镍合金在含硫代硫酸根离子之氯化钠水溶液中的孔蚀研究

电化学（中英文） ›› 1999, Vol. 5 ›› Issue (1): 18-24.

镍合金在含硫代硫酸根离子之氯化钠水溶液中的孔蚀研究

李永发,王廷玉,蔡文达

成功大学材料科学及工程学系

收稿日期:1999-02-28 修回日期:1999-02-28 出版日期:1999-02-28 发布日期:1999-02-28

Pitting Corrosion of Ni_Based Alloy in Thiosulfate_ion Containing Chloride Solutions

Lee Yungfa Wang Tingyu Tsai Wenta *

(Dept. of Materials Sci. and Engin.,Cheng kung Univ.,Tainan

Received:1999-02-28 Revised:1999-02-28 Published:1999-02-28 Online:1999-02-28

摘要/Abstract

摘要： 本文研究硫代硫酸根离子对镍基６９０合金在氯化钠水溶液中之孔蚀行为．发现在单纯硫代硫酸钠水溶液中，镍基６９０合金不发生孔蚀．在氯化钠水溶液中，当添加的硫代硫酸根离子浓度低时，会增进孔蚀的敏感性；当硫代硫酸根离子浓度高时，则反而抑制孔蚀．

关键词: 孔蚀, 镍基690合金, 氯化钠水溶液, 硫代硫酸根离子

Abstract: The effect of thiosulfate ion on the pitting corrosion behavior of Ni_Based Alloy 690 in chloride solution was investigated.In plain sodium thiosulfate solution,Alloy 690 was immune to pitting corrosion. However, the addition of low concentration of sodium thiosulfate can enhance the initiation of pitting corrosion of Alloy 690. Nevertheless, inhibition of pitting corrosion was observed at high concentration of addition.

Key words: Pitting corrosion, Alloy 690, Chloride solution, Thiosulfate ion

中图分类号:

TG172.5

李永发,王廷玉,蔡文达. 镍合金在含硫代硫酸根离子之氯化钠水溶液中的孔蚀研究[J]. 电化学（中英文）, 1999, 5(1): 18-24.

Lee Yungfa Wang Tingyu Tsai Wenta * . Pitting Corrosion of Ni_Based Alloy in Thiosulfate_ion Containing Chloride Solutions[J]. Journal of Electrochemistry, 1999, 5(1): 18-24.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y1999/V5/I1/18

[1]	李杰, 牛焱, 宋诗哲. Cu-Ni合金在NaCl溶液中的孔蚀特性[J]. 电化学（中英文）, 2003, 9(4): 422-427.
[2]	唐聿明, 左禹. 碳钢在NaNO_2-NaCl溶液中的电流波动[J]. 电化学（中英文）, 2003, 9(4): 464-470.
[3]	梁成浩,隋洪艳. 人工体液中TiNiCu形状记忆合金的电化学行为[J]. 电化学（中英文）, 2001, 7(2): 210-214.
[4]	杨勇,储炜,南俊民,陈旭光,林祖赓. 实用电极材料体系的共焦显微拉曼光谱研究(英文)[J]. 电化学（中英文）, 2001, 7(1): 30-36.
[5]	刘宏义,李汝桐,蔡文达,谢荣渊,潘永村. 合金元素及模拟热处理对2205双相不锈钢之孔蚀性质影响[J]. 电化学（中英文）, 1999, 5(2): 130-139.