烧结温度对Ru-Ir-Sn氧化物阳极涂层性能的影响

doi:10.61558/2993-074X.1892

电化学（中英文） ›› 2008, Vol. 14 ›› Issue (2): 205-209. doi: 10.61558/2993-074X.1892

烧结温度对Ru-Ir-Sn氧化物阳极涂层性能的影响

嵇雷;王均涛;许立坤;刘文彬;薛桂林;

哈尔滨工程大学材料科学与化学工程学院,海洋腐蚀与防护国家重点实验室中船重工725所青岛分部,海洋腐蚀与防护国家重点实验室中船重工725所青岛分部,哈尔滨工程大学材料科学与化学工程学院,哈尔滨工程大学材料科学与化学工程学院黑龙江哈尔滨150001,海洋腐蚀与防护国家重点实验室,中船重工725所青岛分部,山东青岛266071,山东青岛266071,山东青岛266071,黑龙江哈尔滨150001,黑龙江哈尔滨150001

收稿日期:2008-05-28 修回日期:2008-05-28 出版日期:2008-05-28 发布日期:2008-05-28

The Effect of Annealed Temperature On Properties of Ru-Ir-Sn Oxide Anode Coatings

JI Lei1,2,WANG Jun-tao2,XU Li-kun2,LIU Wen-bin1,XUE Gui-lin1,2

(1.Departement of Material Science and Chemical Enginering of Harbin Engineering University,Harbin 150001,China;2.State Key Laboratory for Marine Corrosion and Protection,Qingdao Branch of Luoyang Ship Material Research Institute,Qingdao 266071,Shandong,China

Received:2008-05-28 Revised:2008-05-28 Published:2008-05-28 Online:2008-05-28

摘要/Abstract

摘要： 应用溶胶凝胶法制备不同焙烧温度的氧化物阳极涂层,SEM,EDX,XRD、强化电解寿命、循环伏安和电化学阻抗等测试表明,烧结温度对阳极涂层的表面形貌以及电化学性能有着很大的影响.随着烧结温度的升高,析氯电位相应增加,寿命相对较长,循环伏安电量与双电层电容值有所下降.

关键词: 氧化物阳极涂层, 焙烧温度, 溶胶凝胶

Abstract: The anode coatings of Ru-Ir-Sn oxide were prepared by sol-gel method with different annealed temperatures.The influences of annealed temperature in properties of anode coatings were characterized by scanning electron microscope(SEM),energy dispersive X-ray detector(EDX),X-ray diffraction(XRD),potential of chlorine evolution,accelerated life,cyclic voltammetry and electrochemical impedance spectroscopy(EIS) tests.The results showed that the annealed temperature affected the morphology of coatings,while the electric quantities of cyclic voltammetry and double layer capacitances of anode coatings had a tendency to fall down and the potential of chlorine evolution and accelerated life had a tendency to increase as the annealed temperature increased.

Key words: oxide anode coatings, annealed temperature, solgel

中图分类号:

TG174.4

嵇雷, 王均涛, 许立坤, 刘文彬, 薛桂林, . 烧结温度对Ru-Ir-Sn氧化物阳极涂层性能的影响[J]. 电化学（中英文）, 2008, 14(2): 205-209.

JI Lei, WANG Jun-tao, XU Li-kun, LIU Wen-bin, XUE Gui-lin, . The Effect of Annealed Temperature On Properties of Ru-Ir-Sn Oxide Anode Coatings[J]. Journal of Electrochemistry, 2008, 14(2): 205-209.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.1892

https://electrochem.xmu.edu.cn/CN/Y2008/V14/I2/205

参考文献

[1]Beer H B.Electrochemical properties of mixed metaloxide coated titanuim anodes in sea water:U S,3711385[P].1973. [2]Pilla A S.Evaluation of anode deactivation in chlor-al-kali cells[J].J Appl Electrochemical,1997,27:1283. [3]Wang TY,Xu L K,Chen G Z.Electrochemical prop-erties of mixed metal oxide coated titanium anodes insea water[J].Electrochemical,2002,8(2):172-175. [4]Wang X,Tang D,Zhou J G.Microstructure,mophologyand electrochemical property of RuO270SnO230mol%and RuO230SnO270mol%coatings[J].Alloys andCompounds,2007,(430):60-66. [5]Ailton J Terezo,Ernesto C Pereira.Preparation andcharacterisation of Ti/RuO2anodes obtained by sol-geland conventional routes[J].Materials Letters,2001,339-345. [6]Panic V,Dekanski A,Wang G,et al.Morphology ofRuO2-TiO2coatings and TEM characterization of oxidesols used for their preparation[J].Journal of Colloidand Interface Science,2003,263:68-73. [7]Panic V,Dekanski A,Milonjic S,etal.The influenceof the aging time of RuO2and TiO2sols on the electro-chemical properties and behavior for the chlorine evolu-tion reaction of activated titanium anodes obtained bythe sol-gel procedure[J].Electrochimica Acta,2000,46:415-421. [8]Panic V V,Dekanski A,Milonjic S K,et al.RuO2-TiO2coated titanium anodes obtained by the sol-gel pro-cedure and their electrochemical behaviour in the chlo-rine evolution reaction[J].Colloids and Surfaces,1999,57:269-274. [9]Mattos-Costa F I,Lima-Neto P de.Machado S A S,etal.Characterization of surfaces modified by sol-gel de-rived RuxIr1-xO2coatings for oxygen evolu-tion in acidmedium[J].Electrochimica Acta,1998,44:1515-1523. [10]Trasatti S.Physical electrochemistry of ceramic oxide[J].Electrochim Acta,1991,36(2):225. [11]Xu L K,Scantlebury J D.A study on the deactivationof an IrO2Ta2O5coated titanium anode[J].CrossionScience,2003,45:2735. [12]Kerner Z,Pajkossy T.On the origin of capacitancedispersion of rough electrodes[J].Electrochimica Ac-ta,2000,46:207.

烧结温度对Ru-Ir-Sn氧化物阳极涂层性能的影响

The Effect of Annealed Temperature On Properties of Ru-Ir-Sn Oxide Anode Coatings

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 7

Metrics

[1]	黄舒, 黎学明, 李武林, 王雯. Ni/Ag2O/RuO2-Pt阴极制备与析氢性能[J]. 电化学（中英文）, 2012, 18(1): 62-67.
[2]	郑隽, 贾鑫, 王翀, 郑明森, 董全峰, . 锂离子电池正极材料LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2在LiNO_3溶液中的电化学性能研究[J]. 电化学（中英文）, 2010, 16(2): 151-155.
[3]	嵇雷, 王均涛, 刘文彬, 许立坤, 薛桂林, . 钌锡比对Ru-Ir-Sn氧化物阳极涂层性能的影响[J]. 电化学（中英文）, 2008, 14(3): 263-268.
[4]	何向明;王莉;张国昀;姜长印;万春荣;. 溶胶凝胶法合成锂离子电池正极材料LiMn_2O_4[J]. 电化学（中英文）, 2006, 12(1): 104-106.
[5]	王科;韩严;王均涛;张晓玲;孙玉璞;. 涂液浓度对Ru-Ti-Ir氧化物阳极涂层性能的影响[J]. 电化学（中英文）, 2006, 12(1): 74-79.
[6]	王科,韩严,王雷远,张晓玲,孙玉璞. 海水电解Ru-Ti-Ir-Sn氧化物阳极涂层研究[J]. 电化学（中英文）, 2005, 11(2): 176-181.
[7]	陈召勇,贺益,刘兴泉,李志结,于作龙. 类溶胶-凝胶法制备LiMn_2O_(4-δ)Cl_δ正极材料[J]. 电化学（中英文）, 2001, 7(1): 132-135.