采用溶胶-凝胶法在Ti表面修饰一层纳米TiO2(nanoTiO2)膜,经X射线粉末衍射(XRD)和扫描电镜(SEM)表征,证明多孔TiO2膜的平均孔径为80 nm.以该多孔膜电极为模板,借助电化学沉积的方法制备了纳米Na2SiF6(nano Na2SiF6).经XRD和透射电镜(TEM)测试证实该Na2SiF6为均一的白锰钒型结构,平均粒径约为20 nm.初步研究了其荧光性质,发现在452.4 nm和285 nm处分别有强的荧光发射峰和激发峰.
The nano TiO2 film was prepared by sol-gel process and characterized with X-ray diffraction(XRD) and scanning electron microscope(SEM).It was found that the average size of pore diameter was about 80 nm for the nano TiO2 film.The Nano Na2SiF6 was synthesized by electrochemical deposition on the nanoporous film electrode and characterized with XRD and transmission electron microscope(TEM).The result showed that the average size of nanoparticle was 20 nm for the nano Na2SiF6.The fluorescence property of nano Na2SiF6 was also studied briefly.The result indicated that the nano Na2SiF6 exhibited strong fluorescence emission at 452.4 nm and 285 nm,respectively.
[1]Jin R,Cao Y,Mirkin C A,et al.Photo-induced con-version of silver nanospheres to nanoprisms[J].Sci-ence,2001,294:1901-1903.
[2]Millstone J E,Park S,Shuford K L,et al.Observationof a quadrupole plasmon mode for a colloidal solution ofgold nanoprisms[J].J Am Chem Soc,2005,127:5312-5313.
[3]Sun Y,Mayers B,Xia Y.Transformation of silvernanospheres into nanobelts and triangular nanoplatesthrough a thermal process[J].Nano Lett,2003,3:675-679.
[4]Jin R C,Cao Y C,Hao E C,et al.Controlling aniso-tropic nanoparticle growth through plasmon excitation[J].Nature,2003,425:487-490.
[5]Wei G T,Yang Z,Lee C Y,et al.Aqueous-organicphase transfer of gold nanoparticles and gold nanorods u-sing an ionic liquid[J].J Am Chem Soc,2004,126:5036-5037.
[6]Cikby A F J,Hornyak G L,Stochert J A,et al.Tem-plate-synthesized nanoscopic gold particle:optical spec-tra and the effects of particle[J].J Phys Chem,1994,98:2963-2971.
[7]Yu Y Y,Chang S S,Lee C L,et al.Gold nanorods:electrochemical synthesis and optical properties[J].JPhys Chem B,1997.101:6661-6664.
[8]Zach M P,Kwokh N,Penner R M.Molybdenumnanowires by electrodeposition[J].Science,2000,290:2120-2123.
[9]The Tianjin Chemical Industry Research Institute(天津化工研究院).The handbook of inorganic salt industry(the first volume)[M].Beijing:Chemical IndustryPress,1996:731-732.
[10]CHU Dao-Bao(褚道葆),SHEN Guang-Xia(沈广霞),ZHOU Xin-Fu(周幸福),et al.Electrocatalyticactivity of nanocrystalline TiO2film modified Ti elec-trode[J].Chem J Chin Univ-Chin(in Chinese),2002,23(4):678-681.
[11]CHU Dao-Bao(褚道葆),YAO Wen-Li(姚文俐),GU Jia-Shan(顾家山),et al.Heterogeneous electro-catalytic reduction of p-nitrobenzoic acid on nanocrys-talline TiO2film modified electrode[J].Chem J ChinUniv-Chin(in Chinese),2004,25(11):2137-2139.
[12]Xiong G,Zhi Z L,Wang X J.Characterization of per-ovskitetype LaCoO3nanocrystals prepared by a stearicacid sol-gel process[J].Mater Sci Lett,1997,16:1064-1068.
[13]Lakowiz J R,Gryczynski I,Gryczynski Z.Lumines-cence spectral properties of CdS nanoparticles[J].JPhys Chem B,1999,103:7613-7620.