应用sol gel法制备纳米α Fe2O3、TiO2及α Fe2O3 TiO2粉体,并以其作前驱体制得该纳米微粒与海藻酸钠的复合膜.由红外光谱(FT IR)、X 射线粉末衍射(XRD)、荧光光谱(PL)、透射电子显微镜(TEM)和循环伏安(I V)等物理化学方法表征、测定各复合薄膜的表面结构与催化活性.紫外 可见吸光光度法等研究结果表明,以杀菌紫外灯作光源,在纳米Fe2O3、TiO2及α Fe2O3 TiO2与海藻酸钠的复合膜悬浮液中,亚甲基蓝可被快速脱色降解,若于α Fe2O3中加入15%的TiO2,其α Fe2O3 TiO2复合晶体比单一的α Fe2O3或TiO2具有更高的光降解活性.
陈力勤
,
钟淮真
,
陈日耀
,
郑曦
,
陈震
. α-Fe_2O_3-TiO_2/SA复合半导体薄膜的制备及光催化性能的研究[J]. 电化学, 2004
, 10(4)
: 452
-459
.
DOI: 10.61558/2993-074X.1601
Three new nano thin films of α-Fe_2O_(3)、TiO_2 and α-Fe_2O_(3)-TiO_2 by doping their powder with sodium alginate polymer were prepared. Surface structure and catalytic activities of the films were characterized by FTIR、XRD、PL、TEM and I-V techniques. The results of UV-visible absorption showed that the methylene blue was mineralized in aqueous of α-Fe_2O_(3)/SA、TiO_2/SA and (α-(Fe_2O_(3)))-TiO_2 /SA upon radiation with ultra violet light. α-Fe_2O_(3) enhanced their photo-decolorized-activities by doping 15% TiO_2.
[1]HengleinA.Small particleresearch:physicochemicalpropertiesofextremelysmallcolloidalmetalandsemiconductorparticles[J].Chem.Rev.,1989,89:1861～1873.
[2]VogelR,HoyerP,WellerH.Quantum sizedPbS,CdS,Ag2S,Sb2S3andBi2S3particlesassensitizersforvariousnanoporouswide bandgapsemiconductors[J].J.Phys.Chem.,1994,98(12):3183～3188.
[3]DhananjeyanMR,MielczarskiE,ThampiKR,etal.PhotodynamicsandsurfacecharacterizationofTiO2andFe2O3photocatalystsimmobilizedonmodifiedpolyethylenefilms[J].J.Phys.Chem.B,2001,105:12046～12055.
[4]BedjaI,KamatPV.CappedsemiconductorcolloidssynthesisandphotoelectrochemicalbehaviorofTiO2cappedSnO2nanocrystallites[J].J.Phys.Chem.,1995,99(22):9182～9188.
[5]LakatosB,KoreczL,GeodermaM.Comparativestudyonthemoessbauerparametersofironhumatesandpolyuronates[J].Eur.Polym.J,1977,19:149～152.
[6] StramelRD,ThomasJK.Photochemistryofironoxidecolloids[J].J.ColloidandInterfaceScience,1986,110(1):121～129.
[7]SabateJ,AndersonMA,KikawaH,etal.AKineticstudyofthephotocatalyticdegradationof3 chlorosalicylicacidoverTiO2membranessupportedonglass[J].J.Catal.,1991,127:167～177.
[8]SoriaJ,ConesaJC,AugugliaroV,etal.Dinitrogenphotoreductiontoammoniaovertitaniumdioxidepowdersdopedwithferricions[J].J.Phys.Chem.,1991,95(1):274～282.
[9] ChenFeili,WangLiangyan,YangBaoshan.StudyonphotocatalyticdecompositionoforganicmicropollutantsindrinkingwaterusingreactorwithTiO2filmcoatingongrasstubesurface[J].ActaEnergiaeSolarisSinica,1999,20(4):471～475.
[10] SpurrRA,MyersH.Quantitativeanalysisofanatase rutilemixtureswithanx raydiffractometers[J].Anal.Chem.,1957,29:760～762.
[11] GaoWei,WuFeng qing,LuoZhen,etal.Studiesontherelationshipbetweenthecrystalformofanditsphotocatalyzingdegradationefficiency[J].ChemicalJournalofChineseUniversities,2001,22(4):660～662.
[12] BickleyR,Gonzalea CarrenoT,LeesJ.Preparationandcharacterizationofsometernarytitaniumoxidephotocatalysts[J].J.SolidStateChem.,1991,92:178～190.
[13] GadsdenJA.InfraredSpectraofMineralsandRelatedInorganicCompounds[M].USA:R.J.AcfordLtd,1975,45～48.
[14] FrankSN,BardAJ.Heterogeneousphotocatalyticoxidationofcyanideandsulfiteinaqueoussolutionsatsemiconductorpowders[J].J.Phys.Chem.,1977,81(15):1484～1488.
[15] FujishimaS,Writing,ChenZhen,YaoJian nian,Translation.ElectrochemDetermMethods[M].Beijing:BeijingUniv.PublishSociety,1995,356.
[16] CuiXiao li,JiangZhi yu.ElectrochemicalbehaviorofITO/TiO2electrodeunderUvillumination[J].ActaPhys.Chim.Sin.,2002,18(11):1014～1017.
[17] SpadaroJT,IsabelleL,RanganathanV.Hydroxylredicalmeduateddegradationofazodyesevidenceforbenzenegeneration[J].Environ.Sci.Technol.,1994,28:1389.
[18] FaustBC,HoffmannRH,BahnemannDW.Photocatalyticoxidationofsulfurdioxideinaqueoussuspensionsofα Fe2O3[J].J.Phys.Chem.,1989,93(17):6371～6381.
[19] TurnerJE,HendewerkM,ParmeterJ,etal.Thecharacterizationofdopedironoxideelectrodesforthephotodissociationofwater[J].J.Electrochem.Soc.,1984,131(8):1777～1783.