本文提出一种电沉积光亮锡钴锌三元合金的新工艺．其溶液组成及操作条件为：Ｎａ３Ｃ６Ｈ５Ｏ７·２Ｈ２Ｏ１００～１５０，Ｎａ２ＥＤＴＡ·２Ｈ２Ｏ２０～３０，ＳｎＣｌ２·２Ｈ２Ｏ１５～２０，ＣｏＳＯ４·７Ｈ２Ｏ２５～３５，ＺｎＣｌ２１５～２０ｇ·Ｌ－１；稳定剂ＷＤＺ－１６０～１００，光亮剂ＷＤＺ－２１５～２０ｍＬ·Ｌ－１．ｐＨ＝４～６，Ｄｋ＝０．５５．０Ａ·ｄｍ－２，Ｔ＝５～３５℃．在此条件下可得到光亮的含Ｃｏ为０．５～３．５％、Ｚｎ为１～１０％的锡钴锌三元合金沉积层．讨论了溶液组成对沉积层组成的影响．
A new process of electrodeposting bright Tin Cobalt Zinc alloy from weak acid solution is proposed in this paper. The solution compositions and operating conditions are Na 3C 6H 5O 7·2H 2O 100～150,Na 2EDTA·2H 2O 20～30,SnCl 2·2H 2O 15～20,CoSO 4·7H 2O 25～35,ZnCl 2 15～20 g·L -1 ;stabilizer WDZ 1 60～100, brightener WDZ 2 15～20 mL·L -1 ; pH=4～6, D K = 0.5～5.0 A·dm -2 , T= 5～35 ℃. A bright Sn Co Zn deposit having Co about 0.5～3.5% and Zn about 1～10% is produced. The effects of bath compositions on Co or Zn content in deposit is also discussed.
1A．Brenner．ElectrodepositionofAaloys．NewYorkandLondon：AcademicPress，19632（日）石井英雄等著，黄健农等译．日本电镀指南．长沙：湖南科学技术出版社，1985：296～2983屠振密．电镀合金原理与工艺．北京：国防工业出版社，1993：177～185，82～854王志军等．锡钴锌三元合金代铬工艺——“代铬－90”添加剂的研制及应用（内部资料）．19905左正忠，侯润香．电沉积可焊性光亮锡－铅合金的研究．材料保护，1994，27（9）：10～146左正忠，侯润香等．电沉积光亮锡锌合金的研究．电镀与环保，1995，15（2）：3～57左正忠，侯润香等．硫酸盐－氯化物体系电沉积枪黑色锡－镍合金．材料保护，1995，28（7）：1～48左正忠，侯润香等．无氰体系中电沉积光亮铜锡合金的研究．武汉大学学报（自然科学版），1995，41（6）：659～6649左正忠，何细华等．无氰溶液中电沉积铜锡合金电化学行为的研究．武汉大学学报（自然科学版），1996，42（2）：141～14510周绍民等．金属电沉积－原理与研究方法．上海：上海科学技术出版社，1987：322～33611郭鹤桐等．理论电化学．北京：宇航出版社，1985