Improvement and Its Mechanism of Storage Performance of Ni-MH Battery

LI Xiao-feng~

(*), MA Li-ping, LOU Yu-wan, LI Feng, XIA Bao-jia(Shanghai Institute of Micro-system and Information Technology, CAS, Shanghai 200050, China

Received:2004-11-28 Revised:2004-11-28 Published:2004-11-28 Online:2004-11-28

摘要/Abstract

摘要： 　应用恒电流充放电法和循环伏安法研究了MH/Ni电池的储存性能.结果表明,储存期间当电池开路电压下降至1.0V以下后,组成正极导电网络的CoOOH将被还原并在随后的充电过程中不能完全复原,导致电池储存性能下降.如于正极中加入镍粉作导电剂,便能在一定程度上减缓这种影响,改善电池的储存性能.

关键词: 金属氢化物-镍电池, 储存性能, 导电网络, 镍粉

Abstract: The storage performance of nickel-metal-hydride (Ni-MH) battery was studied by using galvanostatic charge-discharge and cyclic voltammetry. The experimental results indicated that CoOOH could not be completely restored after its being thoroughly reduced at lower potential, which might weaken electric conduction network in the positive electrode and result in fading of electrochemical properties of Ni-MH battery. Addition of nickel powder as a conductive agent into the positive electrode was beneficial to the capacity recovery after storage.

Key words: Nickel-metal-hydride battery, Storage performance, Electric conduction network, Nickel powder

中图分类号:

TM912.2

李晓峰,马丽萍,娄豫皖,李峰,夏保佳. MH/Ni电池储存性能的改善及其机理研究[J]. 电化学（中英文）, 2004, 10(4): 425-429.

LI Xiao-feng~. Improvement and Its Mechanism of Storage Performance of Ni-MH Battery[J]. Journal of Electrochemistry, 2004, 10(4): 425-429.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2004/V10/I4/425

[1]	许高洁, 杨海燕, 韩鹏献, 张立学, 张克军, 张传健, 范玉华, 毕彩丰, 崔光磊. 锂离子电池MnO/TiN负极研究[J]. 电化学（中英文）, 2012, 18(1): 37-42.
[2]	李晓峰, 魏彦伟, 董会超, . 氧化方式对发泡镍电极中CoOOH导电网络稳定性的影响[J]. 电化学（中英文）, 2008, 14(1): 83-86.