电化学（中英文） ›› 1997, Vol. 3 ›› Issue (4): 420-423.

电液组成对电沉积锌粉腐蚀性能的影响

李清文,杨琴,夏熙

新疆大学应用化学研究所

收稿日期:1997-11-28 修回日期:1997-11-28 出版日期:1997-11-28 发布日期:1997-11-28

The Effect of Solution Composition on the Corrosion Behavior of Electrodeposited Zinc Powder

Li Qingwen* Yang Qin Xia Xi

(Applied Chem. Inst. of xinjiang Univ., Urumqi 830046)

Received:1997-11-28 Revised:1997-11-28 Published:1997-11-28 Online:1997-11-28

摘要/Abstract

摘要： 利用扫描电镜及交流阻抗技术研究不同电液组成（四种体系，即中性、ＥＤＴＡ络合、柠檬酸络合、ＫＯＨ体系）及某些添加物（ＩｎＣｌ３、Ｐｂ（Ａｃ）２及三乙醇胺等）的存在对电沉积锌粉形貌及腐蚀性能的影响，结果表明，若在中性或碱性介质中加入某些添加物如Ｉｎ盐或Ｐｂ盐或采用Ｚｎ－ＥＤＴＡ介质可以改善锌粉的腐蚀性能．

关键词: 电沉积锌粉, 电液组成, 腐蚀性能

Abstract: Zinc powder as a widely anode material can be electrowon from ZnCl2 or ZnO+KOH media. The properties of zinc powder are likely to be modified with electrolytic conditions such as the composition of bath solution, electrolysis manner, current density and additives etc.. In this paper, we have discussed the effect of the compositions of bath solution on the microstructure and corrosion resistance of zinc powder.

中图分类号:

TG146.13

李清文, 杨琴, 夏熙. 电液组成对电沉积锌粉腐蚀性能的影响[J]. 电化学（中英文）, 1997, 3(4): 420-423.

Li Qingwen Yang Qin Xia Xi. The Effect of Solution Composition on the Corrosion Behavior of Electrodeposited Zinc Powder[J]. Journal of Electrochemistry, 1997, 3(4): 420-423.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y1997/V3/I4/420

[1]	李翔, 严彪, 董鹏, . Fe基非晶和纳米晶合金晶化及电化学腐蚀行为[J]. 电化学（中英文）, 2009, 15(3): 269-274.
[2]	杨化滨, 张海昌, 孙华, 王晓丹, 周作祥. CH_3OH-H_2O体系化学镀铜Mg_(1.85)Mm_(0.15)Ni合金的抗腐蚀性能研究[J]. 电化学（中英文）, 2003, 9(2): 196-202.