactions under the catalysis of organic tin compounds.The FTIR results showed that both the "active" and "non-active" silanes had been successfully grafted onto the epoxy resin.Electrochemical impedance spectroscopy(EIS) and accelerated corrosion test(Machu test) showed that the corrosion performance of epoxy coatings could be improved by chemical modification with both the "active" and "non-active" silanes.

Key words: epoxy resin, chemical modification, silane, corrosion performance

中图分类号:

TB304

刘倞, 季卫刚, 胡吉明, 张鉴清, 曹楚南, . 硅烷化学改性环氧涂层的耐蚀性能[J]. 电化学（中英文）, 2009, 15(2): 163-169.

LIU Liang, JI Wei-gang, HU Ji-ming, ZHANG Jian-qing, CAO Chu-nan, . Corrosion Performance of Epoxy Coatings by Chemical Modification with Silanes[J]. Journal of Electrochemistry, 2009, 15(2): 163-169.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.1973

https://electrochem.xmu.edu.cn/CN/Y2009/V15/I2/163

参考文献

[1]Van Ooij W J,Zhu D,Stacy M,et al.Corrosion pro-tection properties of organofunctional silanes—An over-view[J].Tsinghua Science and Technology,2005,10:639-664. [2]Liu L(刘倞),Hu J M(胡吉明),Zhang J Q(张鉴清),et al.Progress in anti-corrosive treatment of met-als by silanization[J].Journal of Chinese Society forCorrosion and Protection,2006,26:59-64. [3]Subramanian V,van Ooij W J.Silane based metal pre-treatments as alternatives to chromating[J].SurfaceEngineering,1999,15:168-172. [4]Sundararajan G P,van Ooij W J.Silane based pretreat-ments for automotive steels[J].Surface Engineering,2000,16:315-320. [5]van Ooij W J,Zhu D Q,Prasad G,et al.Silane basedchromate replacements for corrosion control,paint adhe-sion,and rubber bonding[J].Surface Engineering,2000,16:386-396. [6]Seth A,van Ooij W J.Novel,water-based high-per-formance primers that can replace metal pretreatmentsand chromate-containing primers[J].Journal of Mate-rials Engineering and Performance,2004,13:468-474. [7]Seth A,van Ooij W J,Puomi P,et al.Novel,one-step,chromate-free coatings containing anticorrosionpigments for metals—An overviewand mechanistic study[J].Progress in Organic Coatings,2007,58:136-145. [8]Ji W G,Hu J M,Zhang J Q,et al.Reducing the waterabsorption in epoxy coatings by silane monomer incorpo-ration[J].Corrosion Science,2006,48:3731-3739. [9]Zhu D,van Ooij W J.Corrosion protection of metals bywater-based silane mixtures of bis-[trimethoxysilylprop-yl]amine and vinyltriacetoxysilane[J].Progress in Or-ganic Coatings,2004,49:42-53. [10]Ji W G,Hu J M,Liu L,et al.Water uptake of epoxycoatings modified withγ-APS silane monomer[J].Progress in Organic Coatings,2006,51:439-443. [11]Zhang J T,Hu J M,Zhang J Q,et al.Studies of wa-ter transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS[J].Progress inOrganic Coatings,2004,51:145-151. [12]Ji W G,Hu J M,Liu L,et al.Improving the corro-sion performance of epoxy coatings by chemical modifi-cation with silane monomers[J].Surface&CoatingsTechnology,2007,201:4789-4795. [13]Zhou J M,Lucas J P.Hygrothermal effects of epoxyresin.Part II:variations of glass transition temperature[J].Polymer,1999,40:5513-5522. [14]Fellahi S,Chikhi N,Bakar M.Modification of epoxyresin with kaolin as a toughening agent[J].Journal ofApplied Polymer Science,2001,82:861-878. [15]Tejedor MI,Raredes L,Anderson MA.Evaluation ofATR-FTIR spectroscopy as an“in situ”tool for follow-ing the hydrolysis and condensation of alkoxysilanesunder rich H2O conditions[J].Chemistry of Materi-als,1998,10:3410-3421. [16]Ji W G,Hu J M,Liu L,et al.Enhancement of corro-sion performance of epoxy coatings by chemical modifi-cation with GPTMS silane monomer[J].Journal ofAdhesion Science and Technology,2008,22:77-92. [17]van Ooij W J,Zhu D.Electrochemical impedancespectroscopy of bis-[triethoxysilylpropyl]tetrasulfide onAl 2024-T3 substrates[J].Corrosion,2001,57:413-427.

硅烷化学改性环氧涂层的耐蚀性能

Corrosion Performance of Epoxy Coatings by Chemical Modification with Silanes

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 8

Metrics

[1]	李相波, 许立坤, 邱善广, 王佳, 黄国胜, 董彩常. 碳钢低压冷喷涂铝涂层的海水耐蚀性[J]. 电化学（中英文）, 2013, 19(5): 425-429.
[2]	张洁, 王久林, 杨军. 锂离子电池用富锂正极材料的研究进展[J]. 电化学（中英文）, 2013, 19(3): 215-224.
[3]	苗伟俊, 张余宝, 古宁宇, 刘峰. 表面硅烷化铜箔的电化学腐蚀与防护研究[J]. 电化学（中英文）, 2012, 18(4): 359-364.
[4]	李莉莉, 王炜. 巯基改性棉纤维化学镀银导电布的研究[J]. 电化学（中英文）, 2011, 17(2): 222-226.
[5]	管勇, 刘建国, 严川伟, . 电镀锌钢硅烷-有机膦酸复合钝化膜的制备及性能表征[J]. 电化学（中英文）, 2010, 16(4): 378-384.
[6]	管勇, 刘建国, 严川伟, . 电镀锌钛/锆基无铬化学转化膜的制备与耐蚀性能[J]. 电化学（中英文）, 2010, 16(4): 373-377.
[7]	黄令,林克发,杨防祖,许书楷,周绍民. 铜电极表面硅烷膜的自组装及其性能研究[J]. 电化学（中英文）, 2005, 11(2): 188-192.
[8]	白霞, 孙冬柏, 俞宏英, 孟惠明, 李辉勤, 樊自拴. 铁铬合金空蚀过程的研究[J]. 电化学（中英文）, 2003, 9(1): 54-59.