本文以Al和10%体积比Al2O3的混合粉末为原料，使用便携式低压冷喷涂设备，在Q235碳钢基体上喷涂了Al涂层. 测试涂层自腐蚀电位及动电位极化曲线，结合扫描电镜观察涂层表面及截面微观形貌，研究了低压冷喷涂Al涂层在海水中电化学腐蚀行为，并与高压冷喷涂和热喷涂铝涂层的耐蚀性比较. 结果表明，低压冷喷涂铝涂层结构较为致密，其耐蚀性比高压冷喷涂铝涂层的略低，而明显优于热喷涂铝涂层.
李相波
,
许立坤
,
邱善广
,
王佳
,
黄国胜
,
董彩常
. 碳钢低压冷喷涂铝涂层的海水耐蚀性[J]. 电化学, 2013
, 19(5)
: 425
-429
.
DOI: 10.61558/2993-074X.2130
Taking aluminium (Al) powder mixed with 10% (by volume) of Al2O3 powder as raw materials, the Al coating was prepared on the Q235 carbon steel substrate using a portable low pressure cold spraying equipment. Through the measurements of the corrosion potential and potentiodynamic polarization, the electrochemical corrosion behavior of the low pressure cold sprayed Al coating in seawater was studied in comparison with those of the Al coatings deposited with high pressure cold spray and thermal spray processes. At the same time, the surface and cross-section morphologies of these coatings were observed with scanning electron microscope. The results showed that the corrosion resistance of the low-pressure cold spraying Al coating, which is compact, is lower than that of the high pressure cold sprayed Al coating, while much higher than that of the thermally sprayed Al coating.
[1] Dykhuizen R C, Smith M F. Gas dynamic principles of cold spray[J]. Journal of Thermal Spray Technology, 1998, 7(2): 205-212.
[2] Dong C C(董彩常), Wang H R(王洪仁), Huang G S(黄国胜), et al. Corrosion behavior of cold-sprayed aluminum coating in seawater[J]. Corrosion Science and Protection Technology(腐蚀科学与防护技术), 2010, 22(2): 90-93.
[3] Dzhurinskiy D, Maeva E, Leshchynsky V, et al. Corrosion protection of light alloys by cold spray[C]. Villafuerte V, DoD Corrosion Conference. Centerline (Windsor) Ltd Windsor, ON, Canada: University of Windsor, 2009.
[4] Djordjevic B B, Maev R G. Application for aerospace corrosion protection and structural repair, building on 100 years success: Proceedings of the 2006 International Thermal Spray Conference[C]. Marple B R ，Hyland M M, Lau Y C, et al. May 15-18, 2006 (Seattle, Washington, USA), ASM International, 2006.
[5] hkodkin A, Kashirin A, Klyuev O, et al. The basic principles of DYMET technology, building on 100 Years success: Proceedings of the 2006 international thermal spray conference[C]. Marple B R, Hyland M M, Lau Y C, et al. May 15-18, 2006 (Seattle, Washington, USA), ASM International, 2006.
[6] Koivuluoto H, Vuoristo P. Effect of powder type and compositionon structure and mechanical propertiesof Cu + Al2O3 coatings prepared by using low-pressure cold spray process[J]. Journal of Thermal Spray Technology, 2010, 19: 1081-1092.
[7] Koivuluoto H, Lagerbom J, Kylmalahti M, et al. Microstructure and mechanical properties of low-pressure cold-sprayed (LPCS) coatings[J]. Journal of Thermal Spray Technology, 2008, 17(5/6): 721-727.
[8] Liu C(刘存), Zhao W M(赵为民), Al H(艾华), et al. Electrochemical corrosion behaviors of arc-sprayed aluminium coating[J]. Journal of Chinese Society for Corrosion and Protection(中国腐蚀与防护学报), 2011, 31(1): 62-66.