Surface Enhanced Raman Spectroscopic study of SCN - adsorbed at the Copper and Gold Nanowire Arrays

  • Yao Jianlin a ,
  • Pan Guoping b ,
  • Xue Kuanhong b ,
  • Xie Yong a ,
  • Tang Jing a ,
  • Ren Bin a
Expand
  • ( a State Key Lab. for Phys. Chem. of Solid Surfaces, Dept. of Chem., Xiamen Univ., Xiamen 361005

Received date: 1999-11-28

  Revised date: 1999-11-28

  Online published: 1999-11-28

本文引用格式

姚建林 , 潘谷平 , 薛宽宏 , 谢泳 , 汤儆 , 任斌 . 铜和金纳米线阵列上SCN-的表面增强拉曼光谱[J]. 电化学, 1999 , 5(4) : 371 -376 . DOI: 10.61558/2993-074X.1364

Abstract

Two_dimensional arrays of Cu and Au nanowires have been fabricated by template synthesis method, using the anodic aluminum oxidation films as the template. The morphology of the nanowire array was monitored by atomic force microscope (AFM) in the dissolution processes of the alumina film. Based on the probe molecule strategy, the spectral feature of SCN - adsorbed at the Cu and Au nanowires with different diameters has been investigated by surface enhanced Raman spectroscopy (SERS). The results reveal that the intensity of the SERS bands depends on the length of the exposed nanowires. The C≡N stretching vibration frequency (ν CN ) of SCN - up_shifted significantly with the increase of the diameter of the nanowires in the range of 15 nm to 50 nm. This interesting phenomenon is briefly discussed.

参考文献

1  Preston CKand Moskovits M.Opticalcharacterization ofanodic aluminum oxidefilmscontaining electrochemically deposited metal particles. 1. Gold in phosphoric acid anodic aluminum oxide films.J. Phys. Chem .,1993 ,97 :8 495 2  Hulteen JCand Martin CR,in Nanoparticles and Nanostructured Films,Fendler JH(Ed.) .Weinheim : Wiley_VCH,1998 ,Chapter 10 3  Link S, Wang ZL,El_Sayed M A.Alloyformation of gold_silver nanoparticlesand the dependence ofthe plasmon absorption on theircomposition.J.Phys.Chem .B1999 ,103 :3 529 4  Li BB,Yu DP,Zhang SL.Raman spectralstudy ofsilicon nanowires.Phys.Rev .B1999 ,59 :1 645 5  Foss CA,GaborJ,Hornyak Letal.Template_synthesized nanoscopic gold particles:opticalspectraand theeffectsof particlesize and shape.J.Phys.Chem .,1994 ,98 :2 963 6  Al_Rawashdeh,Sandrock M L,Seudling CJetal. Visible region polarization spectroscopic studies oftemplate_synthesized gold nanoparticles orientedin polyethylene.J.Phys.Chem .B1998 ,102 :361 7  Preston CKand Moskovits M. New technique for the determination of metal particle size in supported metalcatalysis.J.Phys.Chem .1988 ,92 :2 957 8  Routkevitch D, Haslett TL,Ryan L,etal.Synthesis andresonance Raman spectroscopy of CdSnano_wirearrays.Chem .Phys.,1996 ,210 :343 9  Suh JSand Lee JS.Surface enhanced Raman scatteringfor CdSnanowires depositedin anodic aluminum oxidenanotemplate.Chem .Phys.Lett.,1997 ,281 :384 10 Weitz DA,Gramila TJ, Genack AZ,etal. Anomalouslow_frequency Raman Scattering from rough metalsurface and the origin ofsurface_enhanced Raman scattering.Phys. Rev.Lett.,1980,45 :355 11 Shingubara S, Okino O, Sayama Y, et al. Ordered two_dimensional array formation using self_organizednanoholesofanodically oxidized aluminum .Jpn.J.App.Phys.,1997 ,36 :7 791 12  Tian ZQ,GaoJS,Li XQ,etal.Can Ramanspectroscopy becomea generaltechniqueforsurfacescience andelectrochemistry.J.Raman Spectrosc.,1998 ,29 :703 13 Moskovits M.Surface_enhanced Raman spectroscopy.Rev . Mod.Phys.,1985 ,57 :783 14 Otto A, Mrozek I, Grabhorn H,et al. Surface_enhanced Raman scattering.J. Phys. Condens. Matter,1992 ,4 :1 143 15 Gersten JI,The effectofsurface roughnesson surface enhanced Raman scattering.J.Chem .Phys.,1980 ,72(10):5 779