关键词: 铝合金, 薄电解液层, 电位波动, 点蚀

Abstract: Lens tissues adsorbing 3.5% sodium chloride solution were used to simulate thin electrolyte layers. The 7075 aluminum alloy was immersed under the thin electrolyte layers for 0, 4, 6, 8 and 12 h respectively. Then the fluctuations of natural-corrosion potentials of the alloy were monitored. The fluctuations of natural-corrosion potential were observed rather small in the initial corrosion stages after 6h immersion, and the positive peaks of potential appeared. However the amplitudes reached 20mV after 4h and 12h immersion. The RMS of natural-corrosion potentials decreased with corrosion time at first and then increased. It reached a minimum at 4 h. The k value (slope of linear part) was rather high at 6h. Thus it can conclude from above that the initiation of pitting happened after 6h corrosion.