铝阳极氧化多孔膜层的界面电性能研究

doi:10.61558/2993-074X.2690

电化学（中英文） ›› 1998, Vol. 4 ›› Issue (2): 164-169. doi: 10.61558/2993-074X.2690

铝阳极氧化多孔膜层的界面电性能研究

旷亚非,王玲,胡飞

湖南大学化学化工学院

收稿日期:1998-05-28 修回日期:1998-05-28 发布日期:1998-05-28 出版日期:1998-05-28

Study of Charged Property on the Interface of Porous Membrane of Anodized Aluminum

Kuang Yafei Wang Ling Hu Fei

(Coll. of Chem. and Chem. Eng.,Hunan Univ., Changsha, 410082)

Received:1998-05-28 Revised:1998-05-28 Online:1998-05-28 Published:1998-05-28

摘要/Abstract

摘要： 采用电渗方法研究了经硫酸溶液氧化并利用逆向电解方法剥离后的铝阳极氧化多孔膜层的ζ电位与溶液ｐＨ的关系．结果表明：该多孔膜层在１．０×１０－２ｍｏｌ／ＬＫＣｌ溶液中的ｐＨ等电点（ｐＨＩＥＰ）＝９．２０，２．００＜ｐＨ＜９．２０，ζ＞０，多孔膜荷正电；９．２０＜ｐＨ＜１１．００，ζ＜０，多孔膜荷负电．

关键词: 铝阳极氧化多孔膜层, ζ电位, 等电点

Abstract: Using electrodialytic method, the relation between the pH value of tested solution and the ζ potential of porous anodized aluminum membrane, which was separated by reverse electrolysis from aluminum substrate, has been investigated. The following results can be obtained in 1.0×10-2 mol/L KCl solution: The pHIEP(isoelectric potential) of the porous membrane is equal to 9.20; In the range of 2.00

中图分类号:

TQ153.6

旷亚非, 王玲, 胡飞. 铝阳极氧化多孔膜层的界面电性能研究[J]. 电化学（中英文）, 1998, 4(2): 164-169.

Kuang Yafei Wang Ling Hu Fei. Study of Charged Property on the Interface of Porous Membrane of Anodized Aluminum[J]. Journal of Electrochemistry, 1998, 4(2): 164-169.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/10.61558/2993-074X.2690

https://electrochem.xmu.edu.cn/CN/Y1998/V4/I2/164

[1]	高红丽, 周凯琳, 王琛, 李素娟, 章慧, 夏兴华. 阵列纳米通道中氨基官能团质子化研究[J]. 电化学（中英文）, 2012, 18(3): 229-234.
[2]	余世鑫, 孙雯. 电化学技术在选磷回水利用中的应用[J]. 电化学（中英文）, 1998, 4(2): 176-181.

铝阳极氧化多孔膜层的界面电性能研究

Study of Charged Property on the Interface of Porous Membrane of Anodized Aluminum

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

Metrics