Electrochemical Response of Deformed Marine Steel in Sea-mud Containing Sulfate Reducing Bacteria

HUANG Yan_liang

(Institue of Oceanology,Chinese Academy of Sciences,Qingdao 266071,China

Received:2003-08-28 Revised:2003-08-28 Published:2003-08-28 Online:2003-08-28

摘要/Abstract

摘要： 海洋用钢在海底泥土区常承受具大的应力 ,而应力将对海洋用钢的腐蚀破坏行为产生影响 .本文选用一种常用的海洋用钢 ,采集含有硫酸盐还原菌 (SRB)的天然海泥 ,研究试样在海泥中的腐蚀行为 ,以及试样在有裂纹和无裂纹存在时的电流响应特征

关键词: 海洋用钢, 海泥, 硫酸盐还原菌

Abstract: The corrosion failure behavior of marine steel is affected by stress,which exists in offshore structures at sea_mud region.In order to conduct the study of stress on the electrochemical response of a selected steel,a kind of natural sea_mud containing sulfate reducing bacteria(SRB) was collected.The electrochemical response of cyclic stress of the specimen with and without cracks in sea_mud was analyzed.

Key words: Marine steel, Marine_mud, Sulfate reducing bacteria, Strain electrochemistry

中图分类号:

TG171

黄彦良. 海洋用钢在含硫酸盐还原菌的海泥中的应变电化学响应[J]. 电化学（中英文）, 2003, 9(3): 287-291.

HUANG Yan_liang . Electrochemical Response of Deformed Marine Steel in Sea-mud Containing Sulfate Reducing Bacteria[J]. Journal of Electrochemistry, 2003, 9(3): 287-291.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://electrochem.xmu.edu.cn/CN/

https://electrochem.xmu.edu.cn/CN/Y2003/V9/I3/287

[1]	魏华,王秀通,高荣杰,李焰. SML,ERW管线钢在海泥中的腐蚀行为[J]. 电化学（中英文）, 2005, 11(3): 314-318.
[2]	方汉平, 徐立冲, 张彤. 利用原子力显微镜和分子技术研究海水微生物腐蚀(英文)[J]. 电化学（中英文）, 2003, 9(2): 164-169.
[3]	刘光洲,钱建华,马焱,吴建华. B10合金的硫酸盐还原菌腐蚀研究[J]. 电化学（中英文）, 2002, 8(2): 191-194.
[4]	刘靖,范洪波,徐海平,郑家木焱,许立铭,毛宗强. 碳钢在微生物介质中的腐蚀电化学行为[J]. 电化学（中英文）, 2002, 8(2): 186-190.
[5]	董泽华,郭兴蓬,郑家燊,许立铭. 碳钢在生物膜和硫化物膜下的电化学腐蚀行为[J]. 电化学（中英文）, 2001, 7(2): 173-179.