丝束电极研究裂纹对混凝土中钢筋腐蚀的影响

电化学（中英文） ›› 2006, Vol. 12 ›› Issue (2): 191-194.

丝束电极研究裂纹对混凝土中钢筋腐蚀的影响

李国希;胡金丰;朱日龙;杜艳娜;

湖南大学化学化工学院,湖南大学化学化工学院,湖南大学化学化工学院,湖南大学化学化工学院湖南长沙410082,湖南长沙410082,湖南长沙410082,湖南长沙410082

收稿日期:2006-05-28 修回日期:2006-05-28 出版日期:2006-05-28 发布日期:2006-05-28

Effect of Cracks on Corrosion of Rebar in Concrete Studied by Wire Beam Electrode

LI Guo-xi~

(*),HU Jin-feng,ZHU Ri-long,DU Yan-na(College of Chemistry and Chemical Engineering,Hunan University,Changsha 410082,Hunan,China

Received:2006-05-28 Revised:2006-05-28 Published:2006-05-28 Online:2006-05-28

摘要/Abstract

摘要： 应用丝束电极技术测量浸在10%NaC l溶液中的混凝土内铁丝束的自腐蚀电位和极化电阻分布,研究裂纹对混凝土中铁丝腐蚀的影响和乙醇胺的缓蚀作用.结果表明,裂纹加速了水、氧和氯离子向两侧混凝土中扩散,增加了铁丝腐蚀的不均匀性.乙醇胺扩散到混凝土中,吸附在铁丝表面,基本不改变铁丝的自腐蚀电位,但显著降低了铁丝腐蚀速率,有效抑制了裂纹引起的不均匀腐蚀.

关键词: 混凝土, 钢筋, 腐蚀, 丝束电极, 裂纹, 乙醇胺

Abstract: The effects of crack and ethanolamine on corrosion of rebar in concrete were studied by measuring the distribution of corrosion potential and polarization resistance of iron wires in 10% NaCl solution.The results showed that the diffusion of water,oxygen and chloric ion toward concrete was accelerated by the crack which intensified the nonuniform corrosion of iron wire with the regions near to crack as anode and the uncracked regions as cathode.Ethanolamine could diffuse into the body of concrete and absorb on the surface of iron wire,which reduced iron corrosion evidently and successfully inhibited the nonuniform corrosion caused by crack without changing the corrosion potential.

Key words: Concrete, Rebar, Corrosion, Wire-beam electrode

中图分类号:

TU375

李国希;胡金丰;朱日龙;杜艳娜;. 丝束电极研究裂纹对混凝土中钢筋腐蚀的影响[J]. 电化学（中英文）, 2006, 12(2): 191-194.

LI Guo-xi~. Effect of Cracks on Corrosion of Rebar in Concrete Studied by Wire Beam Electrode[J]. Journal of Electrochemistry, 2006, 12(2): 191-194.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2006/V12/I2/191

参考文献

[1]Mohamm ed T U,O tsuk i N,H isada M,et al.E ffect ofcrack w idth and bar types on corrosion of steel in con-crete[J].Journal of M aterials in C ivil Engineering,2001,13:194~201. [2]Ryu J,O tsuk i N.App lication of electrochem ical tech-n iques for the control of cracks and steel corrosion inconcrete[J].Journal of App lied E lectrochem istry,2002,32:635~639. [3]Mohamm ed T U,O tsuk i N.Corrosion of steel bars incracked concrete underm arine environm ent[J].Journalof M aterials in C ivil Engineering,2003,15:460~469. [4]Tan Y.W ire beam electrode:a new tool for studying lo-calized corrosion and other heterogeneous electrochem i-cal processes[J].Corrosion Sc ience,1999,41:229~247. [5]Hu R Z(胡荣宗),L in C J(林昌健),Zhou X(周香),et al.An investigation on the corrosion potentialim aging at the interface of concrete/re inforc ing bar incorrosion m ed ia[J].E lectrochem istry(in Ch inese),2000,6:227~232. [6]L in C J(林昌健),Zhou X D(卓向东),Chen J D(陈纪东).Corrosion potential im aging at interface ofpolym eric coating/m etal by array electrode techn ique[J].Journal of Ch inese Soc iety for Corrosion and Pro-tection,1997,17:7~11. [7]Hu J F(胡金丰),L i G X(李国希),Deng K(邓凯),et al.Study on non-un iform corrosion of rebar em-bedded in concrete by w ire-beam electrode[J].Journalof Ch inese soc iety for corrosion and protection,2005,25:88~92. [8]Hu J F(胡金丰).Study on corrosion ofRebar Embed-ded in concret by w ire beam E lectrode[D].Changsha:Hunan Un iversity,2004. [9]E lsener B,Buchler M,Stalder F.M igrating corrosioninh ib itor b lend for re inforced concrete:part 1?preven-tion of corrosion[J].Corrosion Sc ience,1999,55:1155~1163. [10]W ang Y(汪鹰),He P(何平),Sh iY X(史苑芗),etal.The corrosion inh ib ition effect and m echan ism of in-h ib itors for rebar studed by A C impedance[J].Journalof Nan jing Un iversity of Chem ical Technology,1998,20:53~57.

[1]	秦凯旋, 常鹏飞, 黄钰林, 李明, 杭弢. 钴互连化学机械抛光浆料中的界面腐蚀行为研究[J]. 电化学（中英文）, 2022, 28(6): 2104471-.
[2]	杨森, 王文昌, 张然, 秦水平, 吴敏娴, 光崎尚利, 陈智栋. 醇硫基丙烷磺酸钠对电解高性能锂电铜箔的影响[J]. 电化学（中英文）, 2022, 28(6): 2104501-.
[3]	张涛, 刘一蒲, 叶齐通, 范红金. 工业级碱性海水电解:近期进展和展望[J]. 电化学（中英文）, 2022, 28(10): 2214006-.
[4]	况先银, 金少强, 曹艳辉, 张艳梅, 董士刚, 朱龙晖, 林理文, 林昌健. 铝合金表面改性对有机涂层附着力的影响及腐蚀防护性能研究[J]. 电化学（中英文）, 2021, 27(6): 624-636.
[5]	邹振文, 郑大江, 王子明, 宋光铃. 新型单丝电极交流探头在3.5wt.% NaCl中的电化学响应规律研究[J]. 电化学（中英文）, 2020, 26(3): 317-327.
[6]	张翅, 李成飞, 李高仁. 负载于刻蚀镍泡沫上钯纳米粒子作为乙醇氧化高性能电催化剂[J]. 电化学（中英文）, 2019, 25(5): 571-578.
[7]	赫威，燕汝，王瑛琦，高翔，马厚义. 在冷轧钢板表面制备二乙烯三胺五甲叉膦酸-锌化学转化膜及其腐蚀防护性能的研究[J]. 电化学（中英文）, 2018, 24(2): 111-121.
[8]	H. A. Fetouh, B.A. Abd-El-Nabey, Y.M. Goher, M. S. Karam. 银纳米颗粒对铝金属在酸性介质中的耐蚀性能研究[J]. 电化学（中英文）, 2018, 24(1): 89-100.
[9]	陈晓航，陈寞静，闵宇霖，徐群杰. 水热法制备铝合金超疏水表面及电化学性能研究[J]. 电化学（中英文）, 2018, 24(1): 28-35.
[10]	徐天宇，王世颖，王文昌，陈智栋. 镍离子对中磷镍基体氯化胆碱无氰浸金表面的改善[J]. 电化学（中英文）, 2018, 24(1): 36-39.
[11]	杨莉，徐兵，王海，董泽华. 适用于钢筋混凝土腐蚀监测的长效MnO₂参比电极的研制[J]. 电化学（中英文）, 2017, 23(1): 36-44.
[12]	王静静，董士刚，张小娟，吕虹玮，伍运昌，杜荣归，林昌健. pH/Cl^-复合探针技术对钢筋混凝土电化学除氯的原位检测[J]. 电化学（中英文）, 2014, 20(2): 95-100.
[13]	叶陈清，胡融刚，侯瑞青，王小平，杜荣归，林昌健*. 敏化处理304不锈钢局部腐蚀行为的扫描微电极法研究[J]. 电化学（中英文）, 2013, 19(6): 507-511.
[14]	曹发和, 夏妍, 刘文娟, 常林荣, 张鉴清. SECM基本原理及其在金属腐蚀中的应用[J]. 电化学（中英文）, 2013, 19(5): 393-401.
[15]	李凌杰, 贺毓玲, 雷惊雷, 张胜涛. 椭圆偏振光谱技术的腐蚀研究应用[J]. 电化学（中英文）, 2013, 19(5): 402-408.