以甲基丙烯酸二甲基氨基乙酯和甲基丙烯酸三氟乙酯为单体,经过自由基聚合反应、成膜和碱化3个步骤制备氢氧型的DMAEMA/TFMA聚合物阴离子交换膜,系统表征该聚合物膜的结构和性能.结果表明:室温下其电导率可达10-2 S.cm-1;该膜的甲醇渗透系数低于10-7 cm2.s-1;以该膜组装的单电池在室温下的最大功率密度为43.2 mW/cm2,在燃料电池中有良好的应用前景.
Anion exchange membrane fuel cells,which use anion exchange membranes as polyelectrolytes,have attracted more and more research interests recently.In this work,a series of hydroxyl-conducting anion-exchange membranes based on the copolymer of 2-(Diethylamino)ethyl methacrylate and fluoro-polyacrylate were prepared by radical polymerization,and their potential applications in alkaline fuel cells were assessed.It was shown that the ionic conductivity of the membranes reached 10-2 S·cm-1 at room temperature,while the methanol permeability was lower than 10-7 cm2·s-1.The maximum power density of fuel cell assembled with this membrane was achieved to be 43.2 mW·cm-2 at room temperature,indicating possible application of this membrane in alkaline fuel cells.
[1]Yu E H,Scott K.Development of direct methanol alka-line fuel cells using anion exchange membranes[J].JPower Sources,2004,137(2):248-256.
[2]Li T,Yang Y.A novel inorganic/organic composite m-embrane tailored by various organic silane coupling a-gents for use in direct methanol fuel cells[J].J PowerSources,2009,187(2):332-340.
[3]Schultz T,Zhou S,Sundmacher K.Current status of andrecent developments in the direct methanol fuel cell[J].Chem Eng Technol,2001,24(12):1223-1233.
[4]Varcoe J R,Slade R C T.Prospects for alkaline anion-exchange membranes in low temperature fuel cells[J].Fuel Cells,2005,5(2):187-199.
[5]Fang J,Shen P K.Quaternized poly(phthalazinon ethersulfone ketone)membrane for anion exchange mem-brane fuel cells[J].J Membr Sci,2006,28(1/2)5:317-322.
[6]Zeng Q H,Liu Q L,Broadwell L,et al.Anion exchangemembranes based on quaternized polystyrene-block-poly(ethylene-ran-butylene)-block-polystyrene for directmethanol alkaline fuel cells[J].J Membr Sci,2010,349(1/2):237-243.
[7]Hibbs M R,Fujimoto C H,Cornelius C J.Synthesis andcharacterization of poly(phenylene)-based anion ex-change membranes for alkaline fuel cells[J].Macromol-ecules,2009,42(21):8316-8321.
[8]Yu Wang(汪瑜).2-(Diethylamino)ethyl methacrylate[J].Sichuan Chemistry Industry(四川化工),1989,(1):49-51.
[9]Souzy R,Ameduri B.Functional fluoropolymers for fuelcell membranes[J].Prog Polym Sci,2005,30(6):644-687.
[10]Qi M Y,Wu G Z,Sha M L,et al.Radiation inducedpolymerization of MMA in imidazolium ionic liquidsand their mixed solutions with organic solvents[J].Radiation Physics and Chemistry,2008,77(10/12):1248-1252.
[11]Kolhe S M,Kumar A.Preparation of strong base anionexchange membrane using 60Co gamma radiation[J].Radiation Physics and Chemistry,2005,74(5):384-390.
[12]Xiong Y,Liu Q L,Zhang Q H.Quaternized cardo poly-etherketone anion exchange membrane for direct meth-anol alkaline fuel cells[J].J Power Sources,2009,193(2):541-546.
[13]Das D B,Nassehi V,Wakeman R J.A finite volumemodel for the hydrodynamics of combined free and por-ous flow in sub-surface regions[J].Advances in Envi-ronmental Research,2002,7(1):35-58.
[14]Xu H K,Fang J,Guo M L,et al.Novel anion exchangemembrane based on copolymer of methyl methacrylate,vinylbenzyl chloride and ethyl acrylate for alkaline fuelcells[J].J Membr Sci,2010,354(1/2):206-211.
[15]Hu Z X,Yin Y,Okamoto K,et al.Synthesis and char-acterization of sulfonated polyimides derived from 2,2-bis(4-sulfophenyl)-4,4-oxydianiline as polymer elec-trolyte membranes for fuel cell applications[J].JMembr Sci,2009,329(1/2):145-152.
[16]Wang E D,Zhao T S,Yang W W.Poly(vinyl alcohol)/3-(trimethylammonium)propyl-functionalized silica hy-brid membranes for alkaline direct ethanol fuel cells[J].International Journal of Hydrogen Energy,2010,35(5):2183-2189.
[17]Wang Jin(王瑾).Synthesis and characterizion of am-monium salt anion exchange membrane[D].Haerbin:Haerbin Industry University,2007.
[18]Yu E H,Scott K.Development of direct methanol alka-line fuel cells using anion exchange membranes[J].JPower Sources,2004,137(2):248-256.
[19]YE Fei(叶飞),CHEN S Z(陈胜洲),DONG X F(董新法),et al.Technical advances in membrane elec-trode assembly fabrication for direct methanol fuel cell[J].Modern Chemical Industry(现代化工),2005,25(9):30-33.
[20]Kang J J,Li W Y,Lin Y,et al.Synthesis and ionicconductivity of a polysiloxane containing quaternaryammonium groups[J].Polymers for Advanced Tech-nologies,2004,15(1-2):61-64.