关键词: 锌电极, Zn-La合金, 固相扩散法

Abstract: Zn_La alloys were prepared by solid phase diffusion method and the effects of La on the electrochemical performance of zinc electrodes were investigated using potentiostatic polarization technique and charging/discharging cycle test. The results showed that adding La to zinc electrode remarkably suppressed the zinc dendrite, the shape of zinc electrode and zinc corrosion, and hence, markedly improved the cycle performance of zinc electrodes. The discharging capacity of the zinc electrode containing 0.5at.% La which was the optimum was still 520 mAh/g after it cycled 80s at the current of 100 mA. The XPS showed that La element mainly adhered on the surface of the zinc electrode in the form of La2O3/La(OH)3 that evidently enhanced the cycle life of the secondary zinc electrode.