应用溶胶凝胶法制备不同焙烧温度的氧化物阳极涂层,SEM,EDX,XRD、强化电解寿命、循环伏安和电化学阻抗等测试表明,烧结温度对阳极涂层的表面形貌以及电化学性能有着很大的影响.随着烧结温度的升高,析氯电位相应增加,寿命相对较长,循环伏安电量与双电层电容值有所下降.
嵇雷
,
王均涛
,
许立坤
,
刘文彬
,
薛桂林
. 烧结温度对Ru-Ir-Sn氧化物阳极涂层性能的影响[J]. 电化学, 2008
, 14(2)
: 205
-209
.
DOI: 10.61558/2993-074X.1892
The anode coatings of Ru-Ir-Sn oxide were prepared by sol-gel method with different annealed temperatures.The influences of annealed temperature in properties of anode coatings were characterized by scanning electron microscope(SEM),energy dispersive X-ray detector(EDX),X-ray diffraction(XRD),potential of chlorine evolution,accelerated life,cyclic voltammetry and electrochemical impedance spectroscopy(EIS) tests.The results showed that the annealed temperature affected the morphology of coatings,while the electric quantities of cyclic voltammetry and double layer capacitances of anode coatings had a tendency to fall down and the potential of chlorine evolution and accelerated life had a tendency to increase as the annealed temperature increased.
[1]Beer H B.Electrochemical properties of mixed metaloxide coated titanuim anodes in sea water:U S,3711385[P].1973.
[2]Pilla A S.Evaluation of anode deactivation in chlor-al-kali cells[J].J Appl Electrochemical,1997,27:1283.
[3]Wang TY,Xu L K,Chen G Z.Electrochemical prop-erties of mixed metal oxide coated titanium anodes insea water[J].Electrochemical,2002,8(2):172-175.
[4]Wang X,Tang D,Zhou J G.Microstructure,mophologyand electrochemical property of RuO270SnO230mol%and RuO230SnO270mol%coatings[J].Alloys andCompounds,2007,(430):60-66.
[5]Ailton J Terezo,Ernesto C Pereira.Preparation andcharacterisation of Ti/RuO2anodes obtained by sol-geland conventional routes[J].Materials Letters,2001,339-345.
[6]Panic V,Dekanski A,Wang G,et al.Morphology ofRuO2-TiO2coatings and TEM characterization of oxidesols used for their preparation[J].Journal of Colloidand Interface Science,2003,263:68-73.
[7]Panic V,Dekanski A,Milonjic S,etal.The influenceof the aging time of RuO2and TiO2sols on the electro-chemical properties and behavior for the chlorine evolu-tion reaction of activated titanium anodes obtained bythe sol-gel procedure[J].Electrochimica Acta,2000,46:415-421.
[8]Panic V V,Dekanski A,Milonjic S K,et al.RuO2-TiO2coated titanium anodes obtained by the sol-gel pro-cedure and their electrochemical behaviour in the chlo-rine evolution reaction[J].Colloids and Surfaces,1999,57:269-274.
[9]Mattos-Costa F I,Lima-Neto P de.Machado S A S,etal.Characterization of surfaces modified by sol-gel de-rived RuxIr1-xO2coatings for oxygen evolu-tion in acidmedium[J].Electrochimica Acta,1998,44:1515-1523.
[10]Trasatti S.Physical electrochemistry of ceramic oxide[J].Electrochim Acta,1991,36(2):225.
[11]Xu L K,Scantlebury J D.A study on the deactivationof an IrO2Ta2O5coated titanium anode[J].CrossionScience,2003,45:2735.
[12]Kerner Z,Pajkossy T.On the origin of capacitancedispersion of rough electrodes[J].Electrochimica Ac-ta,2000,46:207.